Experimental work was carried out to investigate the effect of fire flame (high temperature) on specimens of one way slabs using Self Compacted Concrete (SCC). By using furnace manufactured for this purpose, twenty one reinforced concrete slab specimens were exposed to direct fire flame. All of specimens have the same dimensions. The slab specimens were cooled in two types, gradually by left them in the air and suddenly by using water. After that the specimens were tested under two point loads, to study, the effect of
different: temperature levels (300ºC, 500ºC and 700ºC), and cooling rate (gradually and sudden cooling conditions) on the concrete compressive strength, modulus of rupture, flexural strength and the behavior of reinf

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

Background: Poly (methylmethacrylate) is the most widely used material in denture fabrication. The characteristics of acrylic resin which support microorganism development can threaten the oral health of denture users. This study was assigned to prepareand incorporate Ag-Zn zeolite powder into heat cured denture base material as antimicrobial material and to investigate its effect on some properties of heat cured acrylic denture base materials. Materials and methods: Sliver –zinc zeolite was prepared by ion exchange method and characterized then incorporated into poly (methylmethacrylate) powder in0.5% by weight. Specimens were constructed and divided into 6 groups according to the using tests; each group was subdivided into 2 groups

This study was carried out at Poultry Research Station, State Board of Agricultural Research, Ministry of Agriculture for the period from 27 September 2014 to 9 November 2014 to evaluate the Supplementation of different levels of Conjugated Linoleic Acid (CLA) on productive performance of broiler. Four hundred eighty chicks (Ross-308),one day old were randomly distributed to four dietary treatments for 42 days of age with 3 replicates/vtreatment (40 bird/replicate). Experimental treatments were as follow; T1 (Control diet) without supplement, while the treatment T2,T3 and T4  were Supplemented with 1, 1.5, 2 g CLA /kg diet  respectively. The results showed significant (P ≤ 0.05) increased in mean of body weight, weight gain, ave

Background: The geriatric patients wearing removable partial dentures are increasing in proportion. At the same time, the root caries prevalence accompanied by gingival recession is increasing. A variety of vehicles can deliver fluoride into the oral cavity, including fluoride mouth-rinse, fluoride dentifrice, topical fluoride, and fluoride-releasing restorative materials, all of which effectively prevent root caries and suppress recurrent caries. This study aimed to evaluate the effect of sodium fluoride addition on some mechanical properties of heat cure acrylic denture base material. Material and method: A total of 90 samples were prepared in this study, then divided into three main groups according to the type of test used (hardness, te

The weight of larvae virgins and Alcamlat for males more than the weight of females of the roles themselves that the highest rate of loss in weight of larvae developed to virgins when field conditions were (21.5,22,21.3) mg during June and July and August respectively, recorded the highest degrees of heat and less attributed to moisture

The study was conducted to identify the toxicity of chromium on scenedesmus quadricauda algae alone and in the presence of nutrient metal (Nitrogen). Different concentrations of chromium (0.5, 1.5 , 2.5, 3.5 , 4.5mg/L) were used and the presence nitrogen is (5 ,10 ,50 ,100mg/L) on cultur media(chu-10) with used for cultivation of the algae in controlled conditions(25oC , light intensity 380 –?E/m2 /s. The results showed increasing in the toxicity of the metal when is alone , excess of concentrations an time of exposure. The growth rate decreased from 0.44 to 0.06 cell/ hour after 12 day of the biging of the experiment and of concentrate 4.5 mg/L of chromium. The intermediate active concentrations of the chromium(EC50) was increase

Stabilization of phenol trapped by agricultural waste: a study of the influence of ambient temperature on the adsorbed phenol