The zirconia ceramic restoration (ZCR) is used as substitutes for the metal-ceramic restoration. Clinical studies demonstrating of ZCRs showed a high fracture incidence of veneering layer than metal-ceramic restorations. This attributed to the low bond strength of zirconia to veneering ceramic as a result of lacking of glass content in its matrix. Surface treatment was proposed to improve the bonding strength between zirconia and veneering ceramic. Several studies revealed that some treatment such as airborne particle abrasion (APA) is responsible for generating chipping of veneering ceramic. The study aimed to develop a new zirconia coatings to increase bonding strength between zirconia substrate and veneering porcelain. Three groups of 150 zirconia specimens (discs, rods and crowns) were divided according to the type of surface treatments; Group M1 designated unsintered zirconia specimens coated with a mixture of glaze porcelain powder and partially-sintered zirconia powder prepared at 1100 °C with two particle sizes; A (26 ± 0.3 μm) and size B (47 ± 0.5 μm), group M2 was coated with mixture of ceramic liner paste and same selected particle sizes of partially-sintered zirconia powders. The coated groups (M1 and M2) subdivided according to powder sizes into M1A, M1B, M2A and M2B. APA group (as control) of sintered zirconia specimens abraded with 50 μm aluminium oxide powder. Surface area roughness (Sa) was measured by surface texture analyser. Surface morphology and elemental composition were analysed by scanning electron microscope (SEM). Crystallographic phases were identified by X-ray diffraction (XRD). The coefficient of thermal expansion (CTE) was assessed by a thermomechanical analyser. For shear bond strength (SBS) test was evaluated by a universal testing machine (UTM). The fracture strength (FS) test prepared and measured by Cercon CAD/CAM system and UTM. Fractographic analysis for SBS and FS were examined by a stereomicroscope and SEM. For each test and measurement, 10 specimens were used per group. Finite element analysis (FEA) was used to simulate and predict the iv stress distributions of the static oblique load in coated and non-coated zirconia crown models. The collected data were analysed by one-way ANOVA and Tukey HSD test at (P<0.05). Surface roughness results showed significant differences among all groups (P<0.000). The M1B group exhibited a higher Sa value (10.33 ± 0.59 μm) among the tested groups. XRD analysis showed tetragonal and monoclinic phases in the control group while only tetragonal was detected in the coated groups. The SBS values for coated groups were higher than the control group. The M1B group showed higher and significant differences in SBS value (37.54 ± 4.38 MPa) among other tested groups (P<0.05). The FS test indicated that coated M1B group (647.92 ± 97.33 N) higher than the other groups (P<0.00). FEA showed the coated crown models have lower stress level than the non-coated model. The new coating (M1B) by airbrush spray technique considered as an alternative way to APA treatment to improve the bond strength of zirconia substrate to veneering ceramic and indicating as an applicable surface treatment for improving the clinical performance of the coated ZCR.
Background: This in vitro study was carried out to evaluate the effects of various veneering dentin ceramic thicknesses and repeated firings on the color of lithium disilicate glass-ceramic (IPS e.max Press) and zirconium-oxide (IPS ZirCAD) all-ceramic systems, measured by clinical spectrophotometers (Easyshade Advance 4.0) . Materials and methods: The 72specimens cube-shaped have the dimension of about 11 mm in width, 14 mm in length, 1mm in thickness, these cores divided into 3 groups according to the type of material each group have (24)core specimens. Each group had been divided into three sub-groups (each having 8 specimens) according to veneering with dentin ceramic thicknesses: as 0.5, 1, or 2 mm (n=8). IPS e.max press and ZirCAD c
... Show More
In this work, the copper metal was treated using Nd:YAG laser with energy 1Joul to enhance corrosion resistance and improve surface properties. The copper metal has many applications in industry as well as water, oil and gas pipes. The same conditions, (laser power density, scan speed, distance between paths, medium gas-air) were applied in the laser surface treatment, After laser treatment, the samples microstructures were investigated using optical microscope (OM) to examine micro structural changes due to laser irradiation. Specimen surfaces were investigated using atomic force microscopy (AFM), X-ray diffraction (XRD), macro hardness, and corrosion test before and after laser treatment to
... Show More
(3)
Objective: To evaluate and compare the effect of mechanical surface treatment (groove, aluminum oxide particles)
with 45 degree bevel type of joint on tensile bond strength of acrylic specimens repaired by two curing methods
(microwave and water both).
