The zirconia ceramic restoration (ZCR) is used as substitutes for the metal-ceramic restoration. Clinical studies demonstrating of ZCRs showed a high fracture incidence of veneering layer than metal-ceramic restorations. This attributed to the low bond strength of zirconia to veneering ceramic as a result of lacking of glass content in its matrix. Surface treatment was proposed to improve the bonding strength between zirconia and veneering ceramic. Several studies revealed that some treatment such as airborne particle abrasion (APA) is responsible for generating chipping of veneering ceramic. The study aimed to develop a new zirconia coatings to increase bonding strength between zirconia substrate and veneering porcelain. Three groups of 150 zirconia specimens (discs, rods and crowns) were divided according to the type of surface treatments; Group M1 designated unsintered zirconia specimens coated with a mixture of glaze porcelain powder and partially-sintered zirconia powder prepared at 1100 °C with two particle sizes; A (26 ± 0.3 μm) and size B (47 ± 0.5 μm), group M2 was coated with mixture of ceramic liner paste and same selected particle sizes of partially-sintered zirconia powders. The coated groups (M1 and M2) subdivided according to powder sizes into M1A, M1B, M2A and M2B. APA group (as control) of sintered zirconia specimens abraded with 50 μm aluminium oxide powder. Surface area roughness (Sa) was measured by surface texture analyser. Surface morphology and elemental composition were analysed by scanning electron microscope (SEM). Crystallographic phases were identified by X-ray diffraction (XRD). The coefficient of thermal expansion (CTE) was assessed by a thermomechanical analyser. For shear bond strength (SBS) test was evaluated by a universal testing machine (UTM). The fracture strength (FS) test prepared and measured by Cercon CAD/CAM system and UTM. Fractographic analysis for SBS and FS were examined by a stereomicroscope and SEM. For each test and measurement, 10 specimens were used per group. Finite element analysis (FEA) was used to simulate and predict the iv stress distributions of the static oblique load in coated and non-coated zirconia crown models. The collected data were analysed by one-way ANOVA and Tukey HSD test at (P<0.05). Surface roughness results showed significant differences among all groups (P<0.000). The M1B group exhibited a higher Sa value (10.33 ± 0.59 μm) among the tested groups. XRD analysis showed tetragonal and monoclinic phases in the control group while only tetragonal was detected in the coated groups. The SBS values for coated groups were higher than the control group. The M1B group showed higher and significant differences in SBS value (37.54 ± 4.38 MPa) among other tested groups (P<0.05). The FS test indicated that coated M1B group (647.92 ± 97.33 N) higher than the other groups (P<0.00). FEA showed the coated crown models have lower stress level than the non-coated model. The new coating (M1B) by airbrush spray technique considered as an alternative way to APA treatment to improve the bond strength of zirconia substrate to veneering ceramic and indicating as an applicable surface treatment for improving the clinical performance of the coated ZCR.
The present study was designed in the aquaculture and fish nutrition research aquarium in the College of Veterinary Medicine/Baghdad University from a period 1/3 to 1/6/2013 to investigate the toxicity of the herbicide glyphosate aqua on Barbus sharpeyi fish. Fish fingerlings were used with average weight between 10 – 15 gm to measure the (LC50), and 200 fingerlings were used to know the acute and chronic toxic effect for the herbicide. The fingerlings were randomly distributed as 10 fish for each aquarium. Fish were divided into four treatments and control group (without addition of herbicide). The first processing with a concentration of 0.415 mg/L for a duration of exposure 90 days, the second processing group with a concentration 0.
... Show More
EP/ metal composites were prepared as adhesives between two steel rods. Epoxy resin (EP) was used as a matrix with metal as fillers (Al, Cu, Fe,).
The preparation method for tensile adhesion tests includes two steel rods with adhesive composites between the rods to measure adhesion strength Sad and adhesion toughness Gad.
