Nanocrystalline TiO 2 and CuO doped TiO 2 thin films were successfully deposited on suitably cleaned glass substrate at constant room temperature and different concentrations of CuO (0.05,0.1,0.15,0.2) wt% using pulse laser deposition(PLD) technique at a constant deposition parameter such as : (pulse Nd:YAG laser with λ=1064 nm, constant energy 800 mJ, with repetition rate 6 Hz and No. of pulse (500). The films were annealed at different annealing temperatures 423K and 523 K. The effect of annealing on the morphological and electrical properties was studied. Surface morphology of the thin films has been studied by using atomic force microscopes which showed that the films have good crystalline and homogeneous surface. The Root Mean Square value of thin films surface roughness is increased with the increase of annealing temperature. Also, the grain size increases with the increasing of CuO concentration and annealing. The temperatures dependence of the electrical conductivity and the activation energy at temperature ranging from (293-473) K of the as-deposited and films annealed at different annealing temperatures have been studied. The results show that as the film concentration of and conductivity increases, while the activation energy (Ea 1 , E a2 ) decreases. Both, the annealing and composition effects on Hall constant, charge carrier concentration, Hall mobility were investigated. Hall Effect measurements show that all films have n- type charge carriers, and the concentration and annealing increase carriers concentration while the mobility decreases.
Ceramic coating compose from a ceramic mixture (MgO, Al2O3) and metall (Al-Ni) were produced by Thermal Spray Technique. The mixed ratio of used materials Al:Ni (50%) and 40% of Al2O3 and 10% MgO. This mixture was spray on a stainless steel substrate of type (316 L) by using thermal spray with flame method and at spraying distances (8, 12, 16 and 20) cm, then the prepared films were treated by laser and thermal treatment. After that performing a hardness and adhesion tests were eximined. The present study shows that the best value of the thermal treatment is 1000 ℃ for 30 mint; the optimum spray distance is 12 cm and most suitable laser is 500 mJ where the microscopic and mechanical character
... Show More
(1)
Ferrite with general formula Ni1-x Cox Fe2O4(where x=0.0.1,0.3,0.5,0.7, and 0.9), were prepared by standard ceramic technique. The main cubic spinel structure phase for all samples was confirmed by x-ray diffraction patterns. The lattice parameter results were (8.256-8.299 °A). Generally, x -ray density increased with the addition of Cobalt and showed value between (5.452-5.538gm/cm3). Atomic Force Microscopy (AFM) showed that the average grain size and surface roughness was decreasing with the increasing cobalt concentration. Scanning Electron Microscopy images show that grains had an irregular distribution and irregular shape. The A.C conductivity was found to increase with the frequency and the addition of Cobal
... Show More
(1)
(12)
(11)
MJ Abbas, AK Hussein, Journal of Physical Education, 2019
(3)
(4)
(4)
Thin films of (CdO)x (CuO)1-x (where x = 0.0, 0.2, 0.3, 0.4 and 0.5) were prepared by the pulsed laser deposition. The CuO addition caused an increase in diffraction peaks intensity at (111) and a decrease in diffraction peaks intensity at (200). As CuO content increases, the band gap increases to a maximum of 3.51 eV, maximum resistivity of 8.251x 104 Ω.cm with mobility of 199.5 cm2 / V.s, when x= 0.5. The results show that the conductivity is ntype when x value was changed in the range (0 to 0.4) but further addition of CuO converted the samples to p-type.
(9)
(10)
This study included the estimation of growth rate, viability and morphological changes in different culture media (NNN, P-Y, RPMI- 1640, and Panmed). Promastigotes cultured in RPMI-1640 showed maximal growth rate after (2, 4, 6) days of cultivation (27.26 ± 0.05), (172.20 ± 0.1) and (343.81 ± 1.48) million parasites / ml for each day respectively, while P-Y media gave the highest mean of growth rat after (8 and 10) days of cultivation (307.16 ± 1.67) and (303.5 ± 4.96) million parasites / ml for each day respectively. P-Y medium showed the maximal percentage of viability after (2, 4, 6, 8, and 10) days of cultivation (99.76 ± 0.5) %, (98.30 ± 0.17) %, (96.1 ± 0.1) %, (92.5 ± 0.52) % and (87.26 ± 0.05) % for each day respectively.
... Show MoreThe objective of this study was shed light for cultivation and maintenance of Trichomonas vaginalis parasite growth after isolated it by vaginal swaps from females suffering vaginitis and abnormal vaginal discharges in these media CPLM and TAB media to detect growth curve, morphological changes and viability of parasite in the two culture media, together with effect of sheep and bovine serum on the growth of it. The results of this studies were showed there was abtaine differences between the two types of media , The maximum growth of parasite was in TAB medium after 72 hours incubation with use of bovine serum, while such growth was maximized after 144 hours incubation with the use of sheep serum. In CPLM medium, a maximum gro
... Show More