Density functional theory calculations are employed to investigate the impact of edifenphos molecule on the reactivity and electronic sensitivity of pure calcium oxide (CaO) nanocluster. The strong adsorption of edifenphos molecule on CaO nanocluster occurs by the sulfur head of the adsorbate, and the amount of the energy of this adsorption is around − 84.40 kcal/mol. The adsorption of edifenphos molecules results in a decrease in the values of Eg of CaO from 4.67 to 3.56 eV, as well as an increase in the electrical conductance. Moreover, the work function of CaO nanocluster is significantly affected, which changes the current of the field emission electron. Eventually, the recovery time is calculated around 99 ms at ambient temperature f

Pure and doped TiO 2 with Bi films are obtained by pulse laser deposition technique at RT under vacume 10-3 mbar, and the influence of Bi content on the photocvoltaic properties of TiO 2 hetrojunctions is studied. All the films display photovoltaic in the near visible region. A broad double peaks are observed around λ= 300nm for pure TiO 2 at RT in the spectral response of the photocurrent, which corresponds approximately to the absorption edge and this peak shift to higher wavelength (600 nm) when Bi content increase by 7% then decrease by 9%. The result is confirmed with the decreasing of the energy gap in optical properties. Also, the increasing is due to an increase in the amount of Bi content, and shifted to 400nm when annealed at 523

In this study, gold nanoparticle samples were prepared by the chemical reduction method (seed-growth) with 4 ratios (10, 12, 15 and 18) ml of seed, and the growth was stationary at 40 ml. The optical and structural properties of these samples were studied. The 18 ml seed sample showed the highest absorbance. The X- ray diffraction (XRD) patterns of these samples showed clear peaks at (38.25^o, 44.5^o, 64.4^o, and 77.95^o). The UV-visible showed that the absorbance of all the samples was in the same range as the standard AuNPs. The field emission-scanning electron microscope (FE-SEM) showed the shape of AuNPs as nanorods and the particle size between 30-50 nm. Rhodamine-610 (RhB) was prepared at 10<

Experimentation Multi effective and fertile grew human desire to discover new ways to express beauty in artwork .And dabble term experimentation in the performing arts and arts architecture, cinema and television in the test forms and interest in the visual effects and movements seek to establish and beauty and schools of thought in literature and art. This study aims to identify

Optical detector was manufactured Bashaddam thermal evaporation technique at room temperature under pressure rays studied characteristics of reactive Scout efficiency quantitative ratio of the signal and the ability equivalent to noise

The research consisted of four chapters, the first of which wasa methodological framework. The problem of research was determined by a question drawn up by the researcher as follows: What are the intellectual contents of science fiction films ?. The main objective of the research was to uncover the intellectual contents of contemporary science fiction films. The most important research terms (content, thought, ideology, science fiction, contemporary) were defined as either the second chapter (the theoretical framework) The second topic was entitled "The Intellectual Contents of Contemporary Science Fiction Films", in which the films of the science fiction and its current intellectual contents were discussed. The third topic included the

In this work, magnesium aluminate spinel (MA) (MgO 28 wt%, Al2O3 72 wt%) stoichiometric compound , were synthesized via solid state reaction (SSR) Single firing stage, and the impact of sintering on the physical properties and thermal properties as well as the fine structure and morphology of the ceramic product were examined. The Spinel samples were pressed at of (14 MPa) and sintering soaking time (2h). The effect of adding oxide titania (TiO2) was studied. The obtained powders were calcined at a temperature range of 1200 and 1400 °C. The calcined samples spinel were characterized by XRD, it showed the presence of developed spinel phase end also showed that the best catalyst is titania. The SEM image showed the high sintering temperat