Conducting polyaniline / ZnO nano composites are synthesized
using a simplified cheap method with one step in –situ chemical
polymerization, and AC conductivity (σac) of the prepared samples is
studied in the range of frequency from 50 Hz to 15MHz.). The
presence of polarons in the conjugated polymer chain are responsible
for the ac conductivity is reliance on the frequency in these
composites. The effect of increasing the ZnO nano particle
concentration irradiation and gamma radiation on the electric
conductivity was analyzed. The result showed that the
nanocomposite prepared has the highest conductivity, from pure
polyaniline and the exponential factor S was found increasing with
ZnO content it was 0

The whole research paper examines the impact of ozone as either a just use-alone and coagulation benefit, mainly upon the reduction of dissolved organic carbon from the water with a moderate rate of DOC 10.75 mg/land CaCO3 calcium hardness 300 mg/l. A raw water sample has been taken from the Tigris River (Baghdad, Iraq) was being adopted in research work. The performance of ozone therapy has been assessed by calculations of DOC, DOC quantities, UV254, as well as total trihalomethane (TTHM). Research findings have shown that with 0.9 mg O3/mg DOC ozone use-alone, approximately 60% UV254 reduction and approximately 28% DOC reduction will occur.DOC fractionation analysis indicates that within the water samples, ozone could alter the co

Background : Shoulder pain is a common problem that can pose difficult diagnostic and therapeutic challenges for the family physician It is the third most common musculoskeletal complaint in the general population, and account for 5% of all general practitioners musculoskeletal consults Objective: To determine the diagnostic performance of ultrasonography compared with the physical examination for detection of rotator cuff tears in painful shoulder syndrome. Method: Prospective study was done on seventy patients (48 male, 22 female), age ranged between 30-70 years (mean age 50 years), From February 2007 to July 2011, were subjected to comparative study in Al-Kindy teaching hospital with rotator cuff tears, including physical and ultrasonogr

Background: Cyclin D1 proto-oncogene is an important regulator of (G1 to S) phase progression in many different cell types. The Aims of this study were to evaluate the immunohistochemical expression of Cyclin D1 in mucoepidermoid and adenoid cystic carcinoma of the salivary glands and to correlate the immunoexpression of this protein with the clinicopathological findings. Materials and methods Retrospectively, twelve of archival formalin fixed paraffin embedded tissue samples of salivary Mucoepidermoid and fourteen blocks of adenoid cystic carcinomas obtained from the archives of the department of oral pathology / college of dentistry / Baghdad university, Al-Shaheed Ghazi hospital, were included in this study. Five micrometer sections o

Piroxicam is a non-steroidal anti-inflammatory drug (NSAID) used in the treatment of musculo-skeletal and joint disorders. The problem with this drug is its poor solubility in water and hence poor bioavailability after oral administration. In order to improve its solubility and dissolution behavior, hydrophilic additives such as starch, lactose, superdisintegrants including crospovidone (C.P), cross carmellose sodium (CCS), and sodium starch glycolate (SSG) were physically dry mixed with the drug by simple trituration. The improvement in the solubility in 0.1 N HCl was obtained as the amount of starch or lactose increased in the physical mixture, while for superdisintegrants, they further improve the solubility when they are present in s

Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

In this work, 332 Al alloy was prepared and reinforced with (0.5% and 1%) nano-Al₂O₃ particles. The prepared unreinforced and reinforced 332 Al alloy with nano-Al₂O₃ were solution heat treated (T6) at 510 ̊C and aged at 225 ̊C with different times (1, 3, and 5 h). Hardness test was performed on all the prepared alloys. All prepared alloys were dry slided under different applied loads (5, 10, 15, and 20 N) against steel counterface surface using pin on disk apparatus. The results showed that refinement effect was observed after addition of nano-Al₂O₃ particles and a change in silicon morphology after performing the solution heat treatment. The results also showed that har

Effect of the thermal annealing at 400oC for 2 hours and Argon laser radiation for half hour on the optical properties of AgAlS2 thin films, prepared on glass slides by chemical spray pyrolysis at 360oC with (0.18±0.05) μm thickness .The optical characteristics of the prepared thin films have been investigated by UV/Vis spectrophotometer in the wavelength range (300 – 1100)nm .The films have a direct allow electronic transition with optical energy (Eg) values decreased from (2.25) eV for untreated thin films to (2.10) eV for the annealed films and to (2.00) eV for the radiated films. The maximum value of the refractive index (n) for all thin films are given about (2.6). Also the extinction coefficient (K) and the real and imaginary d