This study involves the design of 24 mixtures of fiber reinforced magnetic reactive powder concrete containing nano silica. Tap water was used for 12 of these mixtures, while magnetic water was used for the others. The nano silica (NS) with ratios (1, 1.5, 2, 2.5 and 3) % by weight of cement, were used for all the mixtures. The results have shown that the mixture containing 2.5% NS gives the highest compressive strength at age 7 days. Many different other tests were carried out, the results have shown that the carbon fiber reinforced magnetic reactive powder concrete containing 2.5% NS (CFRMRPCCNS) had higher compressive strength, modulus of rupture, splitting tension, str

A successful synthesis of mesoporous Santa Barbara amorphous (SBA-15) with nanoparticle size was attempted using prepared sodium silicate from Iraqi high silica sand. EO20PO70EO20 copolymer was used as a template at highly acidic conditions (pH < 2). The effect of crystallization temperature of (100, 110, 120, and 130 0C), and crystallization time of (24, 48, 72, and 120 h) on surface properties was studied. The experiments were characterized using XRD, FTIR, AFM, BET, and FESEM. The XRD and FTIR tests represent amorphous SBA-15 without any impurities. Decreasing average particle size distribution increased the surface area, and decreased the porosity (pore volume, and pore size) in all experiments. The texture properties were su

The creation and characterisation of biodegradable blend films based on chitosan and polyvinyl alcohol for application in a range of packaging is described. The compatibility between the chitosan and PVA polymers was good. Composite films had a compact and homogeneous structure, according to the morphology analysis. The mechanical test result of PVA/CH at concentrations 5% showed, that The higher values of TS recorded in sample (p1, with 40 MPa) while the lower values appeared in sample (p9, with 22.09 MPa), the TS decreased gradually as the amount of PVA increased in blend film. While the blend film of pure Chitosan exhibits a poor mechanical strength which makes it a poor candidate for packaging but Blending CH with PVA together improved

A friction stir spot welding (FSSW) process is an emerging solid state joining process in which the material that is being welded does not melt. In this investigation an attempt has been made to understand the effect of tool shoulder diameter on the mechanical properties of the joint. For this purpose four welding tools diameter (10,13, 16 and 19) mm at constant preheating time and plunging time were used to carry
out welding process. Effect of tool diameter on mechanical properties of welded joints was investigated using shear stress test and Microhardness of joint which welded was studied. Based on the stir welding experiments conducted in this study the results show that aluminum alloy (1200) can be welded using (FSSW) process with

The nanocompsite of alumina (Al₂O₃) produced a number of beneficial effects in alloys. There is increasing in resistance of materials to surface related failures , such as the mechanical properties , fatigue and stress corrosion cracking .The experimental results observed that the adding of reinforced  nanomaterials  type Al₂O₃  enhanced the   HB hardness, UTS, 0.2 YS and ductility of 2014 Al/Al₂O₃ nano composites . the analysis of experiments, indicated that The maximum enhancement was observed at 0.4 wt.% Al₂O₃. The ultimate improvement percentage were 15.78% HB hardness, 18.1% (UTS), 12.86% (

     This work compares the changes in optical and structural properties of cerium oxide (CeO2) when doped with different concentrations (3%,5%,7%, and 9%) of two oxides, In2O3 and Eu2O3. X-ray diffraction and spectrophotometry were employed in the visible, ultraviolet, and near-infrared regions. The findings demonstrated that CeO2 doped with In2O3 and Eu2O3 thin films were polycrystalline and had a cubic structure. The crystal size increased from 20.5 to 32.15 when Eu2O3 doping ratio increased from 0% to 7% and then decreased to 28.46 nm at 9%. While the crystal size showed an increase from 20.5 to 21.42 nm with the increase of the In2O3 doping ratio, while the lattice constant measured for cubic CeO2 changed opposite to that

Compounds from ZnO doped with AgO in different ratio (0,3,5,7, and 9)wt.% were prepared.Thin films from the prepared compounds were deposited on a glass substrate using the pulsed laser deposition method. The XRD pattern confirmed the presence of a single-phase hexagonal wurtzite ZnO structure, without the presence of a secondary phase. AFM measurements showed an increase in both average grain size and average surface roughness with increasing concentration content of (AgO).The crystallite size of ZnO of the main peak corresponding to the preferred plane of crystal growth named (100) increases from 17.8 to 22.5nm by increasing of AgO doping ratio  from 0 to 9%. The absorbance and transmittance in the wavelength range (350-1100 nm)

This study was conducted in a laboratory experiment at the University of Baghdad, College of Science, computing Department, 5 km from the center of Baghdad city, in 2021 to evaluate the sorting method for the tomato crop. The experiments were conducted in a factorial experiment under a complete randomized design with three replications and using SAS analysis, artificial neural network, image processing, the study of external characteristics, and physical features; fruit surface area and fruit circumference were 1334.46 cm2,57.53 cm2 and free diseases. The error value was less than zero, while training with outputs recorded the highest value and which was 5. The neural network's performance between the input and the mean square of th