The artificial silk (Rayon) was produced from the fronds of date palms which was taken from date palm trees (type Al-Zahdi) from the Iraqi gardens. Two main parts of the frond, namely leaves and stalks were used in this study to produce rayon. The palm fronds were converted into a powder of 90-180 micrometers. Major steps were used to produce rayon; delignification, bleaching and finally dissolution. Modified organosolv method which uses organic solvent method was applied to remove high lignin content. Three variables were studied in the delignification process: temperature, the ratio of ethanol to water and digestion time. The results showed that the best percent of lignin removal was (97%) which occured at; digestion time (80 minutes), temperature (185oC) and the ratio of ethanol: water of 50: 50 wt/wt. Statistical experimental design type Central Composite Design (CCD) has been used to find a mathematical relationship between the variables and the remaining lignin percent as a dependent variable. The effect of using different catalysts in delignification process have been studied and found that the best catalyst is sodium hydroxide at the concentration (0.025) mole/L which gave the same percent removal of lignin (97%) but with low digestion time about 30 min. In the next step, the cellulose was dissolved using. NaOH with different concentrations (4%-12%) and the results showed that the optimum concentration of sodium hydroxide was 8% at temperature - 20oC. In order to improve cellulose dissolution, urea was added with proportion (6% NaOH + 4% urea). Finally, the cellulose was spinning with 10% H2SO4 to prepare rayon.
New series of Schiff bases 2(a-j) and corresponding beta-lactam derivatives 3(a-j) were synthesized from cefalexin (1) as starting material. The compound (1) was reacted with different aldehydes and ketones to give Schiff bases derivatives 2(a-j). The synthesized Schiff bases were cyclized by chloroacetyl chloride in the presence of triethylamine to form beta-lactam derivatives 3(a-j). The compounds were characterized by deremination melting point, FT-IR and 1H NMR. The beta-lactam derivatives were screened in vitro antibacterial against some bacterial species
(2)
This work contain many steps starting from esterification of isophthalic acid to yield diester compound [I] which was converted to their acid hydrazide [II], then the later compound reacted with ethylacetoacetate to yield pyrazol-5-one compound [III]. Afterword added acetyl chloride to give the compound [IV], thereaction of this compound with theiosemicarbazide ledto produce a new carbothioamide compound [V], Which was reacted with ethyl chloro acetate to yield thethioxoimidazolidin compound [VI]. The condensation reaction of this compound with different substituted aldehyde give new alkene derivatives[VII]a-d. The synthesized compounds were characterized by melting points , FT-IR ,1H-NMR and Mass spectroscopy .
Novel heterocyclic polyimide 5(a,b) have been synthesized based on polyacrylic backbone. The synthetic route start with nucleophilic substitution of 2-amino, or 4-amino, pyridine 1(a,b) to the polyacryloyl chloride afforded poly substituted amide 2(a,b). Another nucleophilic substitution were carried with adipoyl chloride to form polyimide chloride 3(a,b). Treatment of 3(a,b) with hydrazine hydrate afforded acid hydrazide polyimide 4(a,b), which upon cyclocondensation with carbon disulfide gave the target heterocyclic polyimide. The synthesized compounds were identified by spectroscopic methods: FT-IR, 1H-NMR and 13C-NMR.
Some esters were prepared from reaction of different molecular weight of PVA with some acid chloride (prepared by reaction of acid with thionyl chloride or phosphorous pentachloride)in the presence of pyridine. The thermal and reological properties were studied. The increasing Of bulky groups decreasing stability of the thermal and reological properties.
A research include of synthesized five member ring, which has been synthesized by condensation of 2-(1-(4- hydroxyphenyl) ethylidene)hydrazine-1-carbothioamide[I] with α-chloro ethylacetate in sodium acetate (fused) to form ethyl 2-(4-(1-((4-oxo-2-thioxopyrrolidin-3-ylidene)hydrazono) ethyl)phenoxy)acetate [II]. After that reacted [II]with hydrazine hydrate to resulting compound [III]. Compound [III] was refluxed with 4-aminobenzoicacid in excess of phosphorus oxy chloride give compound [IV],the later compound [IV] interact with acetyl acetone or ethylacetoacetate give to pyrazole and pyrazoline derivatives[V],[VI]. While when reacted with different aromatic aldehydes and one ketone consistence Schiff base derivatives [VII]a-e . The FTIR a
... Show MoreIn this paper the new starting material 2-(5-chloro-1H-benzo[d]imidazole-2-yl) aniline (1) was synthesized by the condensation reaction of 4-chloro-o-phenylenediamine and anthranilic acid .The new Mannich base derivatives were synthesized using formaldehyde and different secondary amines to synthesize a new set of benzimidazole derivatives(2-5). Also, the new Schiff-base derivatives (6-10) were synthesized from the reaction of compound (1) with various aromatic aldehydes and the closure-ring was done successfully using mercapto acetic acid to get the new thiazolidine derivatives(11-12).These new compounds were characterized using some physical techniques like:FT-IR Spectra and 1HNMR Spectra.
Nanocrystalline copper sulphide (Cu2-xS) powders were synthesized by chemical precipitation from their aqueous solutions composed of different molar ratio of copper sulfate dehydrate (CuSO4.5H2O) and thiorea (NH2)2CS as source of Cu+2, S-2 ions respectively, and sodium ethylene diamine tetra acetic acid dehydrate (EDTA) as a complex agent. The compositions, morphological and structural properties of the nanopowders were characterized by energy dispersive spectroscopy (EDS), scanning electron microscope (SEM), and X-ray diffraction (XRD), respectively. The compositional results showed that the copper content was high and the Sulfur content was low for both CuS and Cu2S nanopowders. SEM images shows that all products consist of aggregate o
... Show More
(1)
Activated carbon loading with metals oxides is new adsorbents and catalyst, which seem very promising for desulfurization process. The present study deals with the preparation of three metals oxides loaded on activated carbon (AC). The tri composite of ZnO/NiO/CoO/AC was characterized by X-Ray Diffraction (XRD), X-Ray florescence (XRF), N2 adsorption for BET surface area, pore volume and Atomic Force Microscopy (AFM). The effect of calcination temperature is investigated. The best calcination temperature is 250oC based on the presence of phase, low weight loss and keep at high surface area. The surface area and pore volume of prepared tri composite are 932.97m2/g and 0.6031cm3/g respec
... Show MorePhenol condensed with β-keto esters via Pechmann condensation to form derivatives of Coumarin in various reaction conditions by two ways. Present paper is comparative study of synthesis Coumarin with the yield of product , reaction time and reaction conditions.
A research include of synthesized five member ring, which has been synthesized by condensation of 2-(1-(4- hydroxyphenyl) ethylidene)hydrazine-1-carbothioamide[I] with α-chloro ethylacetate in sodium acetate (fused) to form ethyl 2-(4-(1-((4-oxo-2-thioxopyrrolidin-3-ylidene)hydrazono) ethyl)phenoxy)acetate [II]. After that reacted [II]with hydrazine hydrate to resulting compound [III]. Compound [III] was refluxed with 4-aminobenzoicacid in excess of phosphorus oxy chloride give compound [IV],the later compound [IV] interact with acetyl acetone or ethylacetoacetate give to pyrazole and pyrazoline derivatives[V],[VI]. While when reacted with different aromatic aldehydes and one ketone consistence Schiff base derivatives [VII]a-e . The FTIR a