Studying the Effect of Addition Particles of Alumina (Al2O3) and Zirconia (ZrO2), on Some Mechanical Properties for Matrix Composites (Al-Si-Mg) Alloy
...Show More Authors

This study is concerned with the effect of adding two kinds of ceramic materials on the mechanical properties of (Al-7%Si- 0.3%Mg) alloy, which are zirconia with particle size (20μm > P.S ≥ 0.1μm) and alumina with particle size (20μm > P.S ≥ 0.1μm) and adding them to the alloy with weight ratios (0.2, 0.4, 0.6, 0.8 and 1%). Stirring casting method has been used to make composite material by using vortex technique which is used to pull the particles to inside the melted metals and distributed them homogenously.

After that solution treatment was done to the samples at (520ºC) and artificial ageing at (170ºC) in different times, it has been noticed that the values of hardness is increased with the aging time of the original alloy and reached its highest value after (8hr).

Mechanical tests were done to the original alloy and the composite material at the maximum hardness value and represented by tensile, hardness, and wear tests. It was found that the hardness value is increased with increment of the amount of added particles; also the increment in the hardness of the alloy which is reinforced with alumina is more than that reinforced with zirconia.

Regarding the tensile test, results show that the strength and yield resistance of the composite material are more than that in the original alloy and these values are increased with increasing the amount of the added particles and they reached maximum values at (0.6%). Then they are decreased but these values remain at higher values than those in the original alloy. However, the ductility is decreased as compared with the original alloy and this decrement was more obvious with the increasing amount of the added particles. The increment of strength and yield resistance of the alloy reinforced by alumina was higher than that reinforced with zirconia, while the ductility of the alloy reinforced by zirconia was higher than that happened by the addition of alumina. Also zirconia and alumina addition to the original alloy decreased the wear rate, and the decrement would be more with the increased amount of adding particles. In addition the wear resistance of the alloy reinforced with alumina was larger than that reinforced with zirconia. X-rays testing proved that secondary phase (AlFeSi) appeared in both original alloy and the composite material. While heat treatment led to the appearance of phases (Mg2Al) and (Mg2Si) in original alloy. This was led to obvious improvement in the mechanical properties in addition to appearance ceramic particles in the microstructure of the composite material.

This structure somewhat homogenous has fine grains as compared with large grains in the microstructure of the original alloy. .        

View Publication Preview PDF
Quick Preview PDF
Publication Date
Sun Jun 12 2011
Journal Name
Baghdad Science Journal
Effect of Water on Some Mechanical Properties for Sawdust and Chopped Reeds /UPE composites
...Show More Authors

In this study, composite materials were prepared using unsaturated polyester resin as binder with two types of fillers (sawdust and chopped reeds). The molding method is used to prepare sheets of UPE / sawdust composite and UPE / chopped reeds composite. The mechanical properties were studied including flexural strength and Young's modulus for the samples at normal conditions (N.C). The Commercial wood, UPE and its composite samples were immersed in water for about 30 days to find the weight gain (Mt%) of water for the samples, also to find the effect of water on their flexural strength and Young's modulus. The results showed that the samples of UPE / chopped reeds composite gained highest values of flexural strength (24.

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Fri Mar 31 2017
Journal Name
Al-khwarizmi Engineering Journal
Experimental Study to the Effect of Natural Particles Added to Unsaturated Polyester Resin of a Polymer Matrix Composite
...Show More Authors

Experimental investigations had been done in this study to demonstrate the effect of natural particles used as a reinforcement material to unsaturated polyester resin. The tensile test and water absorption were investigated according to (ASTM D638) and (ASTM D570), respectively. The influence of sunflower husk and pomegranate husk particles, used as a reinforcement material, on the tensile strength, Young's modulus and water absorption with different weight fraction (3%, 7% and 10%) and particle grain size (50µm, 100 µm and 150 µm), has been investigated. The water absorption of polymer composites was studied by measuring the specimen weight before and after immersion in water for one hundred days. In the experiments of tensile test,

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Mon Dec 25 2017
Journal Name
Biomedical And Pharmacology Journal
Effect of the Addition of Polyamide (Nylon 6) Micro-Particles on Some Mechanical Properties of RTV Maxillofacial Silicone Elastomer Before and After Artificial Aging
...Show More Authors

View Publication
Crossref (7)
Crossref
Publication Date
Thu Dec 01 2011
Journal Name
Journal Of Engineering
EFFECT OF COOLING RATE ON MECHANICAL PROPERTIES OF EUTECTIC AND HYPOEUTECTIC Al-Si ALLOYS
...Show More Authors

In this research the effect of cooling rate and mold type on mechanical properties of the eutectic
and hypoeutectic (Al-Si) alloys has been studied. The alloys used in this research work were (Al- 12.6%Si
alloy) and (Al- 7%Si alloy).The two alloys have been melted and poured in two types of molds with
different cooling rates. One of them was a sand mold and the other was metal mold. Mechanical tests
(hardness, tensile test and impact test) were carried out on the specimens. Also the metallographic
examination was performed.
It has been found that the values of hardness for the alloys(Al-12.6%Si and Al-7%Si) which poured in
metal mold is greater than the values of hardness for the same alloy when it poured in a heated

