In the recent decade, injection of nanoparticles (NPs) into underground formation as liquid nanodispersions has been suggested as a smart alternative for conventional methods in tertiary oil recovery projects from mature oil reservoirs. Such reservoirs, however, are strong candidates for carbon geo-sequestration (CGS) projects, and the presence of nanoparticles (NPs) after nanofluid-flooding can add more complexity to carbon geo-storage projects. Despite studies investigating CO2 injection and nanofluid-flooding for EOR projects, no information was reported about the potential synergistic effects of CO2 and NPs on enhanced oil recovery (EOR) and CGS concerning the interfacial tension (γ) of CO2-oil system. This study thus extensively investigates the effect of silica NPs on the γ of CO2/decane system at elevated pressure and temperature to recognise the potential impact of NPs-injection on the future CGS projects. To achieve this, a wide-ranging series of tests have been conducted to reveal the role of hydrophilic and hydrophobic silica NPs on γ of the CO2/oil system. n-decane was utilized as model oil and different amounts of NPs were mixed with the oil phase. Oil-NPs dispersions were formulated using an ultrasonic homogenizer. The γ of the CO2/oil system was measured at different pressures (0.1 to 20 MPa) and temperatures (25 to 70 °C) using a high-pressure temperature optical cell. The γ data were measured using the pendant drop technique via axisymmetric drop shape analysis (ADSA). The results showed that, generally, CO2/oil γ subjected mainly to pressure, temperature, and with less extent to NPs load in the oil phase. γ decreases with increased pressure until reaching a plateau where no more significant decrease in γ was observed. The γ trend with increased temperature, on the other hand, was more completed. No significant impact of temperature on γ was recorded with low pressure (≤ 5 MPa). Similarly, at relatively high pressure (≥ 25 MPa), only a slight variation of IFT with temperature change was recorded. However, for the pressure range from 5 – 25 MPa, IFT was increased remarkably with temperature. Furthermore, NPs in the oil phase exhibit a remarkable influence on IFT. In this context, the presence of hydrophilic silica NPs in the oil phase can significantly reduce the γ of the CO2/decane system. However, hydrophobic silica NPs showed less influence on IFT reduction. The outcomes of this work afford good understandings into applications of NP for EOR and CGS applications and help to de-risk CO2-geological storage projects.
loaded reinforced concrete circular short columns. An experimental investigation into the behavior
of 24 short reinforced concrete columns with and without steel fibers was carried out. The columns
had a circular section (200 mm diameter and 900 mm long). Test variables include concrete
strength, spacing of spiral reinforcement, and inclusion of steel fibers. The axial stress and axial
strains were obtained and used to evaluate the effects of the presence of steel fibers. It was found
that the addition of steel fibers slightly improves the load carrying capacity of the tested columns
whereas it significantly enhances the ductility of these specimens. Test results also indicated that for
the same confinement parameter
(1)
The studying trying to determine the role of Strategic Intelligence on the Process of Green Manufacturing of Sample of Mineral water factories at Dahuk city. The study submit a theoretical frame of Strategic Intelligence and Green Manufacturing, a supposed sample, had been set to reverye the nature of the relations and effect in the study Varity, the study depend on group of the main and branch concurring with the relations and effect between the Strategic Intelligence and Green Manufacturing to answer the following questions about research to problems:
What are the relationships and effects between stra
... Show More
(2)
Abstract Background: The daily usage of maxillofacial prostheses causes them to mechanically deteriorate with time. This study was aimed to evaluate the reinforcement of VST50F maxillofacial silicone by using yttrium oxide (Y2O3) nanoparticles (NPs) to resist aging and mechanical deterioration. Materials and Method: Y2O3 NPs (30–45nm) were loaded into VST50F maxillofacial silicone in two weight percentages (1 and 1.5 wt%), which were predetermined in a pilot study as the best rates for improving tear strength with minimum increase in hardness values. A total of 120 specimens were prepared and divided into the control and experimental groups (with 1 and 1.5 wt% Y2O3 addition). Each group included 40 specimens, 10 specimens for each paramet
... Show More
(4)
(4)
(1)
PMMA (Poly methyl methacrylate) is considered one of the most commonly used materials in denture base fabrication due to its ideal properties. Although, a major problem with this resin is the frequent fractures due to heavy chewing forces which lead to early crack and fracture in clinical use. The addition of nanoparticles as filler performed in this study to enhance its selected mechanical properties. The Nano-additive effect investigated in normal circumstances and under a different temperature during water exposure. First, tests applied on the prepared samples at room temperature and then after exposure to water bath at (20, 40, 60) C° respectively. SEM, PSD, EDX were utilized for samples evaluation in this study. Flexural
... Show More
(16)
(10)
In this research thin films from SnO2 semiconductor have been prepared by using chemical pyrolysis spray method from solution SnCl2.2H2O at 0.125M concentration on glass at substrate temperature (723K ).Annealing was preformed for prepared thin film at (823K) temperature. The structural and sensing properties of SnO2 thin films for CO2 gas was studied before and after annealing ,as well as we studied the effect temperature annealing on grain size for prepared thin films .
(1)
An experimental program was conducted to determine the residual of composite Steel Beams-Reinforced Concrete (SB-RC) deck floors fabricated from a rolled steel beam topped with a reinforced concrete slab, exposed to high temperatures (fire flame) of 300, 500, and 700ºC for 1 hour, and then allowed to cool down by leaving them in the lab condition to return to the ambient temperature. The burning results showed that, by exposing them to a fire flame of up to 300ºC, no serious permanent deflection occurred. It was also noticed that the specimen recovered 93% of 19.2 mm of the deflection caused by burning. The recovered deflection of burned composite SB-RC deck floor at 500ºC was 40% of 77.9 mm of the deflection caused by burning with a res
... Show More