In this study, polymeric coating was developed by incorporating nano graphene in the polymer blend with applications to oil storage tanks. The oil storage tanks samples were brought from the oil Pipeline Company / Doura refinery in Baghdad. The coating polymer was formed with a blend (epoxy resin and repcoat ZR). The proportion of mixing the mixture was 3:1:1 epoxy resin 21.06 gm: repcoat ZR 10.53 gm: hardener 10.53 gm. The blend/graphene was prepared using in stui-polymerization method with different weight percentage 1, 3, 5, and 7 wt % added to blend. The resulting solution was put in a glass tube on a magnetic stirrer for one hour at a temperature of 40 °C. The result of contact angle and water absorption the best ratio of 3wt

Purpose: the purpose of this study is to investigate how managers working for the General Authority for Irrigation and Reclamation Projects react to the impact of Emotional Intelligence (EI) on their performance.   Theoretical framework: The current study includes an intellectual framework on two variables, namely EI and Manager Performance (MP), because it is essential to investigate the relationship between these two variables and the impact of EI on MP.   Design/methodology/approach: The research problem is that a manager's capacity to make wise decisions about their work or interactions with subordinates is diminished when they have inadequate EI. The questionnaire is used as a tool for gathering data for the study, and the st

In this work, the possibility to use new suggested carriers (D= Aspirin, Ibuprofen, Paracetamol, Tramal) is discussed for diclofenac drug (voltarine) by using quantum mechanics calculations. The calculation methods (PM3) and (DFT) have been used for determination the reaction path of (O-D) bond rupture energies. Different groups of drugs as a carrier for diclofenac prodrugs (in a vacuum) have been used; at their optimized geometries. The calculations included the geometrical structure and some of the physical properties, in addition to the toxicity, biological activity, and NLO properties of the prodrugs, investigated using HF method. The calculations were done by Gaussian 09 program. The comparison was made for total energies of reactan

This study was design to characterize the immune response in experimentally Pseudomonas aeruginosa mastitis mice treated probiotic bifidocin and cazacin of Bifidobacterium spp. and Lactobacillus casei. We quantified the level of the IFN-γ and TNF-α cytokines in blood by ELISA technique. IFN-γ level was significantly higher in infected group compared to control (340.21 ± 41.61, 8.45 ± 0.83 pg/ml, respectively). While the level of IFN-γ was significantly higher in mastitis mice than bifidocin and cazacin treated mice. Also, TNF-α level showed a significant increase in mastitis mice compared to controls (320.11±40.33, 8.45±0.83pg/ml, respectively). Among mastitis and bifidocin (9 and 18 mg/ml), cazacin (11 and 22 mg/ml) treate

Background: The study was designed to evaluate the effect of local application of exogenous VEGF/collagen I separately and as a combination in socket healing. Sixty male Albino Wistar rats were subjected for a surgical tooth extraction of upper 1st molar of both sides (right side was considered as experimental site, while left be the control one, treated with 1µL of normal saline). The rats were scarified at 3, 7, 14, 28 days post extraction. Socket healing was histologically examined with immunohistochemistochemical localization of ALP&FGF2. Materials and Method: Sixty male Albino Wistar rats were subjected for a surgical tooth extraction of upper 1stmolar of both sides (right side was considered as experimental site, while left be the

Abstract

    Binary polymer blend was prepared by mechanical mixing method of unsaturated polyester resin with Nitrile Butadiene Rubber (NBR) with different weight ratios (0, 5, 10 and 15) % of (NBR). Tensile characteristics and wear rates of these blends were studied for all mixing ratios. The microstructure of fracture surfaces of the prepared samples were investigated by optical microscope. The results were showed that strain rates of the resin material increase after blending it with rubber while the ultimate tensile strength and Young’s modulus values of it will decrease. It is also noticed that the wear rate of resin decreases with increasing of (NBR) content.

Keywords:<

Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f

Abstract: In this paper, a U-shaped probe with a curvature diameter of half a centimeter was implemented using plastic optical fibers. A layer of the outer shell of the fibers was removed by polishing to a D-section. The sensor was tested by immersing it in a sodium chloride solution with variable refractive index depending on solution concentrations ranging from 1.333 to 1.363. In this design, the sensor experienced a decrease in its intensity as the concentration of the solution increased. The next step The sensor was coated with a thin layer of gold with a thickness of 20 nm, and the sensor was tested with the same solutions which resulted in a shift in wavelengths where the shift in wavelength was 5.37 nm and sensiti