The present investigation considers the effect of curing temperatures (30, 40, and 50˚C) and curing compound method on compressive strength development of high performance concrete, and compares the results with concrete cured at standard conditions and curing temperature (21˚C). The experimental results showed that at early ages, the rate of strength development at high curing temperature is greater than at lower curing temperature, the maximum increasing percentage in compressive strength is 10.83% at 50C˚ compared with 21C˚ in 7days curing age. However, at later ages, the strength achieved at higher curing temperature has been less, and the maximum percentage of reduction has been 5.70% at curing temperature 50C˚ compared with 21

In this work a hybrid composite materials were prepared containing matrix of polymer (polyethylene PE) reinforced by different reinforcing materials (Alumina powder + Carbon black powder CB + Silica powder). The hybrid composite materials prepared are: • H1 = PE + Al2O3 + CB • H2 = PE + CB + SiO2 • H3 = PE + Al2O3 + CB + SiO2 All samples related to electrical tests were prepared by injection molding process. Mechanical tests include compression with different temperatures and different chemical solutions at different immersion times The mechanical experimentations results were in favour of the samples (H3) with an obvious weakness of the samples (H1) and a decrease of these properties with a rise in temperature and the increasing

The preparatory phase since it corresponds to adolescence are the most important stages of life , where the individual 's personality to take shape at this stage and start asking questions about the same , trying to discover the positive and negative traits hehas in order to form distinctive character and also is being he have Love Poll For everything that goes on around him.
And attention to cognitive motivation is important for students because the student who owns a motive cognitively looking for self - knowledge with conviction, and learning then be meaningful and lasts long. The motive of knowledge are common in which cognitive components does not mean exclusive knowledge on academic books and research in the narrow borders but a

Objectives: Successful endodontic treatment outcome requires effective shaping and cleaning of root canals. This study aims to evaluate the smear layer removal after continuous chelation (CC) ) NaOCL\HEDP( and sequential chelation (SC) )NaOCL\EDTA( and their influence on the push-out bond strength (POBS) of Bio-C sealer. Materials and Methods: Palatal roots of the maxillary first molar (n=72) were divided into four groups (n=18) as follows: 3% NaOCL, SC: 3% NaOCL followed by 17% EDTA, CC: 3% NaOCL \9% HEDP and Distilled water. Thirty-two roots (n=8/group) were split longitudinally for smear layer evaluation using SEM. Forty roots were obturated with Guttapercha and Bio-C sealer using a single cone technique. Thre

In this study, the effect of the combination of micro steel fibers and additives (calcium hydroxide and sodium carbonate) on the size of cracks formation and healing them were investigated. This study aims to apply the use of self-healing phenomenon to repair cracks and to enhance the service life of the concrete structures. Micro steel fibers straight type were used in this research with 0.2% and 0.4% by volume of concrete. A weight of 20 and 30 kg/m³ of Ca(OH)₂ and 2 and 3 kg/m³ of Na₂CO₃ were used as a partial cement replacement. The results confirm that the concrete cracks were significantly self-healed up to 30 days re-curing. Cracks width up to 0.2 mm were comp

Background: This in vitro study evaluated the effect of canal dryness and flaring on the accuracy of two electronic apex locators for working length (WL) determination. Materials and methods: Sixty extracted teeth were used, after access opening was done, the occlusal surface was flattened to create stable reference point. The teeth were randomly divided into two equal main groups of flared and unflared group each one of 30 teeth. The flaring was done with Gates Glidden drills. The two main groups were further subdivided into two subgroups: dry canal and wet canal using 5.25% sodium hypochlorite groups, Electronic WL of each sample was determined using both Root ZX and i-Root apex locator. Consequently, histologic WL was determined by shav

This study was aimed to reduce the amount of the sprayed solution lost during trees spraying.  At the same time, the concentration of the sprayed solution on the target (tree or bush) must be ensured and to find the best combination of treatments. Two factors controls the spraying process: (i) spraying speed (1.2 km/h, 2.4 km/h, 3.6 km/h), and (ii) the type of sensor. The test results showed a significant loss reduction percentage. It reached (6.05%, 5.39% and 2.05%) at the speed (1.2 km/h, 2.4 km/h, 3.6 km/h), respectively. It was noticed that when the speed becomes higher the loss becomes less accordingly. The interaction between the 3.6 km/h speed and the type of Ultrasonic sensor led to a decrease in the percentage of the spray