Effect of L-cysteine capping the CdSe, CdSe:CdS on structural and morphological properties
...Show More Authors

Scopus Crossref
View Publication
Publication Date
Sun Dec 07 2008
Journal Name
Baghdad Science Journal
The effect of doping ratio of Cu on the structural properties of CdSe Films
...Show More Authors

Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen

... Show More
View Publication Preview PDF
Crossref
Publication Date
Fri Jan 01 2016
Journal Name
World Scientific News
Effect of annealing temperature on the structural and optical properties of CdSe: 1% Ag thin films
...Show More Authors

Publication Date
Mon Jul 20 2020
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Thickness Effect of CuAlTe2 Thin Films on Morphological, Structural and Visual Properties
...Show More Authors

     CuAlTe2 thin films were evaporation on glass substrates using the technique of thermal evaporation at different range of thickness (200,300,400and500) ±2nm. The structures of these films were investigated by X-ray diffraction method; showing that films possess a good crystalline in tetragonal structure. AFM showed that the grain size increased from (70.55-99.40) nm and the roughness increased from (2.08-3.65) nm by increasing the thickness from (200-500) nm. The optical properties measurements, such as absorbance, transmtance, reflectance, and optical constant as a function of wavelength showed that the direct energy gap decreased from (2.4-2.34) eV by the gain of the thickness.

View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Thu Jun 08 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
The Effect of the (Se) percentage on Compositional, Morphological and structural properties of Bi2(Te1-xSex)3 thin films
...Show More Authors

  Alloys of Bi2[Te1-x Sex]3 were prepared by melting technique with different values of  Se percentage (x=0,0.1,0.3,0.5,0.7,0.9  and 1). Thin films of these alloys were prepared by using thermal evaporation technique under vacuum of 10-5 Torr on glass substrates, deposited at room temperature with a deposition rate (12nm/min) and a constant thickness (450±30 nm). The concentrations of the initial elements Bi, Te and Se in the Bi2 [Te1-x Sex]3 alloys with different values of Se percentage (x), were determined by XRF,The morphological and structural properties were determined by AFM and XRD techniques.  AFM images of Bi2[Te1-x Sex]3 thin films  show that the average diameter and the average surface roughness inc

... Show More
View Publication Preview PDF
Crossref
Publication Date
Thu Apr 13 2017
Journal Name
Journal Of Multidisciplinary Engineering Science Studies (jmess)
The Effect Of Thickness On Some Physical Properties Of CdSe Thin Films
...Show More Authors

Publication Date
Fri Jan 03 2020
Journal Name
Chalcogenide Letters
THE EFFECT OF Ag CONTENT AND HEAT TREATMENT ON STRUCTURAL AND MORPHOLOGICAL PROPERTIES OF THIN (Cu1-xAgx)2 ZnSnSe4 FILMS
...Show More Authors

(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora

... Show More
Preview PDF
Publication Date
Sat Mar 01 2008
Journal Name
Iraqi Journal Of Physics
The effect of Cu concentration on some of the electrical properties of CdSe films
...Show More Authors

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f

... Show More
View Publication Preview PDF
Publication Date
Sat Jul 01 2023
Journal Name
Journal Of Materials Science: Materials In Electronics
Effect of phosphoric acid chemical etching on morphological, structural, electrical, and optical properties of porous GaAs Schottky diodes
...Show More Authors

View Publication
Scopus (5)
Crossref (2)
Scopus Clarivate Crossref
Publication Date
Mon Apr 24 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Synthesis Of Nanostructured TiO2 Thin Films By Pulsed Laser Deposition (PLD) And The Effect Of Annealing Temperature On Structural And Morphological Properties
...Show More Authors

  In this work, nanostructured TiO2 thin films were grown by pulsed laser deposition (PLD) technique on glass substrates. TiO2 thin films then were annealed at 400-600 °C in air for a period of 2 hours. Effect of annealing on the structural and morphological were studied. Many growth parameters have been considered to specify the optimum conditions, namely substrate temperature (300 °C), oxygen pressure (10-2 Torr), laser fluence energy density (0.4 J/cm2), using double frequency Q-switching Nd:YAG laser beam (wavelength 532nm), repetition rate  (1-6 Hz) and the pulse duration of 10 ns. The results of the X-ray test show that all nanostructures tetragonal are polycrystalline. These results show that grain size increase fr

... Show More
View Publication Preview PDF
Publication Date
Sat Mar 18 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Studying the Effect of Doping With Aluminum on The Optical Properties Of CdSe Thin Films
...Show More Authors

CdSe thin films were deposited on glass sudstrate by thermal evaporation method with thickness of (300±25%) nm with deposition rate (2±0.1) nm/s and at substrate temperature at (R.T.). XRD analysis reveals that the structure of pure thin films are Hexagonal and polycrystalline with preferential orientation (002). In this research ,we study the effect of doping with (1,2,3)% Aluminum on optical energy gap of (CdSe) thin film . The absorption was studied by using (UV - Visible 1800 spectra photometer ) within the wavelength (300-1100) nm absorption coefficient was calculated as a function of incident photon energy for identify type of electronic transitions it is found that the type of transition is direct , and we calculated the opt

... Show More
View Publication Preview PDF