Methodology: Eighty specimens (80) were prepared from pink heat cure acrylic resin. They were divided into two
main groups (40 specimen repaired by microwave energy and 40 specimens repaired by water bath method).Each
group can be divided into four subgroups of ten according to the surface treatment. The control group A was left
intact, group B received no surface treatment, group C and D received surface treatment by (groove, 50 m aluminum
oxide particles). Specimens
Background The application of nanotechnology to biomedical surfaces is explained by the ability of cells to interact with nanometric features. The aim of this study was to consider the role of nanoscale topographic modification of CPTi dental implant using chemical etching method for the purpose of improving osseointegration. Materials and methods: Commercial pure titanium rod was machined into 20 dental implants. Each implant was machined in diameter about 3mm, length of 8mm (5mm was threaded part and 3mm was flat part). Implants were prepared and divided into 2 groups according to the types of surface modification method used: 1st group (10 implant) remained without nano surface modification (control), 2nd group include (10 implant) etche
... Show MoreObjective: This study evaluated the effect of immediate dentin sealing on the marginal adaptation of lithium disilicate overlays with three different types of resin-luting agents: preheated composite, dual-cure adhesive resin, and flowable composite. Materials and Methods: Forty-eight maxillary first premolars of similar size were prepared with a butt joint preparation design. The teeth were separated into two primary groups, each with twenty-four teeth: Group DDS: Delay dentin sealing (non-IDS) teeth were not treated. Group IDS: dentin sealing was applied immediately after teeth preparation. Each group was subsequently separated into three separate subgroups. Subgroups (DDS+Phc, IDS+Phc): cemented with preheated composite (Enamel plus HRi,
... Show More
(1)
As a result of the exacerbation of the problem of water pollution, research was directed towards studying the treatment using ceramic membranes, which proved to be highly effective in treating all water sources. The research aims to study the possibility of preparing a new type of ceramic membranes from Syrian zeolite that was not previously used in this field. In this research, ceramic membranes were prepared from Syrian raw zeolite in several stages. Zeolite sample was characterized, grinded, mixed with boric acid, pressed to form desks, treated thermally according to experiment program, finally coated with silver nanoparticles. Specifications of prepared membranes were determined according to reference methods, effectiveness of prepar
... Show More
(1)
(1)
(1)
The current research is concerned with methods of formation and their effect on the sintering process of ceramic materials. The research is divided into a number of chapters. The first chapter addressed the research structure (the research problem, importance, objective, limits, and it also defined the terms used in the research). The second chapter addressed the theoretical framework, where the theoretical framework has been divided into three sections. The first section dealt with methods of formation of ceramic materials including: Plasticizing method 2- semi-dry pressing method 3- dry pressing method 4- extrusion method 5- casting method.
The researcher found that there is a clear difference between the methods through her formati
One of the most important problems facing the world today is the energy problem. The solution was in finding renewable energy sources such as solar energy. The solar energy applications in Iraq is facing many problems . One of the most important problems is the accumulation of dust on the solar panels surface which causes decreasing its performance sharply. In the present work, a new technique was presented by using two-axis solar tracking system to reduce the accumulated dust on the solar panel surface and compared it with the fixed solar panels which installed at tilt angles 30° and 45°. The results indicated that the maximum losses of the output power due to accumulation of dust on the fixed solar panels is about 31.4% and 23.1% res
... Show MoreAbstract Objectives: Malocclusion was and remains one of the most common problems which affects the psyche and social status of the individual, so the estimation of the malocclusion severity and needs a percentage of orthodontic treatment of Iraqi patients is the aim of this study. Method: A randomly selected 150 pairs of study models (48 male and 102 female) were involved in this study for patients attending an orthodontic clinic at College of Dentistry/ University of Baghdad seeking for treatment. The DAI scores were collected according to WHO guidelines directly from the study model with a digital caliper, score was calculated using the regression equation of 10 occlusal traits. The dental casts were classified into four groups to determ
... Show More