In this work, Titanium oxide thin films doped with different concentration of CuO (0,5,10, 15,20) %wt were prepared by pulse laser deposition(PLD) technique on glass substrates at room temperature with constant deposition parameter such as : pulse (Nd:YAG), laser with λ=1064 nm, constant energy 800 mJ , repetition rate 6 Hz and No. of pulse (500). The structure , optical and electrical properties were studied . The results of X-ray diffraction( XRD) confirmed that the film grown by this technique have good crystalline tetragonal mixed anatase and rutile phase structure, The preferred orientation was along (110) direction for Rutile phase. The optical properties of the films were studied by UV-VIS spectrum in the range of (360-1100) nm. The optical transmission results show that the maximum transmission over than ~ 48% for pure TiO 2 films and decreases to ~ 30% with increasing the CuO content to 20%wt .The optical energy for pure TiO 2 film was about 3.212eV and decreases to 3.13eVwith increasing of concentration. The results of PL emission at RT shows that there are two peaks positioned around 386 nm and 396 nm for predominated peak and795 nm and 810 for the small peaks. DC measurements show that as the increasing of film concentration lead to increase the conductivity , while the values of activation energy (E a1 ,E a2 ) decrease. Hall effect measurements show that all films have n- type charge carriers and the carriers concentration increases while the mobility decreases with increasing the CuO content.
(2)
(3)
Magnesium Phthalocyanine (MgPc) was deposited on a glass substrate by pulsed laser deposition (PLD) using Q-Switching Nd:YAG laser with wavelength 1064 nm, repetition rate 6 Hz, at room temperature (300K) and different annealing temperatures (373, 473, and 573)K under vacuum condition of 10-3 torr. All films were annealed for one hour to attain crystallinity. X-ray diffraction (XRD) of MgPc powder indicated that MgPc crystallizes in polycrystalline with a monoclinic structure. While comparing the MgPc films, it was observed that the intensity of the characteristic peak increases with temperature, and the crystallization exhibited a monoclinic structure typical of the β-form. The Miller indices, hkl, values for each diffraction peak
... Show More
(1)
A new Schiff bases ligand 4- ((2-hyolroxy phenylimino) methyl) -2, 6-dimethoxyphenol derived from condensation of 2- amino phenol with 4-hydroxy -3, 5-dimethoxy benzaldehyde have been synthesized and characterized by spectroscopy, spectra, Mass spectrum and elemental microanalysis (C.H.N). Metal Complexes with ions have been also synthesized and characterized spectroscopic methods spectroscopy, flame atomic absorption, molar conductivity measurements and magnetic susceptibility. These studies indicate that the moler ratio for the complexes. The complexes showed characteristics octahedral geometry with the (O,N) ligand coordinated in bidentate mode while with showed square planer. The enzyme activity of the ligand and i
... Show More
(21)
(21)
This study was conducted to determine the ability of water treatment system (Vortisand) to reduce some chemical and physical properties for tigris river raw water, It consisted of turbidity, electrical conductivity, pH, total hardness, calcium Hardness as well as temperature in order to determine the unit`s efficiency for reducing their concentration as compared to those in the water produced by some classical potable water projects (Dora and Wathba) in Baghdad. Samples were collected during the cold months (December 2016 and January 2017) and during the hot months (May and June 2017). The results showed that this system has the ability to reduce some properties such as turbidity, the values were 215NTU in raw water and decreased to NTU
... Show MoreThe change in the optical band gap and optical activation energy have been investigated for pure Poly (vinyl alcohol)and Poly (vinyl alcohol) doped with Aluminum sulphate to proper films from their optical absorption spectra. The absorption spectra were measured in the wave range from (200-700) nm at temperature range (25-140) 0C. The optical band gap (Eg) for allowed direct transition decrease with increase the concentration of Aluminum sulphate. The optical activation energy for allowed direct transition band gap was evaluated using Urbach- edges method. It was found that ?E increases with increasing the concentration of Al2 (SO4)3 and decreases when temperature increases.
Polymer electrolyte films composed of PVP and PVP/glycerin with varying concentrations of CuCl2 (10, 20, and 30 wt.%) were synthesized using the solution casting method. The synthesized electrolyte films were characterized using FTIR, XRD, UV-Vis, DSC, and TGA techniques. FTIR spectroscopy revealed an O-H stretching vibration of PVP around 3300 cm(-1), which experienced broadening and a reduction in intensity upon the introduction of glycerin and CuCl2. XRD analysis displayed a characteristic peak at 2 theta similar to 20 degrees, with the peak shifting towards higher angles and a slight decrease in intensity as the CuCl2 concentration increased, indicating a disruption of the crystalline structure of the host matrix. UV-Vis analysis reveal
... Show More
(9)
(11)
This study focuses on producing wood-plastic composites using unsaturated polyester resin reinforced with Pistacia vera shell particles and wood industry waste powder. Composites with reinforcement ratios of 0%, 20%, 30%, and 40% were prepared and tested for thermal conductivity, impact strength, hardness, and compressive strength. The results revealed that thermal conductivity increases with reinforcement, while maintaining good thermal insulation, reaching a peak value of 0.633453 W/m·K. Hardness decreased with increased reinforcement, reaching a minimum nominal hardness value of 0.9479. Meanwhile, impact strength and compressive strength improved, with peak values of 14.103 k/m² and 57.3864568 MPa, respectively. The main aim is to manu
... Show MoreElectronic properties including (bond length, energy gap, HOMO, LUMO and density of state) as well as spectroscopic properties such like infrared, Raman scattering, force constant, reduced mass and longitu- dinal optical mode as a function of frequency are based on size and concentration of the molecular and nanostructures of aluminum nitride ALN, boron nitride BN and AlxB7-XN7 as nanotubes has calculated using Ab –initio approximation method dependent on density functional theory and generalized gradient approximation. The geometrical structure are calculated by using Gauss view 05 as a complementary program. Shows the energy gap of ALN, BN and AlxB7-XN7 as a function of the total number of atoms , start from smallest molecule to reached