Fire flame effect on the compressive strength of reactive powder concrete using different methods of cooling
...Show More Authors

This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &36.07) forgradual and sudden cooling respectively. This reduction was modified by adding steel fiber, the percentage of (1%) characterized the optimum response. Burning RPC that has non-zero steel fiber content up to 400 oC caused an increase in the residual compressive strength for a case of gradual cooling to be (4.37 & 6.25)% for steel fiber volume fraction of (1 & 1.5) % respectively. Sudden cooling method was improved to be the critical cooling method, the negative influence of this method was directly proportion with both burning temperature and steel fiber volume fraction.

Scopus Clarivate Crossref
Publication Date
Sun Jul 31 2016
Journal Name
International Journal Of Advanced Research
Attenuation Coefficient of Reactive Powder Concrete Using Different Energies.
...Show More Authors

View Publication
Crossref (6)
Crossref
Publication Date
Sun Jul 09 2023
Journal Name
Journal Of Engineering
Assessing the Effect of Using Porcelanite on Compressive Strength of Roller Compacted Concrete
...Show More Authors

Roller-Compacted Concrete (RCC) is a zero-slump concrete, with no forms, no reinforcing steel, no finishing and is wet enough to support compaction by vibratory rollers. Because the effectiveness of curing on properties and durability, the primary scope of this research is to study the effect of various curing methods (air curing, emulsified asphalt(flan coat) curing, 7 days water curing and permanent water curing) and different porcelanite (local material used as an Internal Curing agent) replacement percentages (volumetric replacement) of fine aggregate on some properties of RCC and to explore the possibility of introducing more practical RCC for road pavement with minimum requirement of curing. Cubes specimens were sawed from the slab

... Show More
View Publication Preview PDF
Crossref (4)
Crossref
Publication Date
Thu Dec 01 2022
Journal Name
Journal Of Engineering
Influence of Waste Concrete and Glass Recycled on the Strength Properties of Green Reactive Powder Concrete
...Show More Authors

These days, the world is facing a global environmental and sustainability problem due to the increasing generation of large amounts of waste through construction and demolition work, which causes a serious problem for the environment. Therefore, this research was conducted to get rid of the waste disposal problems, including old glass and concrete, which were used as recycled fine aggregates. Seven different mixtures were prepared. The first mixture was with the used sand, which is glass sand, and it was adopted as a reference mixture (ORPC), and three mixtures were prepared for each of the recycled materials (waste concrete and glass) and partially replaced by glass sand in different proportions (25, 50, and 75) %. Some

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Thu Feb 01 2018
Journal Name
Association Of Arab Universities Journal Of Engineering Sciences
Effect of High Temperature (Fire Flame) on the Behavior of Post-tensioned Concrete Beams
...Show More Authors

View Publication Preview PDF
Publication Date
Thu Oct 01 2015
Journal Name
Journal Of Engineering
The Effect of Recycled Heating and Cooling and The Effect of The Speciment Size on The Compressive Strength of Concrete Exposed To High Temperature
...Show More Authors

     In the present work effect of recycled heating and cooling on the values of concrete compressive strength due to high temperature of 4000C was studied.

    The tests show that the percent of reduction in compressive strength of the samples which exposed to a temperature of 4000C for one cycle was 32.5%, while the reduction was 52.7% for the samples which were exposed to recycled heating and cooling of ten times .      

