Thermomechanical analysis (TMA) and differential scanning calorimetry (DSC) are used to investigate the effect of molding and annealing of polyester on the behavior of thermal expansion and crystallization since these factors play role in the reprocessing or recycling of the polymer. The dynamic mode of the TMA provides enhanced characterization information about the polyester since it separates the transitions into reversible and irreversible signals, and also reveals the progress of the amorphous regions as the polyester loses strength with the increasing temperature approaching melting. Slow cooling after annealing brings crystallization that may be attributed to molecular chain straightening due to orientation.

In this work, two groups of nanocomposite material, was prepared from unsaturated polyester resin (UPE), they were prepared by hand lay-up method. The first group was consisting of (UPE) reinforced with individually (ZrO2) nanoparticles with particle size (47.23nm). The second group consists of (UPE) reinforced with hybrid nanoparticles consisting of zirconium oxide and yttrium oxide (70% ZrO2 + 30% Y2O3) with particles size (83.98nm). This study includes the effect of selected volume fraction (0.5%, 1%, 1.5%, 2%, 2.5%, 3%) for both reinforcement nano materials. Experimental investigation was carried out by analyzing the thermo-physical properties like thermal conductivity, thermal diffusivity and specific heat for the polymeric composit

The Cu2SiO3 composite has been prepared from the binary compounds (Cu2O, and SiO2) with high purity by solid state reaction. The Cu2SiO3 thin films were deposited at room temperature on glass and Si substrates with thickness 400 nm by pulsed laser deposition method. X-ray analysis showed that the powder of Cu2SiO3 has a polycrystalline structure with monoclinic phase and preferred orientation along (111) direction at 2θ around 38.670o which related to CuO phase. While as deposited and annealed Cu2SiO3 films have amorphous structure. The morphological study revealed that the grains have granular and elliptical shape, with average diameter of 163.63 nm. The electrical properties which represent Hall effect were investigated. Hall coeffici

New series of 4,4'-((2-(Aryl)-1H-benzo[d]imidazole-1,3(2H)-diyl)bis(methylene))Diphenol(3a-g) was successfully synthesized from cyclization of the reduction product of bis Schiff bases (2) with aryl aldehydes bearing phenolic hydroxyl in the presence of acetic acid. The structure of these compounds was identified from FT-IR, 1H NMR, 13C NMR and EIMs. The Antioxidant capability was screened by DPPH and FRAP assays. Both assays showed antioxidant capability more than BHT as well. Compounds 3b and 3c showed antioxidant capacity slightly less than ascorbic acid. The docking study for theses compound was carried out as III DNA polymerase inhibitor. The results of docking demonstrated that the increase in hinderances around phenolic hydr

New series of 4,4'-((2-(Aryl)-1H-benzo[d]imidazole1,3(2H)-diyl)bis(methylene))Diphenol(3a-g) was successfully synthesized from cyclization of the reduction product of bis Schiff bases (2) with aryl aldehydes bearing phenolic hydroxyl in the presence of acetic acid. The structure of these compounds was identified from FT-IR, 1H NMR, 13C NMR and EIMs. The Antioxidant capability was screened by DPPH and FRAP assays. Both assays showed antioxidant capability more than BHT as well. Compounds 3b and 3c showed antioxidant capacity slightly less than ascorbic acid. The docking study for theses compound was carried out as III DNA polymerase inhibitor. The results of docking demonstrated that the increase in hinderances around phenolic hydroxyl for t

The Electro-Fenton oxidation process is one of the essential advanced electrochemical oxidation processes used to treat Phenol and its derivatives in wastewater. The Electro-Fenton oxidation process was carried out at an ambient temperature at different current density (2, 4, 6, 8 mA/cm²) for up to 6 h. Sodium Sulfate at a concentration of 0.05M was used as a supporting electrolyte, and 0.4 mM of Ferrous ion concentration (Fe²⁺) was used as a catalyst. The electrolyte cell consists of graphite modified by an electrodepositing layer of PbO₂ on its surface as anode and carbon fiber modified with Graphene as a cathode. The results indicated that Phenol concentration decreases with an increase in current dens

Catalytic wet air oxidation of aqueous phenol solution was studied in a pilot plant trickle bed reactor using copperoxide catalyst supported on alumina and silica. Catalysts were prepared by impregnating method. Effect of feed solutionpH (5.9, 7.3, and 9.2), gas flow rate (20%, 50%, 80%, and 100%), WHSV (1, 2, and 3 h-1), temperature (120°C, 140°C,and 160°C), oxygen partial pressure (6, 9, 12 bar), and initial phenol concentration (1, 2, and 4 g/l).Generally, theperformance of the catalysts was better when the pH of feed solution was increased. The catalysts deactivation is relatedto the dissolution of the metal oxides from the catalyst surface due to the acidic conditions. Phenol oxidation reactionwas strongly affected by WHSV,

Catalytic wet air oxidation of aqueous phenol solution was studied in a pilot plant trickle bed reactor using copper
oxide catalyst supported on alumina and silica. Catalysts were prepared by impregnating method. Effect of feed solution
pH (5.9, 7.3, and 9.2), gas flow rate (20%, 50%, 80%, and 100%), WHSV (1, 2, and 3 h-1), temperature (120°C, 140°C,
and 160°C), oxygen partial pressure (6, 9, 12 bar), and initial phenol concentration (1, 2, and 4 g/l).Generally, the
performance of the catalysts was better when the pH of feed solution was increased. The catalysts deactivation is related
to the dissolution of the metal oxides from the catalyst surface due to the acidic conditions. Phenol oxidation reaction
was strongly

Room temperature ionic liquids show potential as an alternative to conventional organic membrane solvents mainly due to their properties of low vapour pressure, low volatility and they are often stable. In the present work, the technical feasibilities of room temperature ionic liquids as bulk liquid membranes for phenol removal were investigated experimentally. In this research several hydrophobic ionic liquids were synthesized at laboratory. These ionic liquids include (1-butyl-3-methylimidazolium bis (trifluoromethylsulfonyl) imide[Bmim][NTf₂], 1-Hexyl-3-methylimidazolium bis (trifluoromethylsulfonyl) imide[Hmim][NTf₂], 1-octyl-3-methylimidazolium bis (trifluoromethylsulfonyl)imide[Omim][NTf₂],1‐butyl