The creation and characterisation of biodegradable blend films based on chitosan and polyvinyl alcohol for application in a range of packaging is described. The compatibility between the chitosan and PVA polymers was good. Composite films had a compact and homogeneous structure, according to the morphology analysis. The mechanical test result of PVA/CH at concentrations 5% showed, that The higher values of TS recorded in sample (p1, with 40 MPa) while the lower values appeared in sample (p9, with 22.09 MPa), the TS decreased gradually as the amount of PVA increased in blend film. While the blend film of pure Chitosan exhibits a poor mechanical strength which makes it a poor candidate for packaging but Blending CH with PVA together improved

Pulsed-laser deposition (PLD) technique was used to prepare thin films from cerium oxide (CeO2) doped with erbium and indium oxides. In order to characterize the morphology and sensing features, these films were deposited on glass and/or single silicon substrates, respectively, with erbium and indium oxides. The morphological investigation conducted using atomic force microscope has shown an increase in the non-regularity of particle diameter with increasing doping ratios of both oxides. The maximum particle diameter of 61.45nm was obtained for 9% Eu2O3-doped CeO2. The surface roughness value of Eu2O3-doped ceria was higher than those of In2O3-doped ceria. The gas sensing measurements were done at

New complexes were synthesized with Schiff base tetradentate ligand (L). The ligand was synthesized by the condensation reaction of the dimedone with 2-hydroxybenzohydrazide. The formula of complexes [M(L) (H2O)2].Cl2, where M represents Mn(II), Ni(II) Cu(II), [Co(L)Cl.H2O]Cl and [Zn(L)(H2O)2]Cl2.2H2O. The ligand was identified using m.p., UV-Vis, FT-IR, Mass, 1H-NMR, and C.H.N. These complexes were characterized using techniques including infrared, UV-Vis absorption, magnetic susceptibility, molar conductivity, elemental analyses, thermogravimetric analysis (TGA), chloride content determination using Mohr’s method, and atomic absorption spectroscopy. The measurements revealed that the complexes are electrolytic. FT-IR results dem

Dental implants can be made of various materials, and amongst them, titanium and titanium alloy were the materials of choice for dental implants for many years because of their biocompatibility. The two alloys have a high level of biocompatibility, a lower modulus of elasticity, and better corrosion resistance than other alloys. Thus, they are frequently utilized in biomedical applications and mostly replace stiff fabrics. The latest advances in a new strontium oxide–cp titanium composite alloy are the main topic of this research. With regard to biomedical applications, additions of strontium oxide were synthesized at three distinct weight percentages (2%, 4%, and 6% by wt%). Powder metallurgy was used to create the alloys, which

Mesoporous SBA-15 with nono particle size distribution, different texture properties, and morphologies have been synthesized by controlling the hydrophilic-hydrophobic character during preparation, i.e., the solubility of micelles of pluronic P123 by controlling the charge of PEO hydrophilic-inorganic silica zone using different charge surfactants CTAB (cationic), F68 (nonionic), and SDBS (anionic). Sodium silicate was used as a silica source. Eo20Po70Eo20 co-polymer was used as a template at highly acidic conditions (pH<2). The experiments were characterized using XRD, FTIR, AFM, BET, and FESEM. The XRD and FTIR tests indicated that the SBA-15 is amorphous and free from impurities. The degree of particle dispersion is sequenced

High performance liquid chromatography was applied for the separation and identification of four antharquinone derivatives, aloe emodin, emodin, chrysophanol and physcion. The separation was carried out using Eurospher 100, C18 column (4.6 mm i.d. x 250 mm, 5 µm) under the following conditions: acetonitile (solvent A) and water: acetic acid (99.9: 0.1 v/v, pH 3.5)( solvent B) as a mobile phase with isocratic elution with 30% solvent B at flow rate 0.8 ml/min. The detection wavelength was set at 254 nm. The four antharquinone derivatives were isolated from the Iraqi rhubarb, Rheum ribes root by preparative TLC, their structures were identified by ¹H NMR and used as standards for HPLC analysis. The percentages of alo

This work is aiming to study and compare the removal of lead (II) from simulated wastewater by activated carbon and bentonite as adsorbents with particle size of 0.32-0.5 mm. A mathematical model was applied to describe the mass transfer kinetic.

The batch experiments were carried out to determine the adsorption isotherm constants for each adsorbent, and five isotherm models were tested to choose the best fit model for the experimental data. The pore, surface diffusion coefficients and mass transfer coefficient were found by fitting the experimental data to a theoretical model. Partial differential equations were used to describe the adsorption in the bulk and solid phases. These equations were simplified and the

A new derivative of PAM, acrylamide was copolymerized with succinic anhydride, and the reaction product reacted with three dyes, anthocyanin, bromophenol, and thymol. The prepared polymers were characterized by X-ray diffraction, FT-IR and UV-visible spectroscopy, proton nuclear magnetic resonance spectrometry, and thermal analysis. FT-IR spectroscopy showed the disappearance of two bands near 3450 and 3380 cm-1 for the stretching vibrations of the primary amine which indicates for the formation of amides. The UV-photolysis of aqueous solutions of different concentrations of the polymers was studied. Polyacrylamide-g-succinic anhydride showed an increase in polymerization under light. An increase of ~ 50% was observed for a 200 mg/L

Electro-kinetic remediation technology is one of the developing technologies that offer great promise for the cleanup of soils contaminated with heavy metals. A numerical model was formulated to simulate copper (Cu) transport under an electric field using one-dimensional diffusion-advection equations describing the contaminant transport driven by chemical and electrical gradients in soil during the electro-kinetic remediation as a function of time and space. This model included complex physicochemical factors affecting the transport phenomena, such as soil pH value, aqueous phase reaction, adsorption, and precipitation. One-dimensional finitedifference computer program successfully predicted meaningful values for soil pH profiles and Cu