The aim of this study is to understand the effect of addition carbon types on aluminum electrical conductivity which used three fillers of carbon reinforced aluminum at different weight fractions. The experimental results showed that electrical conductivity of aluminum was decreased by the addition all carbon types, also at low weight fraction of carbon black; it reached (4.53S/cm), whereas it was appeared highly increasing for each carbon fiber and synthetic graphite. At (45%) weight fraction the electrical conductivity was decreased to (4.36Scm) and (4.27Scm) for each carbon fiber and synthetic graphite, respectively. While it was reached to maximum value with carbon black. Hybrid composites were investigated also; the results exhibit tha

Citric acid is an essential ingredient for the manufacture of (12) key industrial chemicals. Citric acid use is increasing steadily with a high annual growth rate as a result of the development of ever more sophisticated applications. Citric acid is widely utilized in the food and pharmaceutical industries due to its low toxicity when compared to other acidulous. Other uses for citric acid can be found in cleaning supplies and detergents. Based on information from a review of the literature, Citric acid production substrates and methods for surface fermentation, submerged fermentation, solid-state fermentation, and international market expansion are all covered in the current review study. Finally, there is still much to learn about the

In this current work, Purpose; to clearly the fundamental idea for constructing a design and
investigation of spur gear made of composite material its comes from the combination of (high
speeds, low noise, oil-les running, light weight, high strength, and more load capability)
encountered in modern engineering applications of the gear drives, when the usual metallic gear
cannot too overwhelming these combinations.
An analyzing of stresses and deformation under static and dynamic loading for spur gear tooth
by finite element method with isoparametric eight-nodded in total of 200 brick element with 340
nods in three degree of freedom per node was selected for this analysis. This is responsible for the
catastropic fa

The novel groups of organic chromophores containing triphenylamine (TPA) (ATP-I to ATP-IV) have been constructed by structural modification of electron donors with substitution biphenyl and bipyridine rings inserting a π-linkage. Density functional theory (DFT) and time-dependent type of it (TD-DFT) have been operated to study results of donating ability of TPA and spacer on absorption, geometrical, photovoltaic, and energetic attributes of these sensitizers. Structural attributes have been revealed that incorporation of TPA, acceptor and π bridge include a perfect coplanar conformation in TPA-III. Based on frequency computations and ground-state optimization, bandgap (Eg) energy, ELUMO, EHOMO have been determined. For enlightening maximu

The efficient behavior of a low-concentrating photovoltaic-thermal system with a micro-jet channel (LCPV/T-JET) and booster mirror reflector is experimentally evaluated here. Micro-jets promote the thermal management of PV solar cells by implementing jet water as active cooling, which is still in the early stages of development. The booster mirror reflector concentrates solar irradiance into solar cells and improves the thermal, electrical, and combined efficiencies of the LCPV/T-JET system. The LCPV/T-JET system was tested under ambient weather conditions in the city of Bangi, Selangor, Malaysia, and all data was recorded between 10:00 a.m. and 4:00 p.m. Parametric studies were conducted to compare the performance of the LCPV/T-JET system

Background: To evaluate the effect of antierosive agents (10% Nano-Hydroxyapatite (NHA), 10% Casein Phophopeptide-Amorphous Calcium Phosphate (CPP-ACP), and combination of 10% NHA and 10% CPP-ACP) on loss of minerals from enamel surface of permanent teeth treated with antierosive agents when exposed to an acidic beverage and investigate the morphological changes of treated enamel surface after demineralization with cola based beverage under Scanning Electron Microscope (SEM). Materials and Methods: Sixty maxillary first premolars were randomly divided into four groups, 15 teeth for each group. Group I treated with 10% NHA, Group II treated with 10% CPP-ACP, Group III treated with 10% NHA and 10% CPP-ACP, and Group IV did not treat with any

The catalytic cracking of three feeds of extract lubricating oil, that produced as a by-product from the process of furfural extraction of lubricating oil base stock in AL-Dura refinery at different operating condition, were carried out at a fixed bed laboratory reactor. The initial boiling point for these feeds was 140 ºC for sample (1), 86 ºC for sample (2) and 80 ºC for sample (3). The catalytic cracking processes were carried out at temperature range 325-400 ºC and initially at atmospheric pressure after 30 minutes over 9.88 % HY-zeolite catalyst load. The comparison between the conversion at different operating conditions of catalytic cracking processes indicates that a high yield was obtained at 375°C, according to gasoline pr

This work deals with thermal cracking of three samples of extract lubricating oil produced as a by-product from furfural extraction process of lubricating oil base stock in AL-Dura refinery. The thermal cracking processes were carried out at a temperature range of 325-400 ºC and atmospheric pressure by batch laboratory reactor. The distillation of cracking liquid products was achieved by general ASTM distillation (ASTM D -86) for separation of gasoline fraction up to 220 ºC from light cycle oil fraction above 220 ºC. The comparison between the conversions at different operating conditions of thermal cracking processes indicates that a high conversion was obtained at 375°C, according to gasoline production. According to gasoline produ

Deep drawing process to produce square cup is very complex process due to a lot of process parameters which control on this process, therefore associated with it many of defects such as earing, wrinkling and fracture. Study of the effect of some process parameters to determine the values of these parameters which give the best result, the distributions for the thickness and depths of the cup were used to estimate the effect of the parameters on the cup numerically, in addition to experimental verification just to the conditions which give the best numerical predictions in order to reduce the time, efforts and costs for producing square cup with less defects experimentally is the aim of this study. The numerical analysis is used to study

The language that consists of only twenty-eight letters, but it is so broad that we are unable to understand it from all sides and this expansion is mainly caused by imagination, so Arab imagination, whose language goes in all directions And as it always responds to our ears, ancient critics divide imagination into holistic and partial But the language is not limited to these parts only. Do we wonder, where is the structural method of wishing, hope, questions and other methods of all this? In this paper, we try to show the importance of the method of writing in moving imagination in an interactive way, and what is related to human feelings in most, if not all, of its methods By studying the poetry of the believers in the Ahl al-Bayt, pea