In this work, zinc oxide nanoparticles (ZnONPs) and sawdust/epoxy composite (20:80) were mixed using a simple molding method with different ZnONPs concentrations of (0.1, 0.3, 0.5, 0.7, and 1.0 %). The samples of the nanocomposites were characterized by the Scanning Electron Microscopy (SEM) technique to demonstrate the homogeneity of the prepared ZnONPs/nanocomposites. The photocatalytic activity of the samples was examined using the methylene blue (MB) dye as a pollutant solution, through evaluation of the efficiency of the prepared compound in the treatment of organic pollutants under illumination by sunlight. The photocatalytic results showed that after 240 minutes of exposure to sunlight, the sample prepared using (0.5 vol.% of ZnON

A thin CdS Films have been evaporated by thermal evaporation technique with different thicknesses (500, 1000, 1500 and 2000Å) and different duration times of annealing (60, 120 180 minutes) under 573 K annealing temperature, the vacuum was about 8 × 10-5 mbar and substrate temperature was 423 K. The structural properties of the films have been studied by X- ray diffraction technique (XRD). The crystal growth became stronger and more oriented as the film thickness (T) and duration time of annealing ( Ta) increases.

(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora

Di Benzylidenes were prepared by condensation of 1,2-diamino benzene with o- hydroxy benzaldehyde. These dibenzylidenes when treated with one equivalent of malonic anhydride or 5-oxo-spiro[2,3]hexane-4,6-dione in dry benzene give 6-membered heterocyclic ring system of 3-{2-[(2-Hydroxy-benzylidene)-amino]-phenyl}-2-(2-hydroxy –phenyl)-[1,3]oxazinane-4,6-diones ( 1-3) or 7-{2-[(2-hydroxy-benzylidene)-amino]-phenyl}-6-(2-hydroxy-phenyl)-5-oxa-7-aza-spiro[2.5]octane-4,8-diones ( 7- 9 ) But when two equivalents of malonic anhydride or 5-oxo-spiro[2,3]hexane-4,6-dione were used and under sam conditions compounds (4-6 , 10-12 ) were obtained .

 Thin  films   of  pure   tin mono-sulfide  SnS with thicknesses of   (0.85) μm  were prepared by chemical spray  pyrolysis  technique  and  annealed for  two  hours with 673K.The effect of annealing on structural and optical properties for films prepared was  studied.  X-Ray   diffraction  analysis  showed   the  polycrystalline  with   orthorhombic structure.  It was  found  that   annealing process increased the intensity of diffraction peaks. Optical   properties  of  all  samples  were studied by  recording  the  absorption  and  transmission &nbsp

Zinc oxide (ZnO) nanoparticles were synthesized using a modified hydrothermal approach at different reaction temperatures and growth times. Moreover, a thorough morphological, structural and optical investigation was demonstrated using scanning electron microscopy (SEM), x-ray diffraction (XRD), ultra-violate visible light spectroscopy (UV-Vis.), and photoluminescence (PL) techniques. Notably, SEM analysis revealed the occurrence of nanorods-shaped surface morphology with a wide range of length and diameter. Meanwhile, a hexagonal crystal structure of the ZnO nanoparticles was perceived using XRD analysis and crystallite size ranging from 14.7 to 23.8 nm at 7 and 8 ℎ𝑟𝑠., respectively. The prepared ZnO samples showed good abso

 In this work, we are Study the effect of annealing temperature on the structure of a-Ge films doped with Sb and the electrical properties of a-Ge:Sb/c-Si heterojunction fabricated by deposition of a-Ge:Sb film on c-Si by using thermal evaporation. Electrical properties of aGe:Sb/c-Si heterojunction include I-V characteristics in dark at different annealing temperatures and C-V characteristics and with the C-V characteristics suggest that the fabricated heterojunction was abrupt type, built in potential determined by extrapolation from 1/C2-V curve and show that the built - inpotential (Vbi) for the Ge:Sb/Si system increases with the increase of annealing temperatures