This study was undertaken to provide more insight on the optimum injection temperature used for the production of PE crates, thereby saving time and money, and improving part quality. The work included processing trails of HDPE crates in an injection
molding machine at five temperatures ranged from 220 to 300°C. Both Rheological and mechanical characterization was conducted in order to understand the effect of injection temperature on the properties of crates. Oven aging was also applied for (4 weeks) to evaluate the long-term thermal stability. The results revealed that producing the crates at a temperature range of (260-280 °C) gives the best rheological and mechanical result. The lowest drop in thermal stability has been observed

Air pollution is very important topic for those interested in studying the environment because of its importance and the damage caused by it to human, animal and plant life. This research addresses the concept of air pollution, its causes, and its danger, and sheds light on the influence of climate elements on environmental pollution and the effect of temperature, rain, humidity, wind direction and speed, and atmospheric pressure on the increase or decrease of air pollution. This research discusses the sources of air pollution, including natural ones, including dust, smoke resulting from fires, erupting volcanoes, and others, including those resulting from human uses such as the use of fuel and others. The research addressed the dam

This experimental study focuses on scouring in box culvert inlets under steady-state conditions and at different percentages of blockage ranging from 0% to 65%, and also looks at the hydraulics of water in the culvert. The investigation shows that the blockage of the culverts has influenced the scouring pattern at the blocked culverts' entrances. Ten experiments were carried out at the laboratory to see how blockage impacts the scouring pattern upstream of a box culvert during steady flow. Both partially blocked and unblocked cases were implemented in this study. The experimental tests were done until the equilibrium scour occurred, which took about 3.5 hours of water flow to reach equilibrium conditions.  The results r

Background: Manuka honey (MH) is a mono-floral honey derived from the Manuka tree (Leptospermum scoparium). MH is a highly recognized for its non-peroxide antibacterial activities, which are mostly related to its unique methylglyoxal content (MGO) in MH. The beneficial phytochemicals in MH is directly related to their favorable health effects, which include wound healing, anticancer, antioxidant, and anti-inflammatory properties. Aims: The purpose of this study was to evaluate the effect of MH on pro-inflammatory cytokines (IL-8 and TNF-α) in patients with gingivitis and compare it with chlorhexidine (CHX) and distilled water (DW). Materials and Methods: This study was a randomized, double blinded, and parallel clinical trial. Forty-fiv

Study was made on the optical properties of Ge2oSe8othinfilms prepared by vac-uum evaporation as radiated by (0,34,69) Gy of 13 ray.The optical band gab Eg and tailing band A.Et were studied in the photon energy range ( 1 to 3)eV. The a-Ge20Se8o film was found to be indirect gap with energy gap of (1.965,1.9 , 1.82) eV at radiated by B ray with absorption doses of (0,34,69)Gy respectively.The Ea and AEt of Ge20Se80 films showed adecrease in E8 and an increase in AEt with radiation. This be-havior may be related to structural defects and dangling bonds.

ZnS thin films were grown onto glass substrates by flash evaporation technique, the effects of ? – rays on the optical constants of ZnS these films were studied. It was found that ? – rays affected all the parameters under investigation.

Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the

Reflection cracking in asphalt concrete (AC) overlays is a common form of pavement deterioration that occurs when underlying cracks and joints in the pavement structure propagate through an overlay due to thermal and traffic-induced movement, ultimately degrading the pavement’s lifespan and performance. This study aims to determine how alterations in overlay thickness and temperature conditions, the incorporation of chopped fibers, and the use of geotextiles influence the overlay’s capacity to postpone the occurrence of reflection cracking. To achieve the above objective, a total of 36 prism specimens were prepared and tested using an overlay testing machine (OTM). The variables considered in this study were the thickness of the

Conventional flexible pavements are released to different types of failure in the initial phases of their service life due to high traffic density, high speeds, heavy loads, and harsh climates. To eliminate pavement damage and failure early, the present search investigates the impact of adding glass, steel, and basalt fibers in the asphalt mixtures. Also, the study evaluates these materials characteristics compared to the mixtures without fibers. The Marshall test and tensile strength ratio test (TSR) were utilized to evaluate the asphalt mixture's performance. A set of specimens were produced by incorporating glass fiber (GF), steel fiber (SF), and basalt fiber (BF) at (0.10%, 0.15%, 0.20%), (0.25%, 0.35%, 0.45%), and (0.15%, 0.35%