Polycrystalline Cadmium Oxide (CdO) thin films were prepared
using pulsed laser deposition onto glass substrates at room
temperature with different thicknesses of (300, 350 and 400)nm,
these films were irradiated with cesium-137(Cs-137) radiation. The
thickness and irradiation effects on structural and optical properties
were studied. It is observed by XRD results that films are
polycrystalline before and after irradiation, with cubic structure and
show preferential growth along (111) and (200) directions. The
crystallite sizes increases with increasing of thickness, and decreases
with gamma radiation, which are found to be within the range
(23.84-4.52) nm and (41.44-4.974)nm before and after irradiation for

Polycrystalline Cadmium Oxide (CdO) thin films were prepared using pulsed laser deposition onto glass substrates at room temperature with different thicknesses of (300, 350 and 400)nm, these films were irradiated with cesium-137(Cs-137) radiation. The thickness and irradiation effects on structural and optical properties were studied. It is observed by XRD results that films are polycrystalline before and after irradiation, with cubic structure and show preferential growth along (111) and (200) directions. The crystallite sizes increases with increasing of thickness, and decreases with gamma radiation, which are found to be within the range (23.84-4.52) nm and (41.44-4.974)nm before and after irradiation for thickness 350nm and 4

The antioxidant and antibacterial activities of ethanolic extract and phenolic compounds extract of Lemon balm (Melissa officinalis) and Oregano (Oreganum vulgare) plants were studied; the phenolic content and the relationship between these compounds and the above activities were also investigated. The results showed that the Lemon balm had the highest phenolic content (56.5% mg g) and the phenolic content of Oregano was twice lower than Lemon balm. Lemon balm has the highest antioxidant activity which causes lipid peroxidation inhibition activity of linoleic acid (90.5%), this activity was more than ?-tocopherole antioxidant activity (79.3 %). It was found that the main source of antioxidant activity o

In this work we used the environmentally friendly method to prepared ZrO2 nanoparticles utilizing the extract of Thyms plant In basic medium and at pH 12, the ZrO2 NPs was characterized by different techniques such as FTIR, ultraviolet visible, Atomic force microscope, Scanning Electron Microscopy, X-ray diffraction and Energy dispersive X-ray. The average crystalline size was calculated using the Debye Scherres equation in value 7.65 nm. Atomic force microscope results showed the size values for ZrO2 NPs were 45.11nm, and there are several distortions due to the presence of some large sizes. Atomic force microscope results showed the typical size values for ZrO2 NPs were 45.11 nm, and there are several distortions due to the presence of so

Abstract

In this manuscript, a simple new method for the green synthesis of platinum nanoparticles (Pt NPs) utilizing F. carica Fig extract as reducing agent for antimicrobial activities was reported. Simultaneously, the microstructural and morphological features of the synthesized Pt NPs were thoroughly investigated. In particular, the attained Pt NPs exhibited spherical shape with diameter range of 5-30 nm and root mean square of 9.48 nm using Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM), respectively. Additionally, the final product (Pt NPs) was screened as antifungal and antibacterial agent against Candida and Aspergillus species as well as Gram-positive Staphyllococcus aureus and G

Wastewater discharge containing organic dyes may pose a hazard to the environment, which necessitates that dye removal must occur prior to wastewater release into water bodies. Herein, copper oxide nanoparticles (CuO NPs) were prepared by a green precipitation method to enable decolorization of a cationic dye (methyl violet; MV) from aqueous media. Complementary tools were employed to characterize the CuO NPs adsorbent: spectroscopy (FTIR and UV-VIS), microscopy (FESEM and TEM), XRD, BET surface area analysis, and point of zero charge (pHPZC) via potentiometry. The FTIR bands at 722, 663, 569, and 465 cm−1 correspond to the vibrational modes of CuO NPs, along with the optical absorbance band at 275 nm that supports the formation of Cu