This work describes the weathering effects (UV-Irradiation, and Rain) on the thermal conductivity of PS, PMMA, PS/PMMA blend for packaging application. The samples were prepared by cast method at different ratios (10, 30, 50, 70, and 90 %wt). It was seen that the thermal conductivity of PMMA (0.145 W/m.K), and for PS(0.095 W/m.K), which increases by PS ratio increase up to 50% PS/PMMA blend then decreased that was attributed to increase in miscibility of the blend involved. By UV-weathering, it was seen that thermal conductivity for PMMA increased with UV-weathering up to (30hr) then decreased, that was attributed to rigidity and defect formation, respectively. For 30%PS/PMMA, there results showed unsystematic decrease in thermal conduct

Eighty five samples were taken from patients suffering from pneumonia. Seventy-eight isolates were diagnosed as following: Staphylococcus aureus (23), klebsiella pneumoniae (29), Streptococcus pneumoniae (15), Serratia sp. (4), Haemophilus influenzae (4) and Pseudomonas aeruginosa (3). The clinical isolates were tested for antibiotics sensitivity. They appeared highly resistance to penicillin G and Ampicillin at percentage 89.7 and 84.6% respectly while the results showed highly sensitivity to streptomycin at percentege of (12.8%). To study the antibacterial activity of Alium sativum, Eucalyptus microtheca leaves and Cydonia oblonga seeds extracts, five multi resistant strains were used by using agar well diffusion and disk methods at c

In this research, damping properties for composite materials were evaluated using logarithmic decrement method to study the effect of reinforcements on the damping ratio of the epoxy matrix. Three stages of composites were prepared in this research. The first stage included preparing binary blends of epoxy (EP) and different weight percentages of polysulfide rubber (PSR) (0%, 2.5%, 5%, 7.5% and 10%). It was found that the weight percentage 5% of polysulfide was the best percentage, which gives the best mechanical properties for the blend matrix. The advantage of this blend matrix is that; it mediates between the brittle properties of epoxy and the flexible properties of a blend matrix with the highest percentage of PSR. The second stage

A new, accurate, precise and economic two spectrophotometric methods for determination of Paracetamol (Par), Ibuprofen (Ibu), and Caffeine (Caf) were suggested. Those methods were the first and second ratio derivative spectrum using a double devisor. Par, Ibu, and Caf showed many useful peaks for their quantified determination. The validity of all analysis modes for determination of the three compounds, peak to baseline, peak area and peak to peak were according to ICH. The linearity of two methods was between 5 µg/ml as a lower concentration and 50 µg/ml as the highest concentration for three compounds. Recovery percentage was around 100% and relative standard deviation was less than 2.6%. The methods were applied successfully in the

This study present, the density of alum chrom in water and in aqueous solution of poly (ethylene glycol) (1500) at different temperature (288.15, 293.15, 298.15) k. Experimental values of density was used to calculate the apparent molar volume (Vθ), limiting apparent molar volume Vθ˚, experimental slope (Sv) and the partial molar volume at infinite dilution of transfer of solute Δνθ˚. These results have been interpreted the molecular interaction in term of ion- solvent, ion– ion interaction. The structure making /breaking capacities have been inferred from the sign of the second derivative of limiting partial molar volume with respect temperature at constant pressure. Alum has been formed to act as structure breaker in water and aq

Transactions on Engineering and Sciences

Excess molar volumes of five ternary mixtures of 2- methoxy ethanol(1) +butyl acetate(2)+benzene(3), +toluene(3), +chlorobenzene(3), +bromobenzene(3), and +nitrobenzene(3) have been measured at 303.15K. The excess molar volume exhibited positive deviation over the entire range of composition in the systems 2-methoxy ethanol(1)+ butyl acetate(2)+ benzene(3),+toluene(3) and sigmoid behavior in the case of the remaining systems. Flory's statistical theory have been extended to predict the excess molar volumes of the five ternary mixtures at 303.15 k over a wide range of composition . An excellent agreement has been found between the experimental and theoretical excess molar volumes , both in magnitude and sign .

In this paper, chip and powder copper are used as reinforcing phase in polyester matrix to form composites. Mechanical properties such as flexural strength and impact test of polymer reinforcement copper (powder and chip) were done, the maximum flexural strength for the polymer reinforcement with copper (powder and chip) are (85.13 Mpa) and (50.08 Mpa) respectively was obtained, while the maximum observation energy of the impact test for the polymer reinforcement with copper (powder and chip) are (0.85 J) and (0.4 J) respectively