Burnishing improves fatigue strength, surface hardness and decrease surface roughness of metal because this process transforms tensile residual stresses into compressive residual stresses. Roller burnishing tool is used in the present work on low carbon steel (AISI 1008) specimens. In this work, different experiments were used to study the influence of feed parameter and speed parameter in burnishing process on fatigue strength, surface roughness and surface hardness of low carbon steel (AISI 1008) specimens. The first parameter used is feed values which were (0.6, 0.8, and 1) mm at constant speed (370) rpm, while the second parameter used is speed at values (540, 800 and 1200) rpm and at constant feed (1) mm. The results of the fatigue

This research aims to test the ability of glass waste powder to adsorb cadmium from aqueous solutions. The glass wastes were collected from the Glass Manufacturing Factory in Ramadi. The effect of concentration and reaction time on sorption was tested through a series of laboratory experiments. Four Cd concentrations (20, 40, 60, and 80) as each concentration was tested ten times for 5, 10, 15, 20, 25, 30, 35, 40, 45, and 50 min. Solid (glass wastes) to liquid was 2g to 30ml was fixed in each experiment where the total volume of the solution was 30ml. The pH, total dissolved salts and electrical conductivity were measured at 30ºC. The equilibrium concentration was determined at 25 minutes, thereafter it was noted that the sorption

Membrane manufacturing system was operated using dry/wet phase inversion process. A sample of hollow fiber membrane was prepared using (17% wt PVC) polyvinyl chloride as membrane material and N, N Dimethylacetamide (DMAC) as solvent in the first run and the second run was made using (DMAC/Acetone) of ratio 3.4 w/w. Scanning electron microscope (SEM) was used to predict the structure and dimensions of hollow fiber membranes prepared. The ultrafiltration experiments were performed using soluble polymeric solute poly ethylene glycol (PEG) of molecular weight (20000 Dalton) 800 ppm solution 25 °C temperature and 1 bar pressure. The experimental results show that pure water permeation increased from 25.7 to 32.2 (L/m2.h.bar) by adding a

Membrane manufacturing system was operated using dry/wet phase inversion process. A sample of hollow fiber membrane was prepared using (17% wt PVC) polyvinyl chloride as membrane material and N, N Dimethylacetamide (DMAC) as solvent in the first run and the second run was made using (DMAC/Acetone) of ratio 3.4 w/w. Scanning electron microscope (SEM) was used to predict the structure and dimensions of hollow fiber membranes prepared. The ultrafiltration experiments were performed using soluble polymeric solute poly ethylene glycol (PEG) of molecular weight (20000 Dalton) 800 ppm solution 25 °C temperature and 1 bar pressure. The experimental results show that pure water permeation increased from 25.7 to 32.2 (L/m2.h.bar) by adding aceton

    The characterization and design of this study of new liquid crystals with a V shape compounds containing thiazolidine-2,4-dione and 1,3-phenylene as a core unite with mesophase properties were reported. Preparation  and characterization of chloroacetic acid, water, and thiourea to produce thiazolidine-2,4-dione [I] in the presence of strong hydrochloric acid. The 4-hydreoxybenzaldehyde and n-alkyl bromide were reacted with potassium hydroxide to create the n-alkoxy benzaldehyde., then the compound [I] reacted with [II]n in presence of piperidine to produce compounds [III]n. Also, converted resorcinol to a corresponding  compound [IV] by refl

    The characterization and design of this study of new liquid crystals with a V shape compounds containing thiazolidine-2,4-dione and 1,3-phenylene as a core unite with mesophase properties were reported. Preparation  and characterization of chloroacetic acid, water, and thiourea to produce thiazolidine-2,4-dione [I] in the presence of strong hydrochloric acid. The 4-hydreoxybenzaldehyde and n-alkyl bromide were reacted with potassium hydroxide to create the n-alkoxy benzaldehyde., then the compound [I] reacted with [II]_n in presence of piperidine to produce compounds [III]_n. Also, converted resorcinol to a corresponding  compound [IV] by refluxing pyridine and DMF with two moles of chlora

Some new 2,5-disubsituted-1,3,4-oxadiazole derivatives with azo group were synthesized by known reactions sequence . The structure of the synthesized compounds were confirmed by physical and spectral means .

Oral jelly is a semisolid preparation that could resolve problem associated withdosage form’s swallowing, especially in pediatric and elderly ones. This work aimedto prepare oral flurbiprofen (FBP) jelly to improve patient compliance. Heating andcongealing method was used to prepare FBP jelly using three different polymers (pectin,sodium carboxymethyl cellulose, and hydroxypropyl methylcellulose). The effect ofdifferent concentrations of pectin and sucrose on jelly properties was studied. Theresults revealed that both pectin and sodium carboxymethyl cellulose polymers gaveacceptable jelly appearance and consistency. It was also observed that the increase ofpectin or sucrose concentration had a significant impact on jelly viscosity. All pe