New types of hydrodesulfurization (HDS) catalyst Re-Ni-Mo/ γ-Al2O3 was prepared and tested separately with two prepared conventional HDS catalysts (Ni-Mo/ γ-Al2O3 and Co-Mo//γ-Al2O3) by using a pilot plant hydrotreatment unit. Activities of three prepared hydrodesulfurization catalysts were examined in hydrodesulfurization (HDS) of atmospheric gas oil at different temperatures 275 to 350 °C and LHSV 1 to 4 h-1 , the reactions conducted under constant pressure 40 bar and H2/HC ratio 500 ml/ml .Moreover, the hydrogenation of aromatic (HAD) in gas oil has been studied. HDS was much improved by adding promoter Re to the Ni-Mo/Al2O3 catalyst. The results showed that Re-Ni-Mo/ γ-Al2O3 have more activity in desulfurization than NiMo//γ-Al2O3 and Co-Mo/ γ-Al2O3 catalysts. The efficiency of hydrodesulfurization was markedly reduced over the Co -Mo/ γ-Al2O3.Also the result showed that NiMo//γ-Al2O3 have a minimum aromatic content 15.44 %.
Sulphated zirconia (SZ) is one of the most important solid acid catalysts was synthesize at different operating conditions, different calcination temperature and sulfonating time has been used. The prepared catalyst was distinguished by X-ray Diffraction (XRD), particle size and morphology of catalyst were checked by atomic force microscopy (AFM) and scanning electron microscopy (SEM) respectively, in addition to analysis by (DTA) Differential thermally and Energy Dispersive X-Ray (EDX). Finally, the N2 adsorption-desorption was used to measure the surface area (BET) and pore volume. High degree of tetragonal crystallinity was obtained 90 %, and surface area of 169 m2/g and pore volume of 0.39 cm3g-1 at 600°C calcination temperature for 3
... Show More
(4)
KE Sharquie, AA Noaimi, MN Almallah, Journal of Cosmetics, Dermatological Sciences and Applications, 2014 - Cited by 2
In this paper we report the use of supersonic jet laser induced fluorescence (LIF) spectroscopy to facilitate the study of the spectra of some organometallic sandwich compounds particularly the metallocenes. The charge-transfer processes within these compounds, especially ligand to metal charge transfer within decamethylrhenocene ( - C5 Me5)2 Re were of particular interest. The spectrum shows a high degree of structures, indicating that there are several levels populated and these molecules are able to undergo many possible transitions
KE Sharquie, R Hayani, J Al-Rawi, A Noaimi, SH Radhy, CLINICAL AND EXPERIMENTAL RHEUMATOLOGY, 2010
(16)
(12)
Research deals the crises of the global recession of the facets of different and calls for the need to think out of the ordinary theory and find the arguments of the theory to accommodate the evolution of life, globalization and technological change and the standard of living of individuals and the size of the disparity in income distribution is not on the national level, but also at the global level as well, without paying attention to the potential resistance for thought the usual classical, Where the greater the returns of factors of production, the consumption will increase, and that the marginal propensity to consume may rise and the rise at rates greater with slices of low-income (the mouths of the poor) wi
... Show More
A new Schiff base ligand Bis-1,4-di[N-3-(2-hydroxy-1-amino)- acetophenonylidene] benzylidene [L] and its complexes with (Mn(II) ,Co(II) ,Ni(II and Cu(II)) were synthesized . The ligand was prepared in two steps. In the first step a solution of (terphthalaldehyde) in methanol reacts under reflux with (p-aminoacetophenone) to give an intermediate compound [1-[3-({4-[(3-Acetyl-phenylimino)-methyl]-benzylidene}-amino)-phenyl]- ethanone which reacts in the second step with (2-Amino-phenol) giving the mentioned ligand. The complexes were synthesized by addition the corresponding metal salt solution to the solution of the ligand in methanol under reflux in (1:1) metal to ligand ratio. On the basis of, molar conductance, I.R., UV-Vis, HPLC, chlorid
... Show More
NiO nanoparticle synthesis by chemical method and characterized by XRD with crystal size 11.72
nm and grain size 13 nm from FESEM image also NiO micro used ,two NiO as an additive to evaluate the
possibility of producing photodegradable polymers, the practical application of solid-phase photocatalytic
degradation of polyvinyl chloride (PVC- NiO composite films) was investigated. PVC has a negative impact
on the environment since its polymer degrades slowly, yet it has a wide range of industrial applications and
the amount used shows no evidence of diminishing use. Thus, a synthesis of modified PVC- NiO micro and
nano has been studied with 0, 50, 100, 150, 200, 250, and 300 (hours) as irradiation time a
(6)
(1)
Faujasite type NaY zeolite catalyst was prepared from locally available kaolin, then the prepared NaY zeolite have been modified by exchanging of sodium ion with ammonium to produce NH4Y zeolite. NH4Y zeolite was converted to HY zeolite by ion exchanging with oxalic acid. Zinc and nickel promoters have been added to the prepared HY zeolite catalyst, and the effect of these promoters on the catalytic activity of the prepared HY catalyst was studied in fluid catalytic cracking process using light gas oil as a feedstock. The experimental results show that the promoted catalyst gives higher gas oil conversion and gasoline yield than HY zeolite catalyst at the same reaction temperature and WHSV. It was also found that the promoted catalyst gi