Background: to evaluate the effect of different dentifrices on the surface roughness of two composite resins (nanofilled-based and nanoceramic – based composite resins). Materials and methods: Forty specimens (diameter 12 mm and height of 2mm) prepared from different composite resin materials: Z350 (nanofilled composite, and Ceram-X (nanoceramic) .they were subjected to brushing simulation equivalent to the period of 1 year. The groups assessed were a control group brushed with distilled water (G1), Opalescence whitening toothpasteR (G2), Colgate sensitive pro-relief (G3) and Biomed Charcoal Toothpaste (G4). The initial and final roughness of each group was tested by surface roughness tester. The results were statistically analyzed using

A successful synthesis of mesoporous Santa Barbara amorphous (SBA-15) with nanoparticle size was attempted using prepared sodium silicate from Iraqi high silica sand. EO20PO70EO20 copolymer was used as a template at highly acidic conditions (pH < 2). The effect of crystallization temperature of (100, 110, 120, and 130 0C), and crystallization time of (24, 48, 72, and 120 h) on surface properties was studied. The experiments were characterized using XRD, FTIR, AFM, BET, and FESEM. The XRD and FTIR tests represent amorphous SBA-15 without any impurities. Decreasing average particle size distribution increased the surface area, and decreased the porosity (pore volume, and pore size) in all experiments. The texture properties were su

Let be a ring. Given two positive integers and , an module is said to be -presented, if there is an exact sequence of -modules with is -generated. A submodule of a right -module is said to be -pure in , if for every -Presented left -module the canonical map is a monomorphism. An -module has the -pure intersection property if the intersection of any two -pure submodules is again -pure. In this paper we give some characterizations, theorems and properties of modules with the -pure intersection property.

Let be a ring. Given two positive integers and , an module is said to be -presented, if there is an exact sequence of -modules with is -generated. A submodule of a right -module is said to be -pure in , if for every -Presented left -module the canonical map is a monomorphism. An -module has the -pure intersection property if the intersection of any two -pure submodules is again -pure. In this paper we give some characterizations, theorems and properties of modules with the -pure intersection property.

Zirconia ceramic restoration (ZCR) has a higher fracture incidence rate than metal ceramic restoration. Different surface treatments were used to improve fracture performance of ZCR such as grit blasting (GB) by aluminium oxide powder. This type of surface treatment generate residual stresses on veneering ceramic causing crack initiation and ending with a fracture. In order to overcome the stress generated by GB, zirconia surface coating is used as a surface treatment to improve fracture resistance and to accommodate stresses along the ZCR layers. Fifty zirconia ceramic crowns were fabricated and divided according to the type of surface treatment into three groups; the first group is (ZG), involving 20 cores were coated with a mixture of pa

This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3

Objective(s): The aim of this study is to compare the impact strength of a heat cured denture-base acrylic resin
reinforced with metal wire and glass fibers.

Methodology: Forty five specimens were prepared from pink heat cure acrylic resin. Specimens were grouped into;
group-I (control group) which consists of 15 specimens with no reinforcement, group-II which consists of 15 specimens
reinforced with metal wire, and group-III consists of 15 specimens reinforced with glass fibers. Specimens were tested
by using charpy impact machine.

Results: The result showed that there was a highly significant difference in impact strength value among the testing
groups at (P < 0.001).

Conclusion: The impact str

Background: Thermocycling simulates the temperature dynamics in the oral environment. This in vitro study done to measure and compare the effect of thermocycling on the shear bond strength of stainless steel and sapphire brackets bonded to human enamel teeth using light cured orthodontic adhesive and debonded at various time, and to measure adhesive remnant index after debonding. Materials and Methods: one-hundred-twenty extracted upper first premolars for orthodontic reason were used in this study; depending on weather thermocycled or not, the sample was divided into two main groups, then within each group 30 teeth were used for stainless-steel brackets (Bionic®) and for sapphire brackets (Pure®). Both groups were subdivided into three

Mesoporous SBA-15 with nono particle size distribution, different texture properties, and morphologies have been synthesized by controlling the hydrophilic-hydrophobic character during preparation, i.e., the solubility of micelles of pluronic P123 by controlling the charge of PEO hydrophilic-inorganic silica zone using different charge surfactants CTAB (cationic), F68 (nonionic), and SDBS (anionic). Sodium silicate was used as a silica source. Eo20Po70Eo20 co-polymer was used as a template at highly acidic conditions (pH<2). The experiments were characterized using XRD, FTIR, AFM, BET, and FESEM. The XRD and FTIR tests indicated that the SBA-15 is amorphous and free from impurities. The degree of particle dispersion is sequenced

this work, a simple method was used to prepare the MnO2 nanoparticles. These nanoparticles then were characterized by several techniques, such as X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy (SEM) and atomic force microscope (AFM). The results showed that the diffraction peak of MnO2 nanoparticles was similar to that of standard data. The images of AFM and SEM indicated that the MnO2 nanorods were growing from the MnO2 nano spherical shape. PVA-pentaerythritol/MnO2 nanocomposite films were fabricated by evaporating casting method. The dielectric constant and loss tangent of P-Ery/MnO2 films were measured between 10 kHz and 1 MHz using LCR. As the content of MnO2 increased, the dielectric constant