In this study, composite materials were prepared using unsaturated polyester resin as binder with two types of fillers (sawdust and chopped reeds). The molding method is used to prepare sheets of UPE / sawdust composite and UPE / chopped reeds composite. The mechanical properties were studied including flexural strength and Young's modulus for the samples at normal conditions (N.C). The Commercial wood, UPE and its composite samples were immersed in water for about 30 days to find the weight gain (Mt%) of water for the samples, also to find the effect of water on their flexural strength and Young's modulus. The results showed that the samples of UPE / chopped reeds composite gained highest values of flexural strength (24.

In this paper a thin films of selenium was prepare on substrates of n-Si by evaporation in a vacuum technique with thickness about 0.5μm. And then an annealing process was done on samples at two temperature (100 and 200) C ° in a vacuum furnace (10^-3 torr).
Some structural, optical and mechanical properties of prepared thin films were measured. Results showed that the prepared film was the crystallization, optical transmittance and micro hardness of the prepared thin films increased significantly after annealing.

Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

Dental clinicians and professionals need an affordable, nontoxic, and effective disinfectant against infectious microorganisms when dealing with the contaminated dental impressions. This study evaluated the efficiency of hypochlorous acid (HOCl) as an antimicrobial disinfectant by spraying technique for the alginate impression materials, compared with sodium hypochlorite, and its effect on dimensional stability and reproduction of details. HOCl with a concentration of 200 ppm for 5 and 10 min was compared with the control group (no treatment) as a negative control and with sodium hypochlorite (% 0.5) as a positive control. Candida albicans, Staphylococcus aureus, and Pseudomonas aeruginosa were selected to assess the antimicrobi

In the present research, the electrical properties which included the ac-conductivity (σac), loss tangent of dielectric (tan δ) and real dielectric constant (ε’) are studied for nano polycarbonate in different pressures and frequencies as a function of temperature these properties were studied at selective temperature gradients which are (RT-50-100-150-250)°C. The results of the study showed that the values of dielectric constant and dissipation factor increase with increasing pressure and temperature and decreases by increasing frequency. And the results of electrical conductivity showed that it increases with increasing temperature, pressure and frequency.

  A biological experiment was conducted to study the effect of different concentrations of gibberellic acid and urea fertilizer and their interactions in some characteristic related to green growth of fenugreek plant (Trigonella foenum-graecum L.) in the green house of Department of Biology in College of Education (Ibn­al­Haitham)/Baghdad University for the growth season (2008­2009) in pots of (5 kgm) soil per pot, and four concentrations of gibberellic acid were used, they are (0,25,50,100) ppm, these concentrations were sprayed after the perfection of  the  fourth leaf for the plant. Moreover, three levels of urea fertilizer were used, they were (0.25, 0.50, 1.00) gm/pot. These concentrations were added as two p

    Different percents(1.0,2.5,5.0 and 10)wt%of MgO powders were added to ZnO powder to study their effects on the physical properties of ZnO.Density, porpsity and water absorption of ZnO were decreased as MgO weigth percentage content increased. The values of vickers hardneess have double values especially at 1.0 wt % of MgO.

The experiment was carried out in the green house of, Biology Department of ,College of
Education , Ibn Al-Haitham , Baghdad University. For growth season 2008-2009 via planting
seeds of three genotypes of barley cultivars Baraka , Becson and Baraka x Forest ,to study the
effect of different concentrations of NaCl (o , 50 ,100 , 150 , 200 ) mM.L on some
growth parameters such as fresh and dry weight of shoot and elements plants the experiment
carried out by using completely randomized design applied with four replicates . Data were
statistically analyzed by using least significant differenceat0.05probabilitylevel.
The results showed that an increase in NaCl salt concentrations from 0 to 200mM.L
-1
leads

The Inhbititory effect of cocentrated and non-cocentrated supernatant of the probiotic Lactobacillus salivarius against growth of some potential pathogenic microorganisms which included Pseudomonas eruginosa, Klebsiella spp, Escherichia coli and Candida albicans. The results were diffusion assay revealed that concentrated and non-concentrated supernatant had inhitory effect against pathogenic bacteria with inhibition zone renged between 13-17mm while inhibition effect of concentrated supernatant against C.albicans was inhibition zone 8mm. On the other hand, the effect of these suprnatant against biofilm formation of the tested microorganisms was studied. The result showed that the concentrated supernatant had inhibitory effect on biofil

In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850^oC) using single screw extruder and a mixing machine operated at a temperature between (190-200^oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength