This thesis aims to study the effect of addition polymer materials on mechanical properties of self-compacting concrete, and also to assess the influence of petroleum products (kerosene and gas oil) on mechanical properties of polymer modified self-compacting concrete (PMSCC) after different exposure periods of (30 ,60 ,90 ,and 180 days).

Two type of curing are used; 28 days in water for SCC and 2 days in water followed 26 days in air for PMSCC.

The test results show that the PMSCC (15% P/C ratio) which is exposed to oil products recorded a lower deterioration in compressive strength's values than reference concrete. The percentages of reduction in compressive strength values of PMSCC (15% P/C ratio) was

 In the current study, the definition of mapping of fuzzy neutrosophic generalized semi-continuous and fuzzy neutrosophic alpha has generalized mapping as continuous. The study confirmed some theorems regarding such a concept. In the following, it has been found relationships among fuzzy neutrosophic alpha generalized mapping as continuous, fuzzy neutrosophic mapping as continuous, fuzzy neutrosophic alpha mapping as continuous, fuzzy neutrosophic generalized semi mapping as continuous, fuzzy neutrosophic pre mapping as continuous and fuzzy neutrosophic γ mapping as continuous.

Four Se70Ge20Sb10 alloy samples were prepared using the melt quenching technique. To improve the energy states of the mobility gap, the samples were exposed to gamma radiation from 60Co source at various doses of 600, 1200, 1500, and 2000 Gy. The electrical characteristics were examined both before and after irradiation. The conductivity analysis revealed that all of our samples were impacted by gamma radiation. The reorganization of the amorphous lattice and the degree of radiation-induced disorder have been involved in the changes that occurred in the electrical characteristics of the irradiated samples. All irradiated and non-irradiated samples feature three conduction mechanisms at low temperatures, where the electrical conducti

The importance of specifying proper aggregate grading for achieving satisfactory performance in pavement applications has long been recognized. To improve the specifications for superior performance, there is a need to understand how differences in aggregate gradations within the acceptable limits may affect unbound aggregate base behavior. The effects of gradation on strength, modulus, and deformation characteristics of high-quality crushed rock base materials are described here. Two crushed rock types commonly used in constructing heavy-duty granular base layers in the State of Victoria, Australia, with three different gradations each were used in this study. The gradations used represent the lower, medium, and upper gradation li

    Mauddud formation is one of the most prominent formations in Northeastern Iraq due to its significant hydrocarbon reserves, making accurate geomechanical characterization essential for safe drilling operations and informed development planning. This study constructs a calibrated post-drill one dimensional mechanical earth model (1D-MEM) for selected wells, levering Techlog software to integrate rock mechanical data, image logs, multi-arm caliper measurements, conventional well logs, drilling reports, and core analyses. The methodology provides a detailed workflow for estimating geomechanical properties from log and image analysis to model calibration. Validation of the 1-D MEM performed through cross-comparison with direct me

Cocrystallization is an emerging approach for improving physico-chemical characteristics of an active pharmaceutical ingredient (API) for instance dissolution rate, solubility, stability in addition to mechanical properties without affecting their therapeutic activity. It is of great importance when other approaches like salt or polymorph formation do not encounter the estimated targets. In this review article, an outline of pharmaceutical cocrystals will be presented, with highlighting on factors affecting cocrystallization which include ∆pKa, donors and acceptors hydrogen bonds, molecular recognition point, synthon forming functional groups flexibility, dicarboxylic acid coformers carbon chain length and solvent effe

Fiber reinforced polymer composite is an important material for structural application. The diversified application of FRP composite has taken center of attraction for interdisciplinary research. However, improvements on mechanical properties of this class of materials are still under research for different applications. In this paper we have modified the epoxy matrix by Al₂O₃, SiO₂ and TiO₂ nano particles in glass fiber/epoxy composite to improve the mechanical and physical properties. The composites are fabricated by hand lay-up method. It is observed that mechanical properties like flexural strength, hardness are more in case of SiO₂ modified epoxy composite compare to other nano

Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

In this work, 332 Al alloy was prepared and reinforced with (0.5% and 1%) nano-Al₂O₃ particles. The prepared unreinforced and reinforced 332 Al alloy with nano-Al₂O₃ were solution heat treated (T6) at 510 ̊C and aged at 225 ̊C with different times (1, 3, and 5 h). Hardness test was performed on all the prepared alloys. All prepared alloys were dry slided under different applied loads (5, 10, 15, and 20 N) against steel counterface surface using pin on disk apparatus. The results showed that refinement effect was observed after addition of nano-Al₂O₃ particles and a change in silicon morphology after performing the solution heat treatment. The results also showed that har