A phosphorus‐containing Schiff base was prepared from bis{3‐[2‐(4‐amino‐1,5‐dimethyl‐2‐phenylpyrazol‐3‐ylideneamino)ethyl]indol‐1‐ylmethyl}phosphinic acid and paraformaldehyde as a novel antibacterial compound. The reaction of the Schiff base ligand with VO(IV), Ni(II), Co(II), Cu(II), Zn(II), Cd(II), Hg(II), Pd(II) and Pt(IV) led to binuclear species of metal complexes, depending on the ratio of metal ion and ligand. The ligand and its complexes were investigated using elemental analysis, Fourier transform infrared, ¹H NMR, ¹³C NMR, UV–visible and mass spectra, thermogravimetric analysis, conductivity measurements and thermal analysis. The results showed that the S

In spite of economic importance of sugar cane and sugar beet as they described as industrial crops they still face decreasing rates of production and productivity in Iraq , and their production was not able to satisfy the local industrial demands for sugar . Thus this study aimed at studying and analyzing, production and productivity of sugar cane and sugar beet in Iraq and this has been done by using non serial data that can be obtained from official offices in Iraq . The area and production of sugar cane in Iraq recorded positive annual growth rates during 1970- 1978 which were 6% and 5% consequently , while the productivity of sugar cane recorded at the same duration of time negative annual growth rate which was 1% , while they recorded

In the present study, a powder mixture of elements Ti and Ni was mechanically alloyed in a high energy ball mill. Microstructure of the nanosized amorphous milled product in different stages of milling has been characterized by X- ray diffraction, scanning electron microscopy and differential thermal analysis. We found that time of mechanical alloying is more significant to convert all crystalline structure to the amorphous phase. Nanocrystalline phase was achieved as a result of the mechanical alloying process. The results also indicates that the phase transformation and the grain size occurs in these alloys are controlled by ball milling time

Oilwell cementing operations are crucial for drilling and completion, preserving the well's productive life. However, weak and permeable formations pose a high risk of cement slurry loss, leading to failure. Lightweight cement, like foamed cement, is used to avoid these difficulties. This study is focused on creating a range of foamed slurry densities and examining the effect of gas concentration on their rheological properties. The foaming agent and foam stabilizer are tested, and the optimal concentration is determined to be 2% and 0.12%, respectively, by the weight of the cement.

Furthermore, the construction of samples of foam cement with different densities (0.8, 1.0, 1.2, 1.4, and 1.6) g/cc is performed to f

PMMA (Poly methyl methacrylate) is considered one of the most commonly used materials in denture base fabrication due to its ideal properties. Although, a major problem with this resin is the frequent fractures due to heavy chewing forces which lead to early crack and fracture in clinical use. The addition of nanoparticles as filler performed in this study to enhance its selected mechanical properties. The Nano-additive effect investigated in normal circumstances and under a different temperature during water exposure. First, tests applied on the prepared samples at room temperature and then after exposure to water bath at (20, 40, 60) C^° respectively. SEM, PSD, EDX were utilized for samples evaluation in this study. Flexural

Some biological aspects of the zebra mussel, Dreissena polymorpha have been studied at Al-Musayab thermal power plant ,sixty km. south west of Baghdad. Data collected during the period extended from November, 2002 to October, 2003 except for the month of April The population consisted of five age groups; O, I, II, III, and IV which have 0, 1, 2, 3 and 4 annuli respectively. The study also proved the validity of annuli readings for age and growth determination. The average annual growth rates for age groups O,I, II, III, and IV were 5.7, 5.5, 5.4, 5.2 and 5.4 respectively. Average calculated length for laboratory reared mussel was 2.5 mm compared to 5.4 mm in natural environment. Correlation coefficients were very high between age an