The alfalfa plant, after harvesting, was washed, dried, and grinded to get fine powder used in water treatment. We used the alfalfa plant with ethanol to make the alcoholic extract characterized by using (GCMass, FTIR, and UV) spectroscopy to determine active compounds. Alcoholic extract was used to prepare zinc nanoparticles. We characterized Zinc nanoparticles using (FTIR, UV, SEM, EDX Zeta potential, XRD, AFM). Zinc nanoparticle with Alfalfa extract and alfalfa powder were used in the treatment of water polluted with inorganic elements such as Cr, Mn, Fe, Cu, Cd, Ag by (Batch processing). The batch process with using alfalfa powder gets treated with Pb (51.45%), which is the highest percentage of treatment. Mn (13.18%), which is the lowe

The alfalfa plant, after harvesting, was washed, dried, and grinded to get fine powder used in water treatment. We used the alfalfa plant with ethanol to make the alcoholic extract characterized by using (GC-Mass, FTIR, and UV) spectroscopy to determine active compounds. Alcoholic extract was used to prepare zinc nanoparticles. We characterized Zinc nanoparticles using (FTIR, UV, SEM, EDX Zeta potential, XRD, AFM). Zinc nanoparticle with Alfalfa extract and alfalfa powder were used in the treatment of water polluted with inorganic elements such as Cr, Mn, Fe, Cu, Cd, Ag by (Batch processing). The batch process with using alfalfa powder gets treated with Pb (51.45%), which is the highest percentage of treatment. Mn (13.18%), which is the

This study was carried out in epidemically field with common reed (Phragmites communis Trin.) plants in the Nassiriah cityThiQur governorate ,during 2009/2010 to investigate the influence of plant growth regulator gibberellin (GA3)and cytokinin (CK) in increasing the efficacy of glyphosate and Fluazifop-butyl in common reed control . Factorial experiment in RCBD was used with three replications in tow Factors . Glyphosate 3500mg .l־¹ gave the higher mean of injury score of common reed and lower mean of common reed shoots , shoots dry weight and rhizome dry weight(3.59,22.01 shoot /0.5m² ,0.57Kg / 0.5m² and 250.50gm /0,5m² ),respectively. All plant growth regulators gaves the higher means of common reed shoots and rhizome dry weight com

Irinotecan induced-mucositis is an inflammatory event of intestine caused by an increase in concentration of active metabolite 7­ethyl­10-hydroxycamptothecin (SN­38) in the intestine. Irinotecan must first be converted by a carboxylesterase (CES) to the active metabolite (SN­38), which is subsequently glucuronidated by the hepatic enzyme to SN38G. The SN-38G is deconjugated in the intestine to SN-38 via ?-glucuronidase produced by the intestinal bacterial flora, which accounts for SN-38 delayed intestinal mucositis of irinotecan. To study the protective effect of mentha in irinotecan-induced mucositis, intestinal mucositis induced by I.P injection of irinotecan (75mg/Kg/day) for 4 days. Mentha ethanolic extract orally administered to

The protective effect of ginger extract against cisplatin-induced hepatotoxicity and cardiotoxicity was evaluated in 30 albino white rats(weighing 200-300 gm ) classified into 5groups (6 rats per each group). The rats were treated with 0.5g/kg/day or         1g/kg/day ginger extract orally 5 successive days before and 5 successive days after induction of toxicity with intraperitoneal (IP) injection of (10mg/kg ) cisplatin, resulted in a significant reduction in the levels of aspartate aminotransferase (AST), alanine aminotransferase (ALT) , total serum  billirubin(TSB) , lactate dehydrogenase (LDH) and creatine kinase(CK) enzymes in comparison with the cisplatin treated animals; ginger extract

This article presents the results of an experimental investigation of using carbon fiber–reinforced polymer sheets to enhance the behavior of reinforced concrete deep beams with large web openings in shear spans. A set of 18 specimens were fabricated and tested up to a failure to evaluate the structural performance in terms of cracking, deformation, and load-carrying capacity. All tested specimens were with 1500-mm length, 500-mm cross-sectional deep, and 150-mm wide. Parameters that studied were opening size, opening location, and the strengthening factor. Two deep beams were implemented as control specimens without opening and without strengthening. Eight deep beams were fabricated with openings but without strengthening, while

This article presents the results of an experimental investigation of using carbon fiber–reinforced polymer sheets to enhance the behavior of reinforced concrete deep beams with large web openings in shear spans. A set of 18 specimens were fabricated and tested up to a failure to evaluate the structural performance in terms of cracking, deformation, and load-carrying capacity. All tested specimens were with 1500-mm length, 500-mm cross-sectional deep, and 150-mm wide. Parameters that studied were opening size, opening location, and the strengthening factor. Two deep beams were implemented as control specimens without opening and without strengthening. Eight deep beams were fabricated with openings but without strengthening, while

Fatigue failure is almost considered as the predominant problem affecting automotive parts under dynamic loading condition. Thus, more understanding of crack behavior during fatigue can strongly help in finding the proper mechanism to avoid the final fracture and extent the service life of components. The main goal of this paper is to study the fracture behavior of low carbon steel which is used mostly in automotive industry. For this purpose, the fractography of samples subjected to high and low stress levels in fatigue test then was evaluated and analyzed. Hardness and tensile tests were carried out to determine the properties of used steel. Also, the samples were characterized by microstructure test and XRD analysis to examine the con

Graphene oxide GO was functionalized with 4-amino, 3-substituted 1H, 1, 2, 4 Triazole 5(4H) thion (ASTT) to obtain GOT. GOT characterized by FT-IR, XRD.via modification of the working electrode of the SPCE with the prepared nanomaterial (GOT) the effect of scan rate and pH on the determination of Amoxilline (AMOX) was studied using cyclic voltammetry. AMOX show various responses at pH ranging from 2 to 7 and also was observed sharp increase in the oxidation peaks in the pH 3. The formal potential (midpoint) for AMOX was highly pH-dependent. From the effect of scan rate, surface coverage concentration Γ of electroactive species the values of the electron transfer coefficient and the electron transfer constant rate ket was obtained as 5.39×

a porentioncsisteve has been carried out of the corrosion behavior of inconel(600) in chloride ions (Cl) over the tempreatures 293 over the temperatures 308K in both the dcacrated and the alloy