TiO2 thin films have been deposited at different concentration of
CdO of (x= 0.0, 0.05, 0.1, 0.15 and 0.2) Wt. % onto glass substrates
by pulsed laser deposition technique (PLD) using Nd-YAG laser
with λ=1064nm, energy=800mJ and number of shots=500. The
thickness of the film was 200nm. The films were annealed to
different annealing (423 and 523) k. The effect of annealing
temperatures and concentration of CdO on the structural and
photoluminescence (PL) properties were investigated. X-ray
diffraction (XRD) results reveals that the deposited TiO2(1-x)CdOx
thin films were polycrystalline with tetragonal structure and many
peaks were appeared at (110), (101), (111) and (211) planes with
preferred orientatio

In this research PbS thin film have been prepared by chemical bath deposition technique (CBD).The PbS film with thickness of (1-1.5)μm was thermally treated at temperature of 100°C for 4 hours. Some Structural characteristics was studied by using X-ray diffraction (XRD)and optical microscope photograph some of chemical gas sensing measurements were carried out ,it shown that the sensitivity of (CO2) gas depend on the grain Size and deposition substrate. The grain size of PbS film deposited on on glass closed to 21.4 nm while 37.97nm for Si substrate. The result of current-voltage characterization shwon the sensitivity of prepared film deposited on Si better than film on glass.

thirty adult NewZealand rabbits used in this study, they were divided in to two groups (control and treaded with Helium — Neon laser). A square skin flap done on the medial aspect of the auricle of both sides, a square piece of cartilage incised, pealed out from each auricle and fixed in the site of the other, then the flaps sutured .The site of the operation in the rabbits of the treated group were irradiated using a Helium —Neon laser with (5mw) power for (10 days) began after the operation directly, (3 rabbits) from each group used for collection of specimens for histopathological examination at the weeks (1,2,3,4, & 6) weeks post the operation .The results revealed Early invasion of the matrix with elastic fibers which continue to t

This research investigates new glasses which are best suitable for design of optical systems
working in the infrared region between 1.01 to 2.3μm. This work is extended to Oliva & Gennari
(1995,1998) research in which they found that the best known achromatic pairs are (BAF2-IRG2; SRF2-
IRG3; BAF2-IRG7; CAF2-IRGN6; BAF2-SF56A and BAF2-SF6). Schott will most probably stop the
production of these very little used and commercially uninteresting IRG glasses. In this work equally
good performances can be obtained by coupling BAF2, SRF2&CAF2 with standard glasses from Schott
or Ohara Company. The best new achromatic pairs found are (SRF2-S-TIH10; CAF2-S-LAL9; CAF2-SLAL13
and CAF2-S-BAH27). These new achromatic pai

The aim of this research is to design and construct a
semiconductor laser range finder operating in the near infrared range
for ranging and designation. The main part of the range finder is the
transmitter which is a semiconductor laser type GaAs of wavelength
0.904 μm with a beam expander and the receiver; a silicon pin
detector biased to approve the fast response time with it's collecting
optics. The transmitters pulse width was 200ns at a threshold current
of 10 Ampere and maximum operating current of 38 Ampere. The
repetition rate was set at 660Hz and the maximum operating output
power was around 1 watt. The divergence of the beam was 0.268o
the efficiency of the laser was 0.03% at a duty cycle of 1.32x

The present work focuses on the experimental implementation of one of the fiber optical sensors, the optical glass fiber built on surface Plasmon resonance. A type of optical glass fiber was used in this work, single-mode no-core fiber with pre-tapering diameter: (125.1 μm) and (125.3 μm), respectively. The taper method can be tested by measuring the output power of the optical fiber before and after chemical etching to show the difference in cladding diameter due to the effect of hydrofluoric acid with increasing time for the taper process. The optical glass fiber sensor can be fabricated using the taper method to reduce the cladding diameter of the fibers to (83.12 µm, 64.37 µm, and 52.45 µm) for single-mode fibers using Hydrofluoric

In order for the process of removing pollutants, including dyes, from the aquatic environment to be effective, plant wastes such as banana peels were used as adsorbent surfaces by thermally activating them (ABP) and modifying them with iron oxide nanoparticles (MABP), which were characterized using Fourier transform infrared (FT-IR) and X-ray diffraction (XRD) techniques. They were applied in the field of Janus green (JG) dye adsorption for the batch system and studied the effect of several factors (adsorbent weight, contact time, initial concentration, and temperature). Their data were analyzed kinetically using first- and second-order kinetic models and they were found to follow the second order. Their data were also analyzed thro