The current research reports the preparation and fabrication of the silver paste conductor which is employed as a soldering material for electro – optical components ohmic interconnections. The prepared paste possesses electrical characteristics identical to the ohmic connectors as its observable from resistance – temperature variation. Moreover, the I – V characteristics obeys Ohm’s law and this dependency was further confirmed by the nearly constant capacitance measurements with voltage and frequency. A noticeable improvement in electrical conductivity, compared to the pure silver paste sample, was noted for samples prepared by mixing predetermined weight ratios of brass and copper. Furthermore, stability of electrical resistan

The corrosion of carbon steel in single phase (water with 0.1N NaCl ) and two immiscible phases (kerosene-water) using turbulently agitated system is investigated. The experiments are carried out for Reynolds number (Re) range of 38000 to 95000 corresponding  to rotational velocities from 600 to 1400 rpm using circular disk turbine agitator at 40 0C. In two-phase system test runs are carried out in aqueous phase (water) concentrations of 1 % vol., 5 % vol., 8% vol., and 16% vol. mixed with kerosene at various Re. The effect of Reynolds number (Re), percent of dispersed phase, dispersed drops diameter, and number of drops per unit volume on the corrosion rate is investigated and discussed. Test runs are carried out using two types of

The objective of the current research is to find an optimum design of hybrid laminated moderate thick composite plates with static constraint. The stacking sequence and ply angle is required for optimization to achieve minimum deflection for hybrid laminated composite plates consist of glass and carbon long fibers reinforcements that impeded in epoxy matrix with known plates dimension and loading. The analysis of plate is by adopting the first-order shear deformation theory and using Navier's solution with Genetic Algorithm to approach the current objective. A program written with MATLAB to find best stacking sequence and ply angles that give minimum deflection, and the results comparing with ANSYS.

Heterocyclic compounds are crucial for medicinal chemistry and the development of therapeutic agents like broad-spectrum antibiotics. This study devised a facile procedure to synthesize novel antimicrobial bicyclic heterocycles from 2-mercapto-3-phenylquinazolin-4(3H)-one. Advanced analytical techniques including 1 H and 13C NMR, elemental analysis, and FT-IR spectroscopy characterized the intricate chemical structures of the products. In vitro assays tested the heterocycles against aerobic and anaerobic bacterial strains using fluconazole and ciprofloxacin as antifungal and antibacterial controls. Results demonstrated the formidable broad-spectrum antibacterial and antifungal activities of the synthesized compounds, with growth inhibition

New polymer blend with enhanced properties was prepared from (80 %) epoxy resin (Ep), (20%) unsaturated polyester resin (UPE) as a matrix material. The as-obtained polymer blend was further reinforced by adding Sand particles of particle size (53 μm) with various weight fraction (5, 10, 15, 20 %). Thermal conductivity and sorption measurements are performed in order to determine diffusion coefficient in different chemical solutions (NaOH, HCl) with concentration (0.3N) after immersion for specific period of time (30 days). The obtained results demonstrate that the addition of sand powder to (80%EP/20%UPE) blend leads to an increase of thermal conductivity, with an optimum/minimum diffusion coefficient in (HCl)/(NaOH), respectively.

The synthesis of the bisaldehyde ligand 2-(1,1-dimethyl-1,3-dihydro-2H-benzo[e]indol-2-ylidene)malonaldehyde (B) and its coordinated compounds with Cr(III), Mn(II), Fe(II), Co(II), Ni(II) and Cu(II) ions are reported. The synthetic route of B was completed by adopting the Vilsmeier-Haack reaction. This was based on the mixing of 1,1,2-trimethyl-1H-benzo[e]indole with phosphoryl trichloride and N, N-dimethylformamide (anhydrous) that gave the aminomethylenemalondialdehyde. The use of POCl3 and DMF was aimed to give the Vilsmeier-Haack intermediate, which was kept at 5°C and then heated with stirring at 85°C. The addition of an aqueous NaOH solution (35%) to the reaction mixture resulted in the isolation of B. The monomeric coordinated comp

The study involved the effectiveness of Iraqi attapulgite (IQATP) clay as an environmentally friendly material that easily adsorbs brilliant green (BG) dye from water systems and is identified by various complementary methods (e.g., FTIR, SEM‐EDS, XRD, ICP‐OES, pH_pzc, and BET), where the result reported that the IQATP specific surface area is 29.15 m²/g. A systematic analysis was selected to evaluate the impact of different effective adsorption performance variables on BG dye decontamination. These variables included IQATP dosage (0.02–0.8 g/L), solution pH (3.05–8.15), contact time (ranging from 2 to 25 min), and initial BG dye concentration from 20 to 80 mg/L. The parameter

The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m²/g, and pore volume 0.231 cm³/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst ty