One of the most important phenomenon that occurs in sheet metal forming processes is the spring-back, which causes several geometrical alterations in the parts. The accurate prediction of springback after bending unloading is the key to the tool design, operation control, and precision estimate concerning the part geometry. This study investigated experimentally the effect of pretension in three rolling direction (0, 90, 45 degree) on the springback behavior of the yellow brass, sheet under V shape bending die. The pre-tension ranges from five different levels starting of 11% to 55% from the total strain in each rolling direction by regular increase of 11 %, then bent on a V-die 90 degree for the springback estimate. From experiment the

Thermal conductivity measurement was done for specimens of Polystyrene/ titanium dioxide, Polycarbonate/ titanium dioxide and Polymethylmetha acrylate/ titanium dioxide composites for weight ratio of 1.9/ 0.1 and 1.8/ 0.2 wt% for different thickness of the samples. The experimental results show that the thermal conductivity is increased with the increasing of thickness of layers and with the weight ratio of TiO2

This experiment was carried out in one of the fields (A) affiliated to the College of Agricultural Engineering Sciences / University of Baghdad, for the spring season 2021, On hybrid tomato plants (Mayai Mayai) to test flower viability, using two factors, the first was three levels of irrigation interval (2, 4, 6) days, and the second factor three concentrations of compound Nano fertilizer with concentrations (0, 1.5, 2.5) gm liter-1, so that the number of treatments is 9 treatments and three replications, the number of experimental units is 27 experimental units distributed randomly according to the random drawing method to ensure reducing experimental error and obtaining the most accurate results. A factorial experiment 3 x 3 x 3 was carr

Objectives: The study aims to evaluate patients’ performance toward insulin injection after training program to
identify the variation in skill of patients in insulin injection technique with regard to some variable (i.e.
educational level and duration of insulin injection.
Methodology: A quasi experimental study has been conducted on diabetic patients.
An observational checklist had been prepared which consisted of 4 main areas with 37 sub-items, which are
syringe preparation for injection, insulin drawing; skin preparation for injection and insulin injection. Each of the
sub-items has 2 options yes or no. One score for positive answer and zero for no.
The sample of the study consisted of (n =30) males and females

The present study reports the effect of temperature and liquid hourly space velocity (LHSV) on the cumene cracking reaction rate and selectivity by using a laboratory continuous flow unit with fixed bed reactor operating at atmospheric pressure. The prepared HX zeolite was made from Iraqi kaolin with good crystallinity .The activity and selectivity of prepared HX-zeolite was compared with standard HY zeolite and HX zeolite catalysts in the temperature range of 673-823K and LHSV of 0.7-2.5 h-1 . It was found that the cumene conversion increases with increasing temperature and decreasing LHSV at 823K and LHSV of 0.7 h-1 the conversions 65.32, 42.88 and 59.42 mol% for HY, HX and prepared HX catalysts respectively and at LHSV of 2.5 h-1 and th

Thin films of ZnSxSe1-x with different sulfide content(x)
(0, 0.02, 0.04, 0.06, 0.8, and 0.1), thickness (t) (0.3, 0.5, and 0.7 μm) and annealing temperature (Ta) (R.T 373 and 423K) were fabricated by thermal evaporating under vacuum of 10-5 Toor on glass substrate. The results show that the increasing of sulfide content (x)and annealing temperature lead to decrease the d.c conductivity σDC of and concentration of charge carriers (nH) but increases the activation energy (Ea1,Ea2), while the increasing of t increases σDC and nH but decrease (Ea1,Ea2). The results were explained in different terms

Thin films of the blended solution of (NiPc/C60) on glass substrates were prepared by spin-coated method for three different ratios (100/1, 100/10 and 100/100). The effects of annealing temperature and C60 concentration on the optical properties of the samples were studied using the UV-Vis absorption spectroscopy and FTIR spectra. The optical absorption spectrum consists of two main bands, Q and B band, with maxima at about (602-632) nm and (700-730) nm for Q1 and Q2 respectively, and (340-375) nm for B band. The optical energy gap were determined from optical absorption spectra, The variation of optical energy gap with annealing temperature was nonsystematic and this may be due to the improvement in crystal structure for thin films. Whi

Objective: To evaluate the changes in the surface quality of irreversible hydrocolloid impression material
hydrogum following disinfection with 0.525% sodium hypochlorite, 0.2% Chlorehexidine Gluconate, and 4%
Povidone Iodine.
Methodology: Forty specimens of alginate impression materials hydrogum were fabricated according to the
ISO 1563 and were divided into four groups according to the method of solution dipping: group 1: Dip in
0.525% sodium hypochlorite, group 2: Dip in 0.2% chlorhexidine gluconate, Group 3: Dip in 4% Povidone Iodine,
Group 4: No treatment with any solution (control group). Then the specimens were poured in type II stone.
Surface detail was determined using a stainless steel block in accordance w

The nonlinear optical properties for polymeric (PMMA) doping with dye Rhodmine (R3Go) has been studied .The samples are prepared by normal polymerization method with concentrations of 5x10^-5mol/l and a thickness of 272.5µm.

                         Plasma effect was studied on samples prepared before and after exposure to the Nd: YAG laser for three times 5, 10 and 15 minutes. Z-Scan technique is used to determine the nonlinear optical properties such as; refractive index (n₂) and the coefficient of nonlinear absorption (β). It was found that the nonlinear properties is change by increasi