A thin CdS Films have been evaporated by thermal evaporation technique with different thicknesses (500, 1000, 1500 and 2000Å) and different duration times of annealing (60, 120 180 minutes) under 573 K annealing temperature, the vacuum was about 8 × 10-5 mbar and substrate temperature was 423 K. The structural properties of the films have been studied by X- ray diffraction technique (XRD). The crystal growth became stronger and more oriented as the film thickness (T) and duration time of annealing ( Ta) increases.

Copper oxide thin films were deposited on glass substrate using Successive Ionic Layer Adsorption and Reaction (SILAR) method at room temperature. The thickness of the thin films was around 0.43?m.Copper oxide thin films were annealed in air at (200, 300 and 400°C for 45min.The film structure properties were characterized by x-ray diffraction (XRD). XRD patterns indicated the presence of polycrystalline CuO. The average grain size is calculated from the X-rays pattern, it is found that the grain size increased with increasing annealing temperature. Optical transmitter microscope (OTM) and atomic force microscope (AFM) was also used. Direct band gap values of 2.2 eV for an annealed sample and (2, 1.5, 1.4) eV at 200, 300,400oC respect

In this study is the phenomenon of desertification risk assessment in the Abu Ghraib area west of Baghdad/Iraq, which has an area of about (384.168 km 2), that the annual mean temperature is more than (22 C). Rainfall was low, ranging from the (200 mm) per year for Iraq and (2.82) mm per year of the study area* temperature is high and evaporation is also high (mm 7.73) per year*, so the climate in general of the dry type and the system of soil moisture is the kind of Aridic (Torric). To this study was to identify three indicators to monitor for the period from 2001-2005 using GIS and these indicators are (soil, groundwater and the nature of land use), using ArcGIS 9.1. The results showed that the risk of desertification was part of the leve

Therapeutic contact lenses TCLs is an approach used to enhance corneal residence time and reduce frequent instillation, which is a problem with eye drops.  The problem with CLs is loading of hydrophobic drugs. In this research the CLs were prepared with molecular imprinting MI to enhance the loading of itraconazole, which is used as antifungal drug for fungal keratitis. CLs using different  concentration of hydroxyethyl methacrylate HEMA and methacrylic acid MAA were prepared with and without MI using PEGDA (25 μL) and AIBN (37 mg) as crosslinker and initiator respectively. All the prepared CLs were clear and have good folding endurance. MICLs had significantly higher drug loading compared to conventional CLs. The release of i

The triggering effect for the face pumping of Nd:YVO₄ disc medium of 4×5×0.5 mm was investigated using bulk diode laser at different resonator cavity length in pulse mode and at repetition rate of 1.3kHz. The maximum emitted peak power was found to be 100, 82, and 66 mW for resonator lengths of 10, 13.5, and 17.5 cm respectively, while the threshold pumping power was found to be 41mW. The maximum emitted peak power obtained was 300 mW when using external triggering and 10cm length, with repetition of 3Hz.

Objective: The aim of this study was to evaluate the effect of pumice, burning investment material
and black sand on the surface roughness of heat cure acrylic resin.
Methodology: Sixty specimens were prepared from pink heat cure acrylic resin, the specimens
where grouped into; 20 specimens which polished with pumice and water (control group); 20
specimens which polished with investment material (after burning it) and water; and 20 specimens
which polished with black sand and water. The average surface roughness of specimens after
polishing procedure had been determined by profilometer (surface roughness tester).
Results: Through the application of ANOVA and LSD tests, the result of this study showed that there
wa

Thermal conductivity for epoxy composites filled with Al2O3 and Fe2O3 are
calculated, it found that increasing the weight ratio of Al2O3 and Fe2O3 lead to
increase in the values of thermal conductivity, but the epoxy composite filled with
Fe2O3, have values of thermal conductivity less than for epoxy composite filled with
Al2O3, for the same weight ratio. Also thermal conductivity calculated for epoxy
composites by contact to every two specimens (like sandwich) content same weight
ratio of alumina-oxide and ferrite-oxide, its found that the value of thermal
conductivity lays between the values of epoxy filled Al2O3 and of epoxy filled Fe2O3