Application of zirconia surface coating to improve fracture resistance and stress distribution of zirconia ceramic restorations
...Show More Authors

Zirconia ceramic restoration (ZCR) has a higher fracture incidence rate than metal ceramic restoration. Different surface treatments were used to improve fracture performance of ZCR such as grit blasting (GB) by aluminium oxide powder. This type of surface treatment generate residual stresses on veneering ceramic causing crack initiation and ending with a fracture. In order to overcome the stress generated by GB, zirconia surface coating is used as a surface treatment to improve fracture resistance and to accommodate stresses along the ZCR layers. Fifty zirconia ceramic crowns were fabricated and divided according to the type of surface treatment into three groups; the first group is (ZG), involving 20 cores were coated with a mixture of partially-sintered zirconia powder (PZP) and glaze ceramic powder; the second group is (ZL), including of 20 cores were coated with PZP and liner ceramic paste. The third group is grit blasting (GB), preparing of 10 fully sintered cores at 1350 °C which then abraded by 50 µm aluminium oxide powder. The groups ZG and ZL were further subdivided into ZG26, ZG47, ZL26 and ZL47 based on two PZP sizes (47 and 26 µm). Each treated core was veneered with the veneering ceramic layer. Fracture resistance (FR) was measured by the universal testing machine. Finite element analysis (FEA) was used to simulate the stress distributions on the coated and non-coated zirconia crown models. The ZG47 group had higher FR (647.92 ± 97.33 N) and a significant difference (P < 0.00) compared to GB and other coated groups. The FEA exhibited lower and evenly distributed stresses of the zirconia glaze model than the zirconia liner and the non-coated models. The ZG47 coating considered as an alternative method to GB treatment which increases the FR which significantly improved the clinical performance of the ZCR.

Scopus
Publication Date
Sun Jan 15 2023
Journal Name
Dental Hypotheses
Effect of addition of polymerized polymethyl methacrylate (PMMA) and zirconia particles on impact strength, surface hardness, and roughness of heat cure PMMA: An in vitro study
...Show More Authors

Introduction: This study was designed to examine the effects of addition of the combination of polymerized polymethyl methacrylate (PMMA) and zirconia (ZrO2) particles to heat cure PMMA resin on impact strength, surface hardness, and roughness. Methods: The 70% (w/w) of polymerized PMMA powder (particle size: 0.70mm) was mixed with 30% (w/w) of zirconia powder (ZrO2) (1mm) to produce PMMA-ZrO2 filler. Ninety acrylic specimens created were divided into three groups containing 0% wt (Control group), 2% wt, and 4% wt, PMMA-ZrO2 filler. Ten specimens were used for impact strength, surface hardness and roughness test, blindly. Data were analyzed via oneway ANOVA and the Tukey post hoc test using R 3.6.3. Results: There was statistically signific

... Show More
Publication Date
Fri Jun 28 2013
Journal Name
Journal Of Materials Science And Engineering B
Synthesis of Zirconia Nanoparticles in Distilled Water Solution by Laser Ablation Technique
...Show More Authors

Pulsed laser ablation in liquid (PLAL) has become an increasingly important technique for metals production and metal oxides nanoparticles (NPs) and others. This technique has its many advantages compared with other conventional techniques (physical and chemical). This work was devoted for production of zirconia (ZrO2) nanoparticles via PLAL technique from a solid zirconium target immersed in a wet environment in order to study the effect of this environment on the optical properties and structure of ZrO2 nanoparticles. The solutions which used for this purpose is distilled water (D.W). The produces NPs were characterized by mean of many tests such as UV-visible (UV-Vis.), transmission electron microscope (TEM) and Z-Potential. The UV-Vis.

... Show More
View Publication Preview PDF
Crossref (3)
Crossref
Publication Date
Fri Jan 01 2021
Journal Name
Materials Today: Proceedings
Evaluation of mechanical properties and cytotoxicity of maxillofacial silicone material after incorporation of zirconia nanopowder
...Show More Authors

Resilient polymeric materials such as silicone elastomers are currently used for maxillofacial prostheses construction but the strength of these materials and their clinical performance need to be optimized with the addition of reinforcing fillers. This study investigates the effect of zirconia nanopowder addition on tear strength, tensile strength, elongation at break, Shore A hardness, surface roughness and cytotoxicity of VST-50 maxillofacial silicone. Silicone base was mixed with different amounts (1%, 2% and 3%) of zirconia nanopowder using a vacuum mixer. Silicone without filler was used as control for comparison. Scanning Electron Microscopy and Atomic Force Microscopy were utilized to assess the efficiency of high-shear vacuum mixin

