The artificial silk (Rayon) was produced from the fronds of date palms which was taken from date palm trees (type Al-Zahdi) from the Iraqi gardens. Two main parts of the frond, namely leaves and stalks were used in this study to produce rayon. The palm fronds were converted into a powder of 90-180 micrometers. Major steps were used to produce rayon; delignification, bleaching and finally dissolution. Modified organosolv method which uses organic solvent method was applied to remove high lignin content. Three variables were studied in the delignification process: temperature, the ratio of ethanol to water and digestion time. The results showed that the best percent of lignin removal was (97%) which occured at; digestion time (80 minutes), temperature (185oC) and the ratio of ethanol: water of 50: 50 wt/wt. Statistical experimental design type Central Composite Design (CCD) has been used to find a mathematical relationship between the variables and the remaining lignin percent as a dependent variable. The effect of using different catalysts in delignification process have been studied and found that the best catalyst is sodium hydroxide at the concentration (0.025) mole/L which gave the same percent removal of lignin (97%) but with low digestion time about 30 min. In the next step, the cellulose was dissolved using. NaOH with different concentrations (4%-12%) and the results showed that the optimum concentration of sodium hydroxide was 8% at temperature - 20oC. In order to improve cellulose dissolution, urea was added with proportion (6% NaOH + 4% urea). Finally, the cellulose was spinning with 10% H2SO4 to prepare rayon.
Five new ceftazidime derivatives were designed and synthesized in an attempt to improve the acid stability and may increase the spectrum of ceftazidime. The synthesized compounds included; Schiff base of ceftazidime (compound 1), ceftazidime lysine amide Schiff base (compound 2), ceftazidime lysine amide (compound 3), ceftazidime-di-lysine amide Schiff base (compound 4) and ceftazidime-di-lysine amide (compound 5). New ceftazidime derivatives were successfully prepared characterized and identified using spectral and elemental microanalysis (CHNS) analyses and the results comply with the calculated measurements.
Compounds 1 and 2 were subjected to a stability study in phosphate buffer (0.2M, pH 7.4) and in KCl/HCl buffer (0.
... Show MoreNovel bidentate Schiff bases having nitrogen-sulphur donor sequence was synthesized from condensation of racemate camphor, (R)-camphor and (S)-camphor with Methyl hydrazinecarbodithioate (SMDTC). Its metal complexes were also prepared through the reaction of these ligands with silver and bismuth salts. All complexes were characterized by elemental analyses and various physico-chemical techniques. These Schiff bases behaved as uninegatively charged bidentate ligands and coordinated to the metal ions via ?-nitrogen and thiolate sulphur atoms. The NS Schiff bases formed complexes of general formula, [M(NS)2] or [M(NS)2.H2O] where M is BiIII or AgI, the expected geometry is octahedral for Bi(III) complexes while Ag(I) is expected to oxidized t
... Show More5wt% copper doped zinc oxide (Cu-ZnO) nanostructures were prepared via the hydrothermal technique at different temperatures of 70, 100, 130, 160 and 190oC. UV spectroscopy, FE-SEM microscopy, XRD crystallography, and EDS measurements were used for nanostructure characterization. UV spectroscopy indicated a red shift for the absorption peaks, and hence a blue shift for the energy gap values, as temperature increased from 70 to 190oC. FE-SEM microscopy showed an increase in the average lengths and diameters of the nanostructures following a similar increase in temperature. XRD crystallography indicated decent structural patterns for Cu-ZnO nanostructures with an increase in crystallite size upon temperature incr
