AA3003-H14 aluminum alloy plates were welded by friction stir welding and TIG welding.
Fatigue properties of the welded joints were evaluated based on the superior tensile properties for
FSW at 1500 rpm rotational speed and 80 mm/min welding speed. However, there is not much
information available on effect of welding parameters with evolution of fatigue life of friction stir
welds. The present study experimentally analyzed fatigue properties for base, FSW, and TIG welds
of AA 3003-H14 aluminum alloy. Fatigue properties of FSW joints were slightly lower than the
base metal and higher than TIG welding.

In this work, some mechanical properties of the polymer coating were improved by preparing a hybrid system containing Graphene (GR) of different weight percentages (0.25, 0.5, 1, and 2wt%) with 5wt% carbon fibres (CF) and added to a polymer coating by using casting method. The properties were improved as GR was added with further improvement on adding 5wt% of CF. The impact strength of acrylic polymer with GR increases with increasing weight ratio‏‏ of GR; maximum value was obtained when the polymer coating was incorporated with 1wt% GR and 5wt% CF. The impact strength of acrylic polymer with GR and GR/CF composites incorporated with GR at 1wt% and CF at 5wt%. Hardness increase with increasing weight ratio of Gr and a significant imp

Nanostructure of chromium oxide (Cr₂O₃-NPs) with rhombohedral structure were successfully prepared by spray pyrolysis technique using Aqueous solution of Chromium (III) chloride CrCl₃ as solution. The films were deposited on glass substrates heated to 450°C using X-ray diffraction (XRD) shows the nature of polycrystalline samples. The calculated lattice constant value for the grown Cr₂O₃ nanostructures is a = b = 4.959 Å & c = 13.594 Å and the average crystallize size (46.3-55.6) nm calculated from diffraction peaks, Spectral analysis revealed FTIR peak characteristic vibrations of Cr-O Extended and Two sharp peaks present at 630 and 578 cm-1 attributed to Cr-O “stretching

This work deals with thermal cracking of heavy vacuum gas oil which produced from the top of vacuum distillation unit at Al- DURA refinery, by continuous process. An experimental laboratory plant scale was constructed in laboratories of chemical engineering department, Al-Nahrain University and Baghdad University. The thermal cracking process was carried out at temperature ranges between 460-560^oC and atmospheric pressure with liquid hourly space velocity (LHSV) equal to 15hr^-1.The liquid product from thermal cracking unit was distilled by atmospheric distillation device according to ASTM D-86 in order to achieve two fractions, below 220^oC as a gasoline fraction and above 220^oC as light cycle o

Toxic substances have been released into water supplies in recent decades because of fast industrialization and population growth. Fenton electrochemical process has been addressed to treat wastewater which is very popular because of its high efficiency and straightforward design. One of the advanced oxidation processes (AOPs) is electro-Fenton (EF) process, and electrode material significantly affects its performance. Nickel foam was chosen as the source of electro-generated hydrogen peroxide (H₂O₂) due to its good characteristics. In the present study, the main goals were to explore the effects of operation parameters (FeSO₄ concentration, current density, and electrolysis time) on the catalytic perform

This work includs synthesis of several Schiff bases by condensation of 6- methoxy – 2- amino benzothiazole with some aldehydes and ketones (2- hydroxyl benzaldehyde, 4- hydroxyl benzaldehyde, 4- N,N –dimethy amino acetophenone, benzophenone) to abtain schiff bases (1-5). These schiff bases were found to react with phthalate anhydride to give oxazepine derivatives (6-10) that were reacted with primary aromatic amines to give Diazepine derivatives (11-15). Besides, we prepared new tetrazole derivatives (16-20) from the reaction of the prepared Schiff bases with sodium azide in the prepared compounds that were characterized by physical properties, FT-IR and some of the 1H-NMR and 13C –NMR spectroscopy.

Neuro-ophthalmic disorders are often documented individually for each illness, with little data available on their overall incidence and pattern. The overall incidence of neuro-ophthalmic illnesses in Iraq is still not recorded. This study aimed to evaluate the clinical, demographic, and etiological features of patients seeking consultation at an Iraqi neuro-ophthalmology clinic. A prospective cross-sectional observational research was conducted at the Janna Ophthalmic Center in Baghdad, Iraq. The center serves a diverse patient population from various governorates. All newly diagnosed patients with neuro-ophthalmic disorders who visited the neuro-ophthalmological clinic, regardless of gender or age group, were included. The neuro-ophthalmo

Bubbled slabs can be exposed to damage or deterioration during its life. Therefore, the solution for strengthening must be provided. For the simulation of this case, the analysis of finite elements was carried out using ABAQUS 2017 software on six simply supported specimens, during which five are voided with 88 bubbles, and the other is solid. The slab specimens with symmetric boundary conditions were of dimensions 3200/570/150 mm. The solid slab and one bubbled slab are deemed references. Each of the other slabs was exposed to; (1) service charge, then unloaded (2) external prestressing and (3) loading to collapse under two line load. The external strengthening was applied using prestressed wire with four approaches, wh

Portland Cement is manufactured by adding 3% gypsum to clinker which is produced by grinding, pulverizing, mixing, and then burning a raw mix of silica, and calcium carbonate. Limestone is the main source of carbonates, while clay collected from arable land is the main source of silica. The marl in the Euphrates Formation was studied as an alternative to arable lands. Nine boreholes drilled and penetrated the marl layer in selected locations at the Kufa cement quarry. Forty-one samples of marl from boreholes and four samples of limestone from the closed area were collected. The chemical content of the major oxides and the hardness of the marl layer was very encouraging as a raw material for Portland Cement as they are SiO2 (17.60),