Alloy of (HgTe) has been prepared succesful in evacuated qurtz ampoule at pressure 4×10-5torr, and melting temperature equal to 823K for five days. Thin films of HgTe of thickness 1μm were deposited on NaCl crystal by thermal evaporation technique at room temperature under vacuum about 4×10-5torr as well as investiagtion in the optical porperties included (absorption coefficient , energy gap) of HgTe films and The optical measurements showed that HgTe film has direct energy gap equal to 0.05 eV. The optical constants (n, k, εr, εi) have been measured over will range (6-28)μm.

Out of a total of fifty samples, thirty-five isolates were identified as Serratia marcescens. Thesediverse clinical samples were collected over a three-month period, from October 2023 to December 2023, fromseveral hospitals in Baghdad, including Fatima Al-Zahraa Hospital, Al-Sader Hospital, Ibn Al-Balady Hospital,and Al-Imam Ali Hospital. The clinical samples primarily included urine from patients with urinary tractinfections (UTIs). All isolates were cultured on nutrient agar, MacConkey agar, and blood agar, and theiridentities were confirmed through biochemical testing and the Vitek 2 compact system. Based on phenotypicvirulence factors, the S. marcescens isolates showed varying positive patterns: 32 out of 35 (91.42%) forprotease

Supernova explosions are described as very violent events which transfer a significant amount of energy to interstellar media and are responsible for a large variety of physical processes. This study does not discuss the actual explosion mechanisms but follows the behavior of the dynamical evolution of some selected type I and type II supernova remnant and particularly after a thousand years from their explosion and shows how the density of the medium affects the evolution and the lifetime of each remnant. By studying such behaviors, a simplified model has been proposed here for the velocity and radius of the remnant after thousand years of explosion that depends only on the density of the medium and age of the remnant. It has been found th

The effect of different doses of gamma rays that emitted from 60Co on the development of different stages of lesser grain borer Rhyzopertha dominica (Fab.) was investigated . The results showed that the eggs in both early (1-3 days) and late (7-9) old were very sensitive to gamma rays and its hatch was zero at 10 Gy for both ages in comparison with 83.3% for the control group. Furthermore, the results illustrated that the larval stage in its two old ages were different in the radiosensitivity, the percent of its death were 100% & 96.6% when they exposed to 100 & 120 Gy, respectively. Moreover, the results showed that the sensitivity of pupal stage at age of 1-3 days was increased with increasing the doses of gamma rays, the percent of no

Abstract

The entities responsible for regulating the financial market are seeking to provide high quality accounting information, to provide appropriate protection to investors, and thus encourage them and attract them to increase their investments. the research reached several conclusion, the most prominent of which comes  :-

1-The production of high quality accounting information reduces investment costs and costs of processing accounting information.

2- The production of high quality accounting information helps investors identify the best investment opportunities.

3- The results of the statistical analysis showed that there is significant

A d.c. magnetron sputtering system was designed and fabricated. The chamber of this system is consisted from two copper coaxial cylinders. The inner one used as the cathode and the outer one used as anode with magnetic coil located on the outer cylinder (anode). The axial behavior of the magnetic field strength along the cathode surface for various coil current (from 2A to 14A) are shown. The results of this work are investigated by three cylindrical Langmuir probes that have different diameters that are 2.2mm, 1mm, and 0.45mm. The results of these probes show that, there are two Maxwellian electron groups appear in the central region. As well as, the density of electron and ion decreases with increases of magnetic field strengths.

This paper has investigated experimentally the dynamic buckling behavior of AISI 303 stainless steel Aluminized and as received long columns. These columns, hot-dip aluminized and as received, are tested under dynamic buckling, 22 specimens, without aluminizing (type 1), and 50 specimens, with hot-dip aluminizing at different aluminizing conditions of dipping temperature and dipping time (type 2), are tested under dynamic compression loading and under dynamic combined loading (compression and bending) by using a rotating buckling test machine. The experimental results are compared with Perry Robertson interaction formula that used for long columns. Greenhill formula is used to get a mathematical model that descripts the buckling behavior