   Moreover a study of the effect of specimen sizes on the percentages of compressive strength reduction due to high temperature

... Show More
View Publication Preview PDF
Publication Date
Sat Apr 09 2022
Journal Name
Engineering, Technology & Applied Science Research
Effect of Sustainable Glass Powder on the Properties of Reactive Powder Concrete with Polypropylene Fibers
...Show More Authors

Global warming and environmental damage have become major problems. The production of Portland cement releases large quantities of gas, which cause pollution to the atmosphere. This problem can be solved via the use of sustainable materials, such as glass powder. This study investigates the effect of partial replacement of cement with sustainable glass powder at various percentages (0, 15, 20, and 25%) by weight of cement on some mechanical properties (compressive strength, flexural strength, absorption, and dry density) of Reactive Powder Concrete (RPC) containing a percentage of Polypropylene fibers (PRPC) of 1% by weight. Furthermore, steam curing was performed for 5 hours at 90oC after hardening the sample directly. The RPC was

... Show More
View Publication
Crossref (12)
Crossref
Publication Date
Sun Dec 01 2019
Journal Name
Civil Engineering Journal
Structural Behavior of High Strength Laced Reinforced Concrete One Way Slab Exposed to Fire Flame
...Show More Authors

In this study, an experimental investigation had conducted for six high strength laced reinforced concrete one-way slabs to discover the behavior of laced structural members after being exposed to fire flame (high temperature). Self-compacted concrete (SCC) had used to achieve easy casting and high strength concrete. All the adopted specimens were identical in their compressive strength of ( , geometric layout 2000 750 150 mm and reinforcement specifics except those of lacing steel content, three ratios of laced steel reinforcement of (0.0021, 0.0040 and 0.0060) were adopted. Three specimens were fired with a steady state temperature of  for two hours duration and then after the specimens were cooled suddenly by spraying water. The

... Show More
View Publication
Crossref (4)
Crossref
Publication Date
Fri Oct 01 2021
Journal Name
Civil Engineering Journal
Steel Fiber Enhancement upon Punching Shear Strength of Concrete Flat Plates Exposed to Fire Flame
...Show More Authors

In this study, the effect of fire flame on the punching shear strength of steel fiber reinforced concrete flat plates was experimentally investigated using nine half-scale specimens with dimensions of 1500×1500 mm and a total thickness of 100 mm. The main investigated variables comprised the steel fiber volume fraction 0, 1, and 1.5% and the burning steady state temperature 500 and 600 °C. The specimens were divided into three groups, each group consists of three specimens. The specimens in the first group were tested with no fire effect to be the reference specimens, while the others of the second and third groups were tested after being exposed to fire-flame effect. The adopted characteristics of the fire test were; (one hour) b

... Show More
Crossref (3)
Crossref
Publication Date
Sat Jul 22 2023
Journal Name
Journal Of Engineering
Effect of Fire Flame (High Temperature) on the Self Compacted Concrete (SCC) One Way Slabs
...Show More Authors

Experimental work was carried out to investigate the effect of fire flame (high temperature) on specimens of one way slabs using Self Compacted Concrete (SCC). By using furnace manufactured for this purpose, twenty one reinforced concrete slab specimens were exposed to direct fire flame. All of specimens have the same dimensions. The slab specimens were cooled in two types, gradually by left them in the air and suddenly by using water. After that the specimens were tested under two point loads, to study, the effect of
different: temperature levels (300ºC, 500ºC and 700ºC), and cooling rate (gradually and sudden cooling conditions) on the concrete compressive strength, modulus of rupture, flexural strength and the behavior of reinf

... Show More
View Publication Preview PDF
Crossref (4)
Crossref
Publication Date
Fri Jul 21 2023
Journal Name
Journal Of Engineering
The Effect Of Curing Types On Compressive Strength Of High Performance Concrete
...Show More Authors

The present investigation considers the effect of curing temperatures (30, 40, and 50˚C) and curing compound method on compressive strength development of high performance concrete, and compares the results with concrete cured at standard conditions and curing temperature (21˚C). The experimental results showed that at early ages, the rate of strength development at high curing temperature is greater than at lower curing temperature, the maximum increasing percentage in compressive strength is 10.83% at 50C˚ compared with 21C˚ in 7days curing age. However, at later ages, the strength achieved at higher curing temperature has been less, and the maximum percentage of reduction has been 5.70% at curing temperature 50C˚ compared with 21

... Show More
View Publication Preview PDF