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Sat Dec 31 2022
Journal Name
Iraqi Journal Of Market Research And Consumer Protection
EFFECT OF ADDING DIFFERENT LEVELS OF DILL SEEDS TO THE DIET ON PHYSIOLOGICAL TRAITS OF BROILERS : EFFECT OF ADDING DIFFERENT LEVELS OF DILL SEEDS TO THE DIET ON PHYSIOLOGICAL TRAITS OF BROILERS
...Show More Authors

ABSTRACT

This study was conducted in the poultry field of the department of animal production, college of agricultural engineering sciences, university of Baghdad for the period from 10/15/2021 to 11/25/2021 with the aim of showing the effect of adding different levels of dill seeds to the diet on productive and carcass traits For broiler meat. In this study, 200 unsexed broiler chicks of breed (Ross 308) were used, one day age, with a starting weight of 41.46 g. The chicks were randomly distributed to 5 treatments, and each treatment included 4 replicates, 10 birds for each replicate. The birds were fed three diets: the starter diet, the growth diet and the final diet. The experiment treatments were T1,

... Show More
View Publication Preview PDF
Publication Date
Mon Dec 18 2017
Journal Name
Al-khwarizmi Engineering Journal
Effect of Magnesium Addition on Corrosion Resistance of Aluminum -17%Silicon Alloy
...Show More Authors

The electrochemical behavior of Al-17%Si alloy is investigated in 3.5wt% NaCl solution. Many alloys with addition of the different wt% magnesium metal of  1wt%, 2%, 3wt% ,4.5wt% ,and 9wt% were prepared by gravity die casting . The microstructures of prepared alloys were examined by optical and SEM microscopes. Corrosion behavior was investigated by using potentiostat instrument under static potentials test and corrosion current was recorded to determine corrosion resistance of all prepared samples. It was found that the addition of Mg metal improves the corrosion resistance of Al-17%Si alloy in 3.5%NaCl solution. The alloy containing 1%Mg shows less corrosion rate than the others while the alloys containing 4.5%Mg, 9%Mg content have

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Fri Mar 31 2017
Journal Name
Al-khwarizmi Engineering Journal
Mechanical Properties Investigation of Composite Material Under Different Parameters Variations
...Show More Authors

         The main objective of this research is to design and select a composite plate to be used in fabricating wing skins of light unman air vehicle (UAV). The mechanical properties, weight and cost are the basis criteria of this selection. The fiber volume fraction, fillers and type of fiber with three levels for each were considered to optimize the composite plate selection. Finite element method was used to investigate the stress distribution on the wing at cruise flight condition in addition to estimate the maximum stress. An experiments plan has been designed to get the data on the basis of Taguchi technique. The most effective parameters at the process to be find out by employing L9

... Show More
View Publication Preview PDF
Crossref
Publication Date
Thu Jun 30 2011
Journal Name
Al-khwarizmi Engineering Journal
Comparative Study of the Mechanical Properties of (FS) and MIG Welded Joint in (AA7020-T6) Aluminum Alloy
...Show More Authors

A comprehensive practical study of typical mechanical properties of welded Aluminum alloy AA7020-T6 (Al-Mg-Zn), adopting friction stir welding (FSW) technique and conventional metal inert gas (MIG) technique, is well achieved in this work for real comparison purposes. The essences of present output findings were concentrated upon the FSW samples in respect to that MIG ones which can be summarized in the increase of the ultimate tensile strength for FSW was 340 MPa while it was 232 MPa for MIG welding, where it was for base metal 400 MPa. The minimum microhardness value for FSW was recorded at HAZ and it was 133 HV0.05 while it was 70 HV0.05 for MIG weld at the welding metal. The FSW produce 2470 N higher than MIG welding in the bending t

... Show More
View Publication Preview PDF
Publication Date
Sat Jul 19 2025
Journal Name
Journal Of Baghdad College Of Dentistry
The effect of addition nano particle ZrO2 on some properties of autoclave processed heat cure acrylic denture base material
...Show More Authors

Background: Polymethyl methacrylate (PMMA) is used in denture fabrication and considered as the most reliable material for the construction of removable prosthodontic appliances. The material is far from ideal in fulfilling the mechanical requirements and the effect of autoclave processing has not been fully determined. The purpose of this study was to evaluate the effect of addition of salinized (ZrO2) Nano fillers in percentages 3%, 5% and 7% by weight on some properties of heat cured acrylic processed the by autoclave and compare it with 0% (control) group . Materials and methods: The silanized(ZrO2) Nano-particles was added to PMMA powder by weight in three different percentages 3%, 5% and 7%, mixed by probe ultra-sonication machine.

... Show More
View Publication Preview PDF
Publication Date
Sun Nov 01 2015
Journal Name
Journal Of Engineering
Effect of Wood Flour Addition on the Pore Volume and BET Surface Area Properties of the Prepared Gamma Alumina (ɤ-Al2O3) Extrudates Used in Catalyst Carriers
...Show More Authors

The effect of Wood Flour addition to the gamma alumina powder used in the preparation of gamma alumina (ɤ-Al2O3) catalyst carrier extrudates on the pore volume and BET surface area physical properties was investigated. Two parameters which are size of wood flour particles and its quantity were studied. The sizes of wood flour particles used are 150 µm, 212 µm and 500 µm and the weight percentage added to the gamma alumina powder during the preparation of the extrudates are (1%, 3%, 5% and 10%). The results showed that the addition of wood flour to the gamma alumina powder in order to get gamma alumina extrudates used as catalyst carrier is one of the successful methods to improve the pore volume