This work aims to investigate the tensile and compression strengths of heat- cured acrylic resin denture base material by adding styrene-butadiene (S- B) to polymethyl methacrylate (PMMA). The most well- known issue in prosthodontic practice is fracture of a denture base. All samples were a blend of (90%, 80%) PMMA and (10%, 20%) S- B powder melted in Oxolane (Tetra hydro furan). These samples were chopped down into specimens of dimensions 100x10x2.5mm to carry out the requirements of tensile tests. The compression strength test specimens were shaped into a cylinder with dimensions of 12.7mm in diameter and 20mm in length. The experimental results show a significant increase in both tensile and compression strengths when compared to cont

In this work, p-n junctions were fabricated from highly-pure nanostructured NiO and TiO2 thin films deposited on glass substrates by dc reactive magnetron sputtering technique. The structural characterization showed that the prepared multilayer NiO/TiO2 thin film structures were highly pure as no traces for other compounds than NiO and TiO2 were observed. It was found that the absorption of NiO-on-TiO2 structure is higher than that of the TiO2-on-NiO. Also, the NiO/TiO2 heterojunctions exhibit typical electrical characteristics, higher ideality factor and better spectral responsivity when compared to those fabricated from the same materials by the same technique and with larger particle size and lower structural purity.

This work involves theoretical and experimental studies for seven compounds to calculate the electrons spectrum and NLO properties. The theoretical study is done by employing the Time Depending Density Functional Theory TD-DFT and B3LYP/high basis set 6-311++G (2d,2p), using Gaussian program 09. Experimental study by UV/VIS spectrophotometer device to prove the theoretical study. Theoretical and experimental results were applicable in spectrum and energy gap values, in addition to convergence theoretically the energy gap results from ΔEHOMO-LUMO and UV/VIS. spectrum. Consider the theoretical method very appropriate to compounds that absorb in vacuum UV.

   This study involves the synthesis of new azodye, derived from 2-Amino-6ethoxybenzothiazole and 4-Chloro-3,5-dimethylphenol . The characterization of dye has been described by C.H.N. The TG , IR and Visible. spectroscopic techniques .The acid-base properties were studied at different pH values . The ionization and protonation constants of dye were determined. Solvents effects were also studied at different solvents polarities . The optimum conditions of this formation of complex with Fe(III) were investigated . The analytical applications of this azodye , were studied like; using it as acid-base indicator , and for the determination of nitrite ions

  In this study terpolymer resin  ) p-ABBF) was prepared by condensation of (p-amino benzoic acid) and (Biuret) with formaldehyde in (1:1:3) mol ratio using hydrolic acid as a reaction medium at 130±2 ℃ .The synthesized terpolymer resin was characterized by elemental analysis , FT-IR and (1H-NMR) spectroscopy. The intrinsic viscosity was determined. The thermal stability of the terpolymer was analyzed by (TGA and DSC).The morphological feature of the (p-ABBF) terpolymer resin was studied by scanning electron microscopy (SEM).Bach equilibrium method was employed to study analytical efficiency of the terpolymer resin towards certain trivalent and divalent metal ions such as (Cu+2,Ni+2, Co+2,Zn+2,Cd+2 and Cr+3( where thes

Nanostructured Al2O3has been applied as a protective coating against corrosion of the carbon steel (C.S) in seawater environment (3.5% NaCl) at temperatures range (298-328)K. Aluminananoparticles were deposited on carbon steel substrates by cathodic electrophoretic deposition (EPD) with ethanol as suspension medium and poly(acrylic acid) (PAA) as polymeric charging agent. Meanwhile, thesurface morphology was examined using Atomic-force microscopy (AFM). The cross-section AFM showed that the particles sizes for the Al2O3 NPs is around 60-80 nm. The anticorrosion behaviour of coated C.S was investigated in 3.5% NaCl at temperature range 298-328 K by potentiodynamic polarization measurements. Results show that using PAA in suspension coat incr