Results of tensile adhesion tests show that EP/ metals composite have maximum strength Sad for certain weight percentage of metals 2.95 and 9MPa at 10% for EP/Al and EP/Cu composite and 8.2MPa at 40% for EP/Fe composites
In this research, (MOORA) approach based– Taguchi design was used to convert the multi-performance problem into a single-performance problem for nine experiments which built (Taguchi (L9) orthogonal array) for carburization operation. The main variables that had a great effect on carburizing operation are carburization temperature (oC), carburization time (hrs.) and tempering temperature (oC). This study was also focused on calculating the amount of carbon penetration, the value of hardness and optimal values obtained during the optimization by Taguchi approach and MOORA method for multiple parameters. In this study, the carburization process was done in temperature between (850 to 950 ᵒC) for 2 to 6
... Show More
(2)
(5)
The present work shows a theoretical results that have been used the functional Hybrid of three parameters Lee-Yang-Parr (B3LYP) of the quantum mechanical approach for density functional theory with (Spanish Initiative for Electronic Simulations with Thousands of Atoms) SIESTA code. All calculations were carried out employing the used method at the Gaussian 09 package of programs. It was reported the main point for research on dominance of the bandgap of elongated pi-conjugated molecules by using different chemical groups replacing hydrogen atom in the most molecules that used in this work. The side groups creates another factor that controls the value of the band gap. The dihedral angle between the two pheny
... Show More
We have investigated the impact of laser pulse wavelength on the quantity of ablated materials. Specifically, this study investigated the structural, optical, and morphological characteristics of tungsten trioxide (WO3) nanoparticles (NPs) that were synthesized using the technique of pulsed-laser ablation of a tungsten plate. A DD drop of water was used as the ablation environment at a fixed fluence at 76.43 J/cm2 and pulse number was 400 pulses of the laser. The first and second harmonic generation ablations were carried out, corresponding to wavelengths of 1064 and 532 nm, respectively. The Q-switched Nd: YAG laser operates at a repetition rate of 1 Hz and has a pulse width of roughly 15 ns. These parameters are applicable to both wavelen
... Show More
(8)
(8)
The stability and releasing profile of 2:1 core: wall ratio ibuprofen microcapsules prepared by aqueous coacervation (gelatin and acacia polymers coat) and an organic coacervation methods (ethyl cellulose and sodium alginate polymers coat) in weight equivalent to 300mg drug, were studied using different storage temperatures 40°C, 50°C ,60°C and refrigerator temperature 4°C in an opened and closed container for three months (releasing profile) and four months (stability study).It was found that, these ibuprofen microcapsules were stable with expiration dates of 4.1 and 3.1 years for aqueous and an organic method respectively.Aqueous prepared ibuprofen microcapsules were found more stable than those microcapsules prepared by or
... Show More
A hand lay-up method was used to prepare Epoxy/ metal composites. Epoxy resin (EP) was used as a matrix with metal particles (Al, Cu, and Fe) as fillers.
The preparation method includes preparing square panels of composites with different weight percentage of fillers (10, 20, 30, 40, and 50%). Standard specimens (88mm in diameter) for thermal conductivity tests were prepared to measure thermal conductivity kexp.The result of experimental thermal conductivity kexp, for EP/metal composites show that, kexp increase with increasing weight percentage, For EP/ Al and EP/Cu composites, and it have have maximum values of 0.33 and 0.35 W/m.K, respectively. While kexp for EP/ Fe composite show slight increase with maximum value of 0.186 W/m.K.
PbxCd1-xSe compound with different Pb percentage (i.e. X=0,
0.025, 0.050, 0.075, and 0.1) were prepared successfully. Thin films
were deposited by thermal evaporation on glass substrates at film
thickness (126) nm. The optical measurements indicated that
PbxCd1-xSe films have direct optical energy gap. The value of the
energy gap decreases with the increase of Pb content from 1.78 eV to
1.49 eV.