Chitosan-schiff base with three different ratios of para-Dimethyl aminobenzaldehyde& chitosan Schiff base hydrogels have been prepared for controlled drug release study. The synthesized chitosan Schiff base and chitosan Schiff base hydrogel were characterized by FT-IR, UV-Visible, SEM, analysis. Swelling properties of the hydrogel were investigated at three different media pH (2, 7, 10). The swelling degree varied with the pH, amount of crosslinking agent glutaraldehyde and with the amount of paraDimethylaminobenzaldehyde for the hydrogels. All hydrogels were used for controlled drug release system. Aspirin was used as model drug, in three different buffer solution (2, 7, 10) as release media. The rate of release of drugs in the pH2 is m

The process for preparing activated carbon (AC) made from tea residue was described in this paper. Investigated were the physicochemical characteristics and adsorption efficiency of the produced AC. Activation with potassium hydroxide (KOH) and carbonization at 350 °C are the two key steps in the manufacturing of AC. The activated carbon was used to adsorb Tetracycline (TC). Different parameters were studied at room temperature to show their effects on the adsorption efficiency of TC. These parameters are the initial concentration of adsorbate TC, solution acidity pH, time of adsorption, and adsorbent dosage. The prepared active carbon was characterized using Fourier transform infrared spectroscopy (FTIR), scanning electron microsc

The synthesis, characterization and liquid crystalline properties of N4,N40 -bis((1 H-benzo[d]imidazol-2- yl)methyl)-3,30 -dimethyl-[1,10 -biphenyl]-4,40 -diamine and of their corresponding Mn(II), Fe(II), Ni (II), Cu(II), and Zn(II) complexes are described. The ligand and complexes have been characterized by elemental analysis, magnetic susceptibility measurements (meff), conductometric measurements and Fourier Transform Infrared (FTIR), Nuclear Magnetic Resonance (1 H NMR), (13C-NMR) and UV–Vis spectroscopy. Spectral investigations suggested octahedral coordination geometrical arrangement for M(II) complexes. The phase transition temperatures were detected by differential scanning calorimetry (DSC) analysis and the phases are confirmed

In the present article, Nano crystalline SnS and SnS:3% Bi thin films were fabricated using thermal
evaporation with 400±20 nm thickness at room temperature at a rate deposition rate of 0.5 ±0.01nm
/sec then annealing for one hour at 573 K for photovoltaic application. The prepared samples were
characterized in order to investigate the structural, electrical, morphological, and optical properties
using diverse techniques. XRD and SEM were recorded to investigate the effect of doping and
annealing on structural and morphological possessions, respectively. XRD showed an SnS phase
with polycrystalline and appeared to form an orthorhombic structure, with the distinguish trend
along the (111) grade,

  This work involves synthesis of novel Schiff bases derivatives contining isoxazoline or pyrazoline units starting with chalcons . 4-Aminoacetophenone was react with pnitrobenzaldehyde or p-chlorobenzaldehyde in basic medium giving chalcones [I]a,b by claisenschemidt reactions. The chalcones [I]a,b were reacted with hydroxylamine hydrochloride giving isoxazolines [II]a,b  in basic medium. The chalcone [I]a could also reacted with hydrazine hydrate to give pyrazolines [III]a  . The novel Schiff bases with structural formula [VIII]n , [IX]n , [X]m and [XI]m were prepared by the reaction of amino compounds ; isoxazoline [II]a,b and pyrazolines [III]a with monoaldehydes [VI]n and dialdehydes [VII]m , respectively in dry benze

A simple, inexpensive, and home–built electrostatic spray deposition (ESD) system with stable cone-jet mode was used to obtain nickel oxide (NiO) thin films on glass substrates kept at temperature of 400°C. The primary precursor solution of 0.1 M concentration hydrated nickel chloride dissolved in isopropyl alcohol. The structural, optical and electrical parameters were studied. The optical absorbance spectra for the studied samples showed its maximum around 280 nm. On the other hand, thickness interferometry measurements on the tested samples showed that film thickness was around 400 nm. The optical energy gap of the prepared NiO samples was determined to be 3.75 eV and the maximum value of refractive index was determined to be 2.1 a

An attempt to synthesize the benzoimidazol derivatives from the reaction of o-phenylenediamine and benzoic acid derivatives in the presence of ethanol and various ketones under microwave irradiation, 1 , 5 - benzodiazepinum salt derivatives were obtained instead of them. Unexpected reaction was happened for synthesis a new series of benzodiazepinium salt derivatives in a selective yield . The reaction mechanism was also discussed. The new compounds were purified and identified their structures were elucidated using various physical techniques like; FT- IR spectra, micro elemental analysis (C.H.N) and 1H NMR spectra.

Cadmium sulfide (CdS) nanocrystalline thin films are prepared onto ITO-glass and Si(111) substrates by chemical bath deposition method. The scanning electron microscope images showed that the CdS thin film onto Si substrate is more homogenous without vacancies. The XRD patterns of the CdS nanocrystalline thin film confirm that they have polycrystalline with cubic phase. Room temperature photoluminescence (PL) spectrum of the CdS nanocrystalline thin films shows emission band located at 502nm for CdS/Si sample while the CdS/ITO-glass thin films shows a broad emission band peaked at 505nm. The Raman spectra of CdS nanocrystalline thin films prepared onto Si and ITO-glass substrates contain two main peaks which are corresponding to the firs

We prepared polythiophene (PTH) with single wall carbon nanotube (SWCNT) nanocomposite thin films for Nitrogen dioxide (NO2) gas sensing applications. Thin films were synthesized via electrochemical polymerization method onto (Indium tin oxide) ITO coated glass substrate of thiophene monomer with magnesium perchlorate and different concentration from SWCNT (0.012 and 0.016) % in the presence130mL of Acetonitrile used. X-ray diffraction (XRD), Field Emission Scanning Electron microscopy (FE-SEM), Atomic Force Microscope (AFM) and Fourier Transform Infrared Spectroscopy (FT-IR) were used to characterized these nanocomposite thin films. The response of these nanocomposite for NO₂ gas was evaluated via monitoring the change