The current study suggested a thermal treatment as a necessary proactive step in improving the adsorption capacity of bio-waste for contaminants removal in wastewater. This approach was based on the experimental and histological investigation of biowaste pods shell. This investigation showed that these shells compose of parenchyma cells that store secondary metabolites compounds produced from cells were exhibited in present study. The results also reported that these compounds are extracted directly from the cells as soon as they are exposed to an aqueous solution, hampering their use as an adsorbent material. The increase in the weight of bio-waste adsorbent at unit liquid volume increases the production of secondary metabolites compounds under normal conditions. While thermal conditions accelerate the exit of these compounds from their storage places. After suggested thermal processing, the bio-waste was examined for azo dye removal under different operational conditions (adsorbent weight (1,0.1 g), contact time (24 and 48 hr), and temperature (30, 40, 50,and 60°C). In general, the experimental data showed a good improvement in adsorption potential. The results presented clearly that the increase in temperature has a positive effect on the performance of pollutant removal. The maximum adsorption capacity was 0.035833 mol/g at a temperature of 40°C, and 0.036417 mol/g at a temperature of 50°C. This behaviour may be counterproductive with high temperatures as a result of the release of more secondary metabolites compounds. For other operating conditions, increasing the concentration of the pollutant also improves the efficiency of the process, while this efficiency decreases with the increasing weight of the adsorbent material. For example, the removal capacity was (0.000275, 0.00675 mol/g) with 1 and 0.1 g of the adsorbent weight, respectively. Finally, the present study concluded that the adoption of thermal pre-treatment technology for bio-mass waste is a necessary step in improving the adsorption processes.
The objectives of this paper was the development of a novel ligand, L, which was achieved in two stages: ligand is synthesised by reducing the result of the reaction between cyclohexane-1,2-diamine and 4-hydroxy-3,5-dimethoxycy clohexane-1-carbaldehyde, followed by the production of the 4,4’-((1E,1’E)-(1,2 phenylenebis(azanylylidene))bis(methanylylidene))bis(2,6-dimethoxyphenol) precursor (P). While studying corrosion inhibition (copper alloy) in acid solution by weight loss, compounds were characterised using 1H, 13CNMR (for ligand (L) and (P)), FT-IR and UV spectra, melting point, molar conductivity, %C, %H and %N, %M, and magnetic susceptibility. The complex’s octahedral structure is inferred from the bidentate coordination
... Show More
(5)
(5)
(4)
Objectives The strategies of tissue-engineering led to the development of living cell-based therapies to repair lost or damaged tissues, including periodontal ligament and to construct biohybrid implant. This work aimed to isolate human periodontal ligament stem cells (hPDLSCs) and implant them on fabricated polycaprolactone (PCL) for the regeneration of natural periodontal ligament (PDL) tissues. Methods hPDLSCs were harvested from extracted human premolars, cultured, and expanded to obtain PDL cells. A PDL-specific marker (periostin) was detected using an immunofluorescent assay. Electrospinning was applied to fabricate PCL at three concentrations (13%, 16%, and 20% weight/volume) in two forms, which were examined through field emission
... Show More
(27)
(8)
In this work, chemical spray pyrolysis deposition (CSP) technique was used to prepare a mixed In2O3-CdO thin films with different CdO content (10, 30 and 50)%volume ratio on glass substrates at 150 ᵒC substrate temperature. The surface morphology and structural properties were measured to find the optimum conditions to improve thin films properties for using as photo detector. Current –Time, the sensitivity and response speed vary for each mixture. Samples with 10% vol. CdO content has square pulse response with average rise time nearly 1s and fall time 1s.
This research deals with increasing the hardening and insulating the petroleum pipes against the conditions and erosion of different environments. So, basic material of epoxy has been mixed with Ceramic Nano Zirconia reinforcement material 35 nm with the percentages (0,1,2,3,4,5) %, whereas the paint basis of broken petroleum pipes was used to paint on it, then it was cut into dimensions (2 cm. × 2 cm.) and 0.3cm high. After the paint and percentages are completed, the samples were immersed into the paint. Then, the micro-hardness was checked according to Vickers method and thermal inspection of paint, which contained (Thermal conduction, thermal flux and Thermal diffusivity), the density of the painted samples was calculate
... Show More
(15)
(14)
(1)
(10)
Six mixed ligand complexes were prepared from malonic acid (MA), nicotinic acid (NA), and 2-aminopyridine (AP) in a (1:1:1:1) molar ratio (M: MA: NA: AP.), using aqueous ethanol as a reaction medium. The prepared compounds were analyzed by flame atomic absorption, (C.H.N.) analysis, and FTIR, UV-Vis, and mass spectroscopy, as well as conductivity measurement and magnetic susceptibility studies. Based on the combined analytical data, the prepared complexes were proposed to adopt an octahedral geometry. A urinary tract infection (UTI) is a bacterial infection that affects any part of the urinary tract. The emergence of antibiotic-resistant bacteria and fungi has led to poor patient outcomes and limited treatment options, prompting int
... Show More