High Speed Shock Peening by Fiber Laser for Al Alloy 6061-T6 Thin Sheets

Under cyclic loading, aluminum alloys exhibit less fatigue life than steel alloys of similar strength and this is considered as Achilles's heel of such alloys. A nanosecond fiber laser was used to apply high speed laser shock peening process on thin aluminum plates in order to enhance the fatigue life by introducing compressive residual stresses. The effect of three working parameters namely the pulse repetition rate (PRR), spot size (ω) and scanning speed (v) on limiting the fatigue failure was investigated. The optimum results, represented by the longer fatigue life, were at PRR of 22.5 kHz, ω of 0.04 mm and at both v's of 200 and 500 mm/sec. The research yielded significant results represented by a maximum percentage increase in the fatigue life of 505.25% accompanied by the least deformation for the processed surfaces. SEM images for the specimens processed by the optimum process conditions imply no ablation has occurred at the surface, and the process is completely cold. X-ray diffraction analysis indicates a reduction in grains size, an increase of 28.56% in the lengths of dislocations and formation of effective compressive residual stress at the surface and beneath reaches to 700 μm.

Scopus Clarivate Crossref
View Publication
Publication Date
Wed Jun 16 2021
Journal Name
Application Of Optical Fiber In Engineering
Modified Single Mode Optical Fiber Ammonia Sensors Deploying PANI Thin Films

Modified optical fiber sensors received increasing attention because of their superior properties over electrical sensors. These properties include their immunity towards electromagnetic interference and the ability to be deployed in corrosive and volatile environment. Several optical fiber platforms have been developed for chemical sensing applications based on modifying optical fiber cladding layer such as etched, tapered, D-shaped and etched-tapered. The modifications purpose is to extend the evanescent wave propagating out of the core physical dimensions. Thus, evanescent wave interaction with analyte is enhanced. Modified optical transducing platforms are integrated in gas sensing applications, such as ammonia. Modified optical

... Show More
View Publication
Crossref (1)
Crossref
Publication Date
Tue Jan 08 2019
Journal Name
Iraqi Journal Of Physics
Study of structural, optical and electrical properties of thin Ag2Cu2O4 films prepared by pulsed laser deposition

The influence of sintering and annealing temperatures on the structural, surface morphology, and optical properties of Ag2Cu2O4 thin films which deposited on glass substrates by pulsed laser deposition method have been studied. Ag2Cu2O4 powders have polycrystalline structure, and the Ag2Cu2O4 phase was appear as low intensity peak at 35.57o which correspond the reflection from (110) plane. Scan electron microscopy images of Ag2Cu2O4 powder has been showed agglomerate of oxide particles with platelets shape. The structure of thin films has been improved with annealing temperature. Atomic Force micrographs of Ag2Cu2O4 films showed uniform, homogenous films and the shape of grains was almost spherical and larger grain size of 97.85 nm has o

... Show More
View Publication Preview PDF
Crossref
Publication Date
Mon Feb 04 2019
Journal Name
Iraqi Journal Of Physics
Structural and optical properties of CdO and CdO0.99Cu0.01 thin films prepared by pulsed laser deposition technique

Structural and optical properties of CdO and CdO0.99Cu0.01 thin
films were prepared in this work. Cadmium Oxide (CdO) and
CdO0.99Cu0.01semiconducting films are deposited on glass substrates
by using pulsed laser deposition method (PLD) using SHG with Qswitched
Nd:YAG pulsed laser operation at 1064nm in 6x10-2 mbar
vacuum condition and frequency 6 Hz. CdO and CdO0.99Cu0.01 thin
films annealed at 550 C̊ for 12 min. The crystalline structure was
studied by X-ray diffraction (XRD) method and atomic force
microscope (AFM). It shows that the films are polycrystalline.
Optical properties of thin films were analyzed. The direct band gap
energy of CdO and CdO0.99Cu0.01 thin films were determined from
(αhυ)1/2 v

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Wed Jun 01 2022
Journal Name
Iraqi Journal Of Physics
Synthesis and Characterization of Ternary BexZn1-xO Nano Thin Films prepared by Pulsed Laser Deposition Technique

         Beryllium Zinc Oxide (BexZn1-xO) ternary nano thin films were deposited using the pulsed laser deposition (PLD) technique under a vacuum condition of 10-3 torr at room temperature on glass substrates with different films thicknesses, (300, 600 and 900 nm). UV-Vis spectra study found the optical band gap for Be0.2Zn0.8O to be  (3.42, 3.51 and 3.65 eV) for the (300, 600 and 900nm) film thicknesses, respectively which is larger than the value of zinc oxide ZnO (3.36eV) and smaller than that of beryllium oxide BeO (10.6eV). While the X-ray diffraction (XRD) pattern analysis of ZnO, BeO and Be 0.2 Zn 0.8 O powder and nano-thin films indicated a hexa

