In this study, an easy, low-cost, green, and environmentally
friendlier reagents have been used to prepare CdS QDs, in chemical
reaction method by mixed different ratio of CdO and sulfur in
paraffin liquid as solvent and oleic acid as the reacting media in
different concentration to get the optimum condition of the reaction
to formation CdS QDs. The results give an indication that the
behavior is at small concentration of 4ml of the oleic acid is best
concentration which give CdS QDs of small about to 9.23 nm with
nano fiber configuration.

The aims of study is to detect the inhibitory effect of Saccharomyces boulardii and Lactobacillus acidophilus on Escherichia coli that has been isolated from recurrent urinary tract infection in women. The sensitivity of E.coli isolates to antibiotics had been studied and the most resistant E.coli isolate to antibiotics had been studied .The cup assay was used on nutrient agar and Muller-Hinton agar to detect the inhibitory activity for each S.boulardii yeast grown on YEGP media and L.acidophilus grown on MRS media in which the result showed a high inhibition activity for each of them .Also in this study the adhesion property of E.coli had been evaluated in the presence of S.boulardii at concentration of 1×109 and L.acidophilus at conc

Background Doxorubicin (DOX) is a potent antineoplastic agent used in treating various adult and pediatric cancers, but it tends to provoke dose-dependent cardiotoxicity. Ezetimibe (EZE), a cholesterol-lowering drug, has been reported to possess defensive actions against oxidative stress and inflammation, which are two of the main proposed mechanisms underlying the development of DOX-induced cardiotoxicity (DIC), hence, we aimed to inspect the possible protective effect of EZE against DIC in rats. Methods 24 adult male Wistar rats were allocated into four groups of six: control, DOX, 10 mg/kg EZE plus DOX and 20 mg/kg EZE plus DOX. At the end of the study, the experimental rats were anesthetized and blood samples were collected for b

The magnetic properties of a pure Nickel metal and Nickel-Zinc-Manganese ferrites having the chemical formula Ni_0.1(Zn_0.4Mn_0.6)_0.9Fe₂O₄ were studied. The phase formation and crystal structure was studied by using x-ray diffraction which confirmed the formation of pure single spinel cubic phase with space group (Fd3m) in the ferrite. The samples microstructure was studied with scanning electron microstructure and EDX. The magnetic properties of the ferrite and nickel metal were characterized by using a laboratory setup with a magnetic field in the range from 0-500 G. The ferrite showed perfect soft spinel phase behavior while the nickel sample showed higher magnetic loss an

Cadmium sulfide (CdS) thin films with n-type semiconductor characteristics were prepared by flash evaporating method on glass substrates. Some films were annealed at 250 ^oC for 1hr in air. The thicknesses of the films was estimated to be 0.5µ by the spectrometer measurement. Structural, morphological, electrical, optical and photoconductivity properties of CdS films have been investigated by X-ray diffraction, AFM, the Hall effect, optical transmittance spectra and photoconductivity analysis, respectively. X-ray diffraction (XRD) pattern shows that CdS films are in the stable hexagonal crystalline structure. Using Debye Scherrerś formula, the average grain size for the samples was found to be 26 nm. The transmittance of the

The creation and characterisation of biodegradable blend films based on chitosan and polyvinyl alcohol for application in a range of packaging is described. The compatibility between the chitosan and PVA polymers was good. Composite films had a compact and homogeneous structure, according to the morphology analysis. The mechanical test result of PVA/CH at concentrations 5% showed, that The higher values of TS recorded in sample (p1, with 40 MPa) while the lower values appeared in sample (p9, with 22.09 MPa), the TS decreased gradually as the amount of PVA increased in blend film. While the blend film of pure Chitosan exhibits a poor mechanical strength which makes it a poor candidate for packaging but Blending CH with PVA together improved