... Show MoreAzo-ligand-(HL)([4-((2-hydroxyquinolin-3-yl)diazenyl)-N-(5-methylisoxazol-3-yl)benzenesulfonamide] ) , (2- hydroxy quinolin derivative),reacts with the next metal ions (Cr (III), Fe (III),Co (II) and Cu(II)) forming stable complexes with unique geometries such as(tetrahedral for bothCo (II) and Cu (II), octahedral for both Cr (III) and Fe (III)). The creation of such complexes was detected by employing spectroscopic means involving ultraviolet-visible which proved the obtained geometries, Fourier transfer proved the involvement of coordinated water molecule in all complexes besides the pyrolysis (TGA & DSC) studies proved the coordination of water residues with metal ions inside the coordination sphere as well as chlorine ato
... Show MoreL-Phenylalanine amino acid was condensed with 2-hydroxybezaldehyde to give the Schiff base sodium 2-(2-hydroxybenzylideneamino)-3-phenylpropanoate, which was used as a precursor [NaHL]. The precursor was reacted with 1,2-dichloroethane to give the Schiff base sodium 2,2'-(2,2'-(ethane-1,2diylbis(oxy))bis(2,1-phenylene))bis(methan-1-yl-1-ylidene)bis(azan1-yl-1-ylidene)bis(3-phenyl propanoate), which was used as a ligand [Na2L], in complexation with some metal (II) chloride MCl2, where [M= Co(II), Ni(II), Cu(II) and Zn(II)], to give [M(L)] complexes. The [Na2L] ligand and All complexes were characterized by spectroscopic methods, [FTIR, UV-Vis, atomic absorption], melting point, chloride content, conductivity and magnetic susceptibi
... Show MoreNew complexes of M(II) with mixed ligand of 5-Chlorosalicylic acid (CSA) C7H5ClO3 as primary ligand and L- Valine (L-Val) C5H11NO2 as a secondary ligand were prepared and characterized by elemental analysis (C.H.N), UV., FT-IR, magnetic susceptibility, μeff (B.M) as well as the conductivity measurements (Λm ). In the complexes, the 5-chlorosalicylic acid is bidentate in all complexes coordinating through –OH- and –COO- groups; also L-Valine behaves as a bidentate ligand in all complexes through –NH2 and –COO- groups. These five mixed ligand complexes formulated as Na3[M(CSA)2(L-Val)]. The proposed molecular structure for all complexes is octahedral geometries. The synthesis complexes were tested in vitro for against four bacteria
... Show MoreNew complexes of M(II) with mixed ligand of 5-Chlorosalicylic acid (CSA) C7H5ClO3 as primary ligand and L- Valine (L-Val) C5H11NO2 as a secondary ligand were prepared and characterized by elemental analysis (C.H.N), UV., FT-IR, magnetic susceptibility, µeff (B.M) as well as the conductivity measurements (Λm ). In the complexes, the 5-chlorosalicylic acid is bidentate in all complexes coordinating through –OH- and –COO- groups; also L-Valine behaves as a bidentate ligand in all complexes through –NH2 and –COO- groups. These five mixed ligand complexes formulated as Na3[M(CSA)2(L-Val)]. The proposed molecular structure for all complexes is octahedral geometries. The synthesis complexes were tested in vitro for against four bacteria
... Show MoreThis research includes the synthesis, characterization, and investigation of liquid crystalline properties of new rod-shaped liquid crystal compounds 1,4- phenylene bis(2-(5-(four-alkoxybenzylidene)-2,4-dioxothiazolidin-3- yl)acetate), prepared thiazolidine-2,4-dione (I) by the thiourea reaction with chloroacetic acid and water in the presence of the concentrated hydrochloric acid. The n-alkoxy benzaldehyde (II)n synthesized from the reacted 4- hydreoxybenzaldehyde and n-alkyl bromide with potassium hydroxide, and then the compound (I) was reacted with (II)n in the presence of piperidine to produce compounds (III)n. Also, hydroquinone was converted into a corresponding compound (IV) by refluxing with two moles of chloracetyl chloride in pyr
... Show MoreThe thermal method was used to produce silicoaluminophosphate (SAPO-11) with different amounts of carbon nanotubes (CNT). XRD, nitrogen adsorption-desorption, SEM, AFM, and FTIR were used to characterize the prepared catalyst. It was discovered that adding CNT increased the crystallinity of the synthesize SAPO-11 at all the temperatures which studied, wile the maximum surface area was 179.54 m2/g obtained at 190°C with 7.5 percent of CNT with a pore volume of 0.317 cm3/g ,and with nano-particles with average particle diameter of 24.8 nm, while the final molar composition of the prepared SAPO-11 was (Al2O3:0.93P2O5:0.414SiO2).