... Show More
View Publication
Scopus (11)
Crossref (5)
Scopus Clarivate Crossref
Publication Date
Tue Mar 11 2025
Journal Name
Journal Of Baghdad College Of Dentistry
Evaluation of fracture strength of endodontically treated teeth restored by milled zirconia post and core with different post and core systems (An in vitro comparative study)
...Show More Authors

Background: Restoration of root canal treated teeth with a permanent restoration affect in the success of endodontically treated teeth. This in vitro study was performed to evaluate and compare the fracture strength of endodontically treated teeth restored by using custom made zirconium posts and cores, prefabricated carbon fiber, glass fiber and zirconium ceramic posts. Materials and method: Forty intact human mandibular second premolars were collected for this study and were divided into five groups. Each group contains 8 specimens: Group1: Teeth restored with Carbon Fiber Posts; Group2: Teeth restored with Glass Fiber Posts; Group3: Teeth restored with Zirconium Ceramic prefabricated Posts; Group4: Teeth restored with Zirconium Posts

... Show More
View Publication Preview PDF
Publication Date
Mon Jan 01 2018
Journal Name
Aip Conference Proceedings
The study of behavior titanium pure commercially coated with hydroxyapatite and zirconia
...Show More Authors

View Publication
Scopus Clarivate Crossref
Publication Date
Thu Jun 15 2017
Journal Name
Journal Of Baghdad College Of Dentistry
Fracture Resistance of Endodontically Treated Premolar Teeth with Extensive MOD Cavities Restored with Different Bulk Fill Composite Restorations (An In vitro Study)
...Show More Authors

Background: The present in-vitro study was undertaken to evaluate and compare fracture resistance of weakened endodontically treated premolars with class II MOD cavities restored with different bulk fill composite restorations (EverX posterior, Alert, Tetric EvoCeram Bulk Fill, and SDR). The type and mode of fracture were also assessed for all the experimental groups. Materials and Method: Forty-eight human adult maxillary premolar teeth were selected for this study. Standardized extensive class II MOD cavities with endodontic treatment were prepared for all teeth, except those that were saved as intact control. The teeth were divided into six groups of eight teeth each (n=8): (Group 1) intact control group, (Group 2) unrestored teeth with

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Mon Feb 20 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Studying the Effect of Zirconia on Some Physical Properties of Porcelain
...Show More Authors

In this study porcelain was prepared by using composition consisting of raw materials with in following fractions , 50% kaolin , 25% feldspar, and 25% silica( SiO2) tested by XRay diffraction (XRD) method .Study the effect additives at different concentration from zirconia (ZrO2) (2,5,10,15,20) Wt% on some physical properties of porcelain, the sample is prepared by the conventional manufacturing method , It is found that some physical properties of porcelain changes considerably with the substituent sample, It was found that the increase of zrconia (ZrO2) additive of all our sample produce. Increasing in dielectric constant and bulk density and decreasing with open porosity and dielectric loss tangent

View Publication Preview PDF
Publication Date
Mon Jan 01 2018
Journal Name
Aip Conference Proceedings
Study the effect of nano SiO2 on dielectric strength property of zirconia
...Show More Authors

View Publication
Crossref (1)
Crossref
Publication Date
Mon Jan 01 2018
Journal Name
Aip Conference Proceedings
Study the effect of nano SiO2 on dielectric strength property of zirconia
...Show More Authors

View Publication
Scopus (3)
Crossref (1)
Scopus Clarivate Crossref
Publication Date
Sun Jun 01 2014
Journal Name
Baghdad Science Journal
Fracture Toughness and Hardness studying for Polymer-Ceramic Composite
...Show More Authors

A particulate composite material was prepared by adding the Titanium dioxide (TiO2) with a particle size of (75-150) µm to Epoxy resin at weight percentage of (10%,20%,30%,40%,50%).The following some mechanical properties were studied,fracture toughness, hardness.casting preparation methods were used in this study includes preparing plate of matrix and composites. specimens were prepared according to ASTM for the Mechanical properties tests. After that Another samples were heat treated for three and six hour at 65C?. Fracture toughness (Kic) represent for stress intensity factor results were showed that the curve of three hours aging increases in fracture toughness (Kic) for composites but for six hours aging increases fracture tough

... Show More
View Publication Preview PDF
Crossref