The corrosion behavior of 2024 aluminium alloy was investigated in alkaline medium (pH=13) containing 0.6 . in absence and presence of different concentrations of three amino acids separately [Methionine, Glutamice acid and Lysine] as environmentally friendly corrosion inhibitors over the temperature range (293-308)K. Electrochemical polarization method using potentiostatic technique was employed. The inhibition efficiency increased with an increase of the inhibitor concentration but decreased with increase in temperature . The maximum efficiency value was found with lysine =80.4 of 293 k and 10 . concentration of lysine. The adsorption of the amino acids was found to obey Langmuir adsorption isotherm . Some thermodynamic parameter âˆ

The turning process has various factors, which affecting machinability and should be investigated. These are surface roughness, tool life, power consumption, cutting temperature, machining force components, tool wear, and chip thickness ratio. These factors made the process nonlinear and complicated. This work aims to build neural network models to correlate the cutting parameters, namely cutting speed, depth of cut and feed rate, to the machining force and chip thickness ratio. The turning process was performed on high strength aluminum alloy 7075-T6. Three radial basis neural networks are constructed for cutting force, passive force, and feed force. In addition, a radial basis network is constructed to model the chip thickness ratio. T

Corrosion Resistance Enhancement for low carbon steel is very important to extend its life service, the coating process is one of the methods which can using to achieve this, and it's the most important in surface treatments to improve the properties of metals and alloys surfaces such as corrosion resistance. In this work, low carbon steel was nitrided and coated with nano zinc using gas phase coating technical, to enhance the resistance of corrosion. The process included adding two layers. The first, a nitride layer, was added by precipitating nitrogen (N) gas, and the second, a zinc (Zn) layer, was added by precipitating Zn. The process of precipitating was carried out at different periods (5, 10, and 15 minutes). Scan electron mi

Thermal conductivity for epoxy composites filled with Al2O3 and Fe2O3 are
calculated, it found that increasing the weight ratio of Al2O3 and Fe2O3 lead to
increase in the values of thermal conductivity, but the epoxy composite filled with
Fe2O3, have values of thermal conductivity less than for epoxy composite filled with
Al2O3, for the same weight ratio. Also thermal conductivity calculated for epoxy
composites by contact to every two specimens (like sandwich) content same weight
ratio of alumina-oxide and ferrite-oxide, its found that the value of thermal
conductivity lays between the values of epoxy filled Al2O3 and of epoxy filled Fe2O3

This work involved the co-substitution of the two bioactive ions of strontium and magnesium into the hydroxyapatite (HA) coating which was then electrochemically deposited on Ti-6Al-4V ELI dental alloy (Gr.23) before and after treatment by Micro Arc Oxidation (MAO). The deposited layers were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). The adhesion strength of the coating layer was estimated by using pull-off adhesion test. The adhesion strength of Sr/Mg-HA on the Ti-6Al-4V ELI dental alloy after MAO treatment was 1.79 MPa, which was higher than that before MAO treatment (1.62 MPa). The corrosion behavior of th

This experiment was conducted to examine the effects of injected gibberellic acid GA3 in subcutaneous of hens neck and supplemental vitamin D3 to control basal diet on productive performance and egg shell thickness ,relative weight of egg shell of aged laying hens. Two hundred and seventy Lohmann Brown laying hens at 73 weeks of age were randomly assigned to three treatments groups. Each treatment consist of three replicates (30 hens / replicate). The treatments were : T1 control were injected subcutaneous with 0.2 ml / kg of body weight of ethanol: sesame oil solution, T2 and T3 were injected subcutaneous with 0.2 ml / kg of body weight of ethanol: sesame oil solution which contained 400 μg GA3/ kg of body weight /week during 8 weeks (tre

The importance of internal audit in the growing demand for services in the public and private economic units, and in the rapid growth of its systems professional, has also been recognition of the importance of internal audit quality and the quality of information provided in a long time, as well as the importance of achieving the greatest possible quality in his work to reduce accounting risks of financial reports misleading or fraudulent, which is one of the important features of the audit.

The internal audit quality are linked with the ability of auditors to detect errors in the financial statements, and their willingness to express an opinion technical neutral and non-aligned based on the results of th

Background: Deterioration of maxillofacial silicone properties due to microbial colonization is a common problem and leads to the replacement of the prosthesis. Incorporation of the antimicrobial agent into the silicone could be a solution. The purpose of this study was to evaluate the effect of silver-zinc zeolite addition on some mechanical properties of a maxillofacial silicone (VST-50). Materials and methods: Total 120 specimens were fabricated and divided into 3 groups: 40 specimens for tear strength test, 40 specimens for tensile and percentage of elongation tests and 40 specimens for Shore A hardness and surface roughness. Each group was divided into 4 subgroups according to the amount of zeolite added (0% “control”, 0.5%, 1% and

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.
Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.