Hot Press Bonding of Aluminum Alloy AA6061-T6 to Polyamide and Polyamide Composites

Moneer H. Tolephih; Adnan N. Abood; Hussein M. Saad

doi:10.1088/1757-899X/671/1/012029

Details

Publication Date

Wed Jan 01 2020

Journal Name

Iop Conference Series: Materials Science And Engineering

Volume

671

DOI

10.1088/1757-899X/671/1/012029

Choose Citation Style

Statistics

View publication

2

Statistics

(7)

(5)

Hot Press Bonding of Aluminum Alloy AA6061-T6 to Polyamide and Polyamide Composites

Moneer H. Tolephih

Adnan N. Abood

Hussein M. Saad

...Show More Authors

AbstractIn this study, aluminum alloyAA6061-T6 was joined by a hot press process with three types of material; polyamide PA 6.6 (nylon), 1% carbon nanotube/PA6.6 and 30% carbon fiber/PA6.6 composites. Three parameters were considered in the hot pressing; temperature (180, 200 and 220°C), pressure (2, 3, 4, 5 and 6 bar) and time of pressing (1, 2, 3, 4 and 5 minutes for 200ºC, and 0.25, 0.5, 0.75, 1 and 1.25 minutes for220ºC). Applied pressure has great effect on shear strength of the joint, corresponding to bonding time and temperature. Maximum shear strength was 8.89MPa obtained for PA6.6 at bonding conditions of 4 bar, 220ºC and 0.75 minute. For 30% carbon fiber/PA6,6 shear recorded was 8MPa at 4 bar, 220°C and 1 minute, while 1% carbon nanotube/PA6.6 was registered at 8MPa at 4 bar, 220ºC and 0.75 minute. Mechanical interlocking of polyimide in anodizing surface is 8μm approximately. The melting point and glass transmission temperature of polyimide and composites are decreased after hot pressing.

View Publication

Publication Date

Tue Jan 18 2022

Journal Name

Materials Science Forum

The Effect of Gamma Radiation on the Manufactured HgBa2Ca2Cu2.4Ag0.6O8+δ Compound

Gamma doses radiation

crystal size

strain

degree of crystallinity

Scherrer

crystallinity and Williamson equations.

zainab j

Balqees A.

Mohammed A.

Kareem A.

Auday H.

...Show More Authors

In this article four samples of HgBa₂Ca₂Cu_2.4Ag_0.6O_8+δ were prepared and irradiated with different doses of gamma radiation 6, 8 and 10 Mrad. The effects of gamma irradiation on structure of HgBa₂Ca₂Cu_2.4Ag_0.6O_8+δ samples were characterized using X-ray diffraction. It was concluded that there effect on structure by gamma irradiation. Scherrer, crystallization, and Williamson equations were applied based on the X-ray diffraction diagram and for all gamma doses, to calculate crystal size, strain, and degree of crystallinity. I