Abstract: To study the effect of nickel chloride on bone composition of mice, a number of biophysical and biochemical parameters have been made use. The animals were divided into control and experimental and further subdivided into three groups I, II and III according to the dose of nickel chloride (NiCl2) administered to them i.e. 5.8, 12.8 and 28.2 mg/kg body weight, respectively. Femur bones were obtained by sacrificing the animals three weeks after weaning them once a week. The percentage loss between the wet weight and dry weight of femur in control animals was found to be 32.5+1.5 .In the three experimental groups I,II and III, the percentage loss was 30.4+1.4, 35.3+2.3 and 38.9+2.2 respectively. The percentage loss between the wet weight in wet water and dry weight in wet water was 36.1+2.3 in the controls and 36.6+1.9, 39.5+2.2 and 51.1+3.1 respectively in the three experimental groups. Key words: Nickel Chloride(NiCl2), femur, Bone
A high Tc superconductor with a nominal composition
(Bi1-xPbx)2(Sr1-yBay)2Ca2Cu3O10+δ for (0 £ x £ 0.5) and (0 £ y £ 0.5) was prepared by
a solid state reaction method. The effect of the substitution of Pb for Bi and Ba for Sr and
quenching temperature on the superconductivity has been investigated to obtain the
optimum conditions for the formation and stabilization of the high Tc phase (2223).
The results showed that the optimum sintering temperature for the pure composition is
equal to 875°C and the sintering time is equal to 240h with heating and cooling rate of
60°C/h . Our results indicated that a small amount of (Ba = 0.1) could raise the transition
temperature (Tc), but enhancing Ba to 0.4 has raised
Earth dams in regions with moderate to high seismic activity are crucial for protecting downstream communities. Iraq and its neighboring areas have seen recurrent seismic activity, notably the 2017 Halabja Earthquake, which potentially compromised the integrity of the existing earth dam. The Darbandikhan Dam, affected by an earthquake, has inadequacies in its crest and downstream slope, presenting a greater danger of significant earthquake-induced damage compared to cyclic shocks. Consequently, evaluating the dam's safety is essential for safeguarding downstream residents and identifying optimal ways to avert slope stability failure amid recurrent seismic activity. Iraq's seismicity map is being updated to reflect earthquake magni
... Show More
The research aims at demonstrating the role of the formulation of the green strategy in adopting the areas of the green strategy at the level of jobs in the municipal institutions in the province of Babylon, specifically the Directorate of the municipality of Hilla. The most important areas related to the green strategy were highlighted directly or indirectly, after the indicators of environmental damage emerged from the actions of companies and institutions. The research included a sample size of 222 individual of municipal institutions with different job titles and specializations between the technical and administrative and different levels of academic achievement within the institutions within the Ministry of Construction, Ho
... Show More
Abstract
The present study investigates the effect of acetic acid on corrosion behavior and its potential of hydrothermally sealed anodized AA2319-Al-alloys. Anodizing treatment was performed in stagnant phosphoric acid electrolyte with or without addition of acetic acid. Hydrothermal sealing was carried out in boiling water for each anodized specimen. The open circuit potential of the unsealed and sealed anodized samples was examined using open circuit potential measurement for the purpose of starting in scanning polarization diagrams. The potentiostatic polarization technique measurements were performed to assess corrosion behavior and sealing quality (i.e., degree of sealing) of
... Show MoreDental implants can be made of various materials, and amongst them, titanium and titanium alloy were the materials of choice for dental implants for many years because of their biocompatibility. The two alloys have a high level of biocompatibility, a lower modulus of elasticity, and better corrosion resistance than other alloys. Thus, they are frequently utilized in biomedical applications and mostly replace stiff fabrics. The latest advances in a new strontium oxide–cp titanium composite alloy are the main topic of this research. With regard to biomedical applications, additions of strontium oxide were synthesized at three distinct weight percentages (2%, 4%, and 6% by wt%). Powder metallurgy was used to create the alloys, which
... Show More
(4)
(4)
This study was aimed to study the effect of adding transglutaminase (TGase) on the mechanical and reservation properties of the edible films manufactured from soybean meal protein isolate (SPI) and whey protein isolate(WPI). The results showed an improvement in the properties with increase in the WPI ratios. Thickness of the SPI films amounted 0.097 mm decreased to 0.096 mm for the WPI: SPI films at a ratio of 2:1, when TGase was added decreased to 0.075 mm. While the tensile strength increased from 7.64 MPa for SPI films to eight MPa for the WPI: SPI films at a ratio of 2:1, when TGase was added increased to 11.04 MPa. Also, the elongation of the WPI: SPI films at a ratio of 2:1 presence of the TGase decreased to 40.6% compared wit