Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K

Introduction: Articaine was developed in 1969, with reported advantages which are increased potency, increased duration of its anesthetic effect and superior diffusion through bony tissue. The effectiveness of using 4% articaine infiltration for extraction of mandibular molar teeth in comparison to 2% lidocaine inferior alveolar nerve block is not settled yet. Aim: The aim of this study was to evaluate the effectiveness of using 4% articaine infiltration for extraction of mandibular molars by comparing it to the use of 2% lidocaine inferior alveolar nerve block in terms of success, the volume of local anesthetic agents and the pain experienced during the procedure. Materials and methods: A prospective randomized controlled study included

 The present study discusses one of the most relevant and required topics in the recent period during globalization, the modern Russian system of terms for the oil and gas industry as a whole acquired a complete form in the second half of the twentieth century. The period of the late XX - early XXI centuries. marked by cardinal transformations in all areas of the political, economic, social and cultural life of Russia. These changes could not but affect industrial production. Transition to a new vector of development of the Russian economy based on the development of commercial trade, on the change and improvement of the development of industrial enterprises in the context of the implementation of national projects and the introduction

Anadara granosa is a species of the class bivalve commonly found on the east coast of South Sumatra as a fishery commodity. This species has not been widely studied as a source of new bioactive compounds that have antioxidant abilities. This study aims to analyze the antioxidant ability of A. granosa against DPPH radicals and its phytochemical profile qualitatively. Samples were taken at the fishing port of Sungsang Village, South Sumatra, Indonesia. Furthermore, the samples were extracted using ethanol as a solvent and tested for antioxidants against DPPH radicals, total phenol analysis, and preliminary phytochemical test. Based on the antioxidant test results, the IC₅₀ value of the ethanolic extract of

: Porous silicon (n-PS) films can be prepared by photoelectochemical etching (PECE) Silicon chips n - types with 15 (mA /cm2), in15 minutes etching time on the fabrication nano-sized pore arrangement. By using X-ray diffraction measurement and atomic power microscopy characteristics (AFM), PS was investigated. It was also evaluated the crystallites size from (XRD) for the PS nanoscale. The atomic force microscopy confirmed the nano-metric size chemical fictionalization through the electrochemical etching that was shown on the PS surface chemical composition. The atomic power microscopy checks showed the roughness of the silicon surface. It is also notified (TiO2) preparation nano-particles that were prepared by pulse laser eradication in e

Nanofluids are proven to be efficient agents for wettability alteration in subsurface applications including enhanced oil recovery (EOR). Nanofluids can also be used for CO2-storage applications where the CO2-wet rocks can be rendered strongly water-wet, however no attention has been given to this aspect in the past. Thus in this work we presents contact angle (θ) measurements for CO2/brine/calcite system as function of pressure (0.1 MPa, 5 MPa, 10 MPa, 15 MPa, and 20 MPa), temperature (23 °C, 50 °C and 70 °C), and salinity (0, 5, 10, 15, and 20% NaCl) before and after nano-treatment to address the wettability alteration efficiency. Moreover, the effect of treatment pressure and temperature, treatment fluid concentration (SiO2 wt%) and

In this work, some mechanical properties of the polymer coating were improved by preparing a hybrid system containing Graphene (GR) of different weight percentages (0.25, 0.5, 1, and 2wt%) with 5wt% carbon fibres (CF) and added to a polymer coating by using casting method. The properties were improved as GR was added with further improvement on adding 5wt% of CF. The impact strength of acrylic polymer with GR increases with increasing weight ratio‏‏ of GR; maximum value was obtained when the polymer coating was incorporated with 1wt% GR and 5wt% CF. The impact strength of acrylic polymer with GR and GR/CF composites incorporated with GR at 1wt% and CF at 5wt%. Hardness increase with increasing weight ratio of Gr and a significant imp