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Thu Dec 13 2018
Journal Name
International Journal Of Engineering & Technology
Effect of Steel Fiber on Properties of High Performance No-Fine Concrete

No-fine concrete (NFC) is cellular concrete and it’s light weight concrete produced with the exclusion of sand from the concrete. This study includes the mechanical properties of lightweight reinforced by steel fiber, containing different proportions of steel fiber. This study was done using number of tests. These tests were density, compressive strength, flexural strength and absorption. These tests of the molds at different curing time. The results of tests that implication of fiber to No. fine concrete did not affect significantly on the compressive strength, While the flexural strength were gets better. Results explained that, the flexural strength of (1%) fiber No- fine concrete molds are four times that of the reference mold

... Show More
View Publication
Crossref (1)
Crossref
Publication Date
Sun Oct 01 2017
Journal Name
Journal Of Engineering
Optimization of Surface Roughness for Al-alloy in Electro-chemical Machining (ECM) using Taguchi Method

Electro-chemical Machining is  significant  process to remove metal with using  anodic dissolution. Electro-chemical machining use to removed metal workpiece from (7025) aluminum alloy using Potassium chloride (KCl) solution .The tool used was made from copper. In this present the optimize processes input parameter use are( current, gap and electrolyte concentration) and surface roughness (Ra) as output .The experiments on electro-chemical machining with use current (30, 50, 70)A, gap (1.00, 1.25, 1.50) mm and electrolyte concentration (100, 200, 300) (g/L).  The method (ANOVA) was used to limited the large influence factors affected on surface roughness and found the current was the large influence f

... Show More
View Publication Preview PDF
Publication Date
Wed Apr 05 2023
Journal Name
Journal Of Engineering
Effect of Nb Addition on Hardness and Wear Resist of Cu-Al-Ni Shape Memory Alloy Fabricated By Powder Metallurgy

Cu-Al-Ni shape memory alloy specimens has been fabricated using powder metallurgy technique with tube furnace and vacuum sintering environment , three range of Nb powder weight percentage (0.3,0.6,0.9)% has been added. Micro hardness and sliding wear resist has been tested followed by X-ray diffraction, scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDX) for micro structure observation. The experimental test for the samples has showed that the increase of Nb powder weight percentage in the master alloy has a significant effect on increasing the hardness and decreasing the wear resist therefore it will enhance the mechanical properties for this alloy.

View Publication Preview PDF
Crossref
Publication Date
Fri Aug 02 2019
Journal Name
The Fifth Conference On Smart Monitoring, Assessment And Rehabilitation Of Civil Structures Smar 2019
Rehabilitation of Mohammed Al-Qassim Bridge after Fire Attack Using CFRP Sheets: A Case Study

View Publication
Publication Date
Sun Mar 16 2025
Journal Name
Revista Iberoamericana De Psicología Del Ejercicio Y El Deporte, Issn 1886-8576, Vol. 18, Nº. 4, 2023, Págs. 361-363
The Effect of a Training Curriculum in Developing the Speed Endurance and Strength Characterized By Speed for the Muscles of the Legs for Female Basketball Students

Autorías: Mariam Liwa Abdel Fattah, Liqaa Abdullah Ali. Localización: Revista iberoamericana de psicología del ejercicio y el deporte. Nº. 4, 2023. Artículo de Revista en Dialnet.

View Publication Preview PDF
Scopus (1)
Scopus
Publication Date
Sun Jan 20 2019
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Gallic Acid as Corrosion Inhibitor for Aluminum 6061 in Alkali Solutions

      The research aims to study the corrosion of aluminum alloy(6061) in 0.6 mol. dm-3 NaCl solution in base medium  was examined with out and with Gallic acid as environmentally – friendly corrosion inhibitor at temperature range (298-313)K. The inhibitive action of gallic acid on corrosion of aluminum alloy(6061)  in KOH solution was examined through electrochemical polarization method using potentiostatic technique and surface analysis by optical microscopy,  Polarization measurements indicate that the examined compound act as a mixed type inhibitor. Results appeared that the inhibition occurs through adsorption of the inhibitor molecules on the metal surface and it was obeyed

... Show More
View Publication Preview PDF
Crossref (4)
Crossref