The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m²/g, and pore volume 0.231 cm³/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst ty

This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3

The reuse or recycling of waste materials in different aspects of life is served the objective of sustainability and be beneficial to society. In recent years, a wide variety of waste materials were used in pavement construction. One of these materials is glass that generally produces in large quantities and crushed glass can be considered feasible alternative source of aggregate for asphalt mixture production. This study focused on examining the asphalt mixture properties of wearing course using crushed glass as fine aggregates. Fine crushed glass with various percentages by total weight retained on sieve 2.36 mm, 0.3 mm and 0.075 mm was used in the study. The results indicate that mixes containing crushed glass had lower Marshall stabilit

Objective: To assess the effect of education program on psychological and social changes of secondary school teachers with menopause.

Method: A quasi-experimental design is carried out with the application of a pre- post –test for menopause secondary school teacher's bio-psychosocial changes. Non-probability sample consists of (60 female teachers) (40) teachers from Al- Rusafa first Education Directorate secondary schools, and (20) teachers from Al- Karkh third Education Directorate secondary schools. The sample was exposed to pretest, educational program, and posttest. Data were collected through the utilization of the study instrument (the questionnaire) and application of bio-psychosocial ed

The current study shows the cytotoxicity effect of the Crassula ovata n-hexane extract on esophagus can¬cer. C. ovata is a perennial succulent plant belonging to the Crassulaceae family. In Africa, the leaves were used medicinally to cure epilepsy and diarrhoea by boiling them in milk. The hexane fraction, which is obtained through the maceration method, demonstrates the presence of many compounds that have an anticancer effect, which are ob¬tained by gas chromatography - mass spectroscopy. The phytosterol compound was isolated by a preparative thin layer chromato¬graph and was identified by liquid chromatography - mass spectroscopy. The hexane fraction was found to possess a strong anticancer effect against esophagus cancer. The

Preparation of epoxy/ TiO2 and epoxy/ Al2O3 nanocomposites is studed and investigated in this paper. The nano composites are processed by different nano fillers concentrations (0, 0.01, 0.02 ,0.03, 0.04 ,0.05 ,0.07 and 0.1 wt%). The particles sized of TiO2,Al2O3 are about 20–50 nm.Epoxy resin and nano composites containing different shape nano fillers of (TiO2:Al2O3 composites),are shear mixing with ratio 1 to 1,with different nano hybrid fillers concentrations( 0.025 ,0.0 5 ,0.15 ,0.2, and 0.25 wt%) to Preparation of epoxy/ TiO2- Al2O3 hybrid composites. The mechanical properties of nanocomposites such as bending ,wearing, and fatigue are investigated as mechanical properties.

Adenosine deaminase (ADA; Ec: 3.5.4.4), 5´- Nucleotidase (5´– NT; Ec: 3.1.3.5), and AMP – amino hydrolase (AMP – deaminase AMPDA; Ec: 3.5.4.6) activities were measured in sera of ovarian cancer patients before surgery, and after chemotherapy. The results indicated that ADA specific activity increased significantly (P<0.05), while 5´-NT and AMPDA specific activity decreased significantly (P<0.05) in ovarian cancer patients before surgery in comparison with those of their corresponding control women and benign tumors groups. When the activities of these enzymes were measured after chemotherapy, a significant decrease (P<0.05) in ADA activity, and a significant increase (P<0.05) in 5´- NT and AMPDA activities w