Abstract

One of the most suitable materials to be used in latent heat thermal energy storage system (LHTES) are Phase change materials, but a problem of slow melting and solidification processes made many researchers focusing on how to improve their thermal properties. This experimental work concerned with the enhancing of thermal conductivity of phase change material. The enhancing method was by the addition of copper Lessing rings in phase change material (paraffin wax). The effect of diameter for the used rings was studied by using two different diameters (0.5 cm and 1cm). Also, three volumetric percentages of rings addition (3%, 6% and 10%) were tested for each diameter. The discharging process was done with

The research presented the tagged (aesthetic and expressive characteristics in the works of Jean Dubuffet), so the research objective was: to know the aesthetic and expressive characteristics in the works of (Jean Dubuffet), and the research included four chapters. The aim of the research, the limits of the research, and the definition of terms. The second chapter included four topics. The first topic presented the aesthetic essence and style, while the second topic dealt with expressionism: approaches in concept and meaning.
While the third topic was preoccupied with presenting the aesthetic and expressiveness in the drawings of modernity and beyond, while the fourth topic dealt with: Jean Dubuffet and the experience of raw art. Th

Double hydrothermal method was used to prepare nano gamma alumina   using aluminum nitrate nano hydrate and sodium aluminate as an aluminum source, CTAB (cetyltrimethylammonium bromide) as surfactant, and variable acids: weak acids like; citric, and acitic acids, and strong acids like; hydrochloric and nitric acids as a bridge between aluminum salts and surfactant. Different crystallization times  12, 24, 48, and 72 hrs were applied. All the batches were prepared at pH equals to 9. XRD diffraction technique was used to investigate the crystalline nano gamma alumina pure from surfactant. N₂ adsorption-desorption (BET) was used to measure the surface area and pore volume of the prepared nano alumina, the average p

I mpact strength for Epoxy/Polyurethane, Blends and their composites with two
layers of Glass fibers (0-90) are calculated.
The impact strength of the blends and composites decrease with increasing weight
by weisht percentage of polyurethane . This result is attributed to the high elasticity
of PU , and to the immiscibility between the polymer blends as well as the fiber
delaminates

In  this  work,  three  inorganic  additives were 1,1sed,  these  are  (I)  ;

tetraethyl ammonium bromodichloro phenylphsphin, (II) Chlorinated paraffine. and (ITI) a mixture  of  (50%  by weight  of each) to study the synergetic effect.  These  additives \'v·cre used  as flame retardants with unsaturated  polyester  and  epoxy  resins.;, since  these  resins  are industrially important  and of \Vide uses in life.

Results showed efficiency of these  additives to retard  fl mmabillty and stop burning of resins throqght the ASTM tests used Measurement of Limiting oxygen  index (LOI), &nbs

Glucoamylase from black Aspergillus niger isolate was purified by ammonium sulfate precipitation and sephadex G 200 filtration. A trial for the purification of glucoamylase resulted in an enzyme with a specific activity of 6472 unit/mg protein with 10 times fold. The main goal of the present work was to test this enzyme in hydrolyzing the raw starch. Two substrates were used: corn starch and potato starch 2% (w/v). The effect of enzyme dosage and thermal processing of substrate on kinetics and efficiency of hydrolysis were studied. The results suggested that the glucoamylase activity is increased as the increase of enzyme concentration and the enzyme was sufficiently effective in hydrolyzing tested raw starch, and thermal modification of

     Zinc oxide films (ZnO) are prepared by an electrolysis technique and without vacuum and then annealed atvarious temperatures (300,400,500)^OC for an hour. The structural analysis performed by X-Ray diffraction (XRD) shows,dominant orientation of this films is plane (101), has a hexagonal structure and  polycrystalline pattern and it was is found that the crystal size increases(24,29) nm at annealing temperatures (300, 400)° C, but the crystal size decreases to (20 nm) at annealing temperature (500 ° C). As the results of a surface nature study of these films showed by examining the atomic force microscope (AFM), the grain  size increases from (60.79 to 88.11) nm, and the surface roughnes