The present work describes the adsorption of Ba2+ and Mg2+ions from aqueous solutions by activated alumina in single and binary system using batch adsorption. The effect of different parameters such as amount of alumina, concentration of metal ions, pH of solution, contact time and agitation speed on the adsorption process was studied. The optimum adsorbent dosage was found to be 0.5 g and 1.5 g for removal of Ba2+ and Mg2+, respectively. The optimum pH, contact time and agitation speed, were found to be pH 6, 2h and 300 rpm, respectively, for removal of both metal ions. The equilibrium data were analyzed by Langmuir and Freundlich isotherm models and the data fitted well to both isotherm modes as indicated by higher correlation of deter

Klebsiella pneumoniae causes lethal nosocomial infections, mostly affecting patients with severe burns. More than 80% of its isolates have shown resistance to routinely used antibiotics in parallel with increased infection rates. The study aimed to determine the molecular typing and genetic relatedness of K. pneumoniae. Therefore, 20 multidrug resistant (MDR) K. pneumoniae already isolated from infected burned wounds in two major hospitals of Al-Kut city east Iraq were subjected to genotyping analysis. The random amplified polymorphic DNA (RAPD)-based polymerase chain reaction (PCR) technique was used along with three oligonucleotide primers (P13, OPX-04, and OPY-01). The amplicons’ patterns of the electrophoresis-gel were analyzed by the

Fabrication of porous clay refractory insulating specimens from Iraqi kaolin with different percentage of Expanded Polystyrene (EPS) waste crumbs additions were investigated. After mixing and forming by hand molding, the specimens was dried and fired at 1300 oC. The structural, physical, mechanical and thermal properties of the refractory insulating products were measured. Maximum addition of EPS (1.25 wt%) lead to reduce the linear shrinkage to less than 1.7% and increased apparent porosity up to 50 %. As well as, the density, Modulus of rupture and thermal conductivity were reduced to 1.39 g/cm3, 4.1 MPa and 0.21 W/m.K, respectively. The final outcome, addition of EPS showed good results in the formation of pores without distorting the

Some mechanical and thermal properties of mullite samples prepared by mixing different phases of alumina and silica powders have been studied according to ASTM methods the cold crushing strength of the sintcred bodies.With different porosity, at room temperature was in the range(18-54)Mpa

The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

In light of the limited sources of funding suffered by the Iraqi economy, it highlights the importance of enhancing the efficiency of public expenditure, and if the measurement of the efficiency of public expenditure and identify benchmarks first step of promoting efficiency, the adoption of scientific methods of analysis imperative in promoting the efficiency. Under this framework, the focus was on the methodologies used to measure the efficiency of public spending and supply analysis with trying statement strengths and weaknesses, and make use of it in the measurement of the efficiency of public spending in the Iraqi economy. As well as devise measurable indicators take into account the specificity of the Iraqi economy and the

The research aims to investigate the effects of GMAW or MIG welding process on the mechanical properties of dissimilar aluminum alloys 2024-T351 and AA 6061- T651. A series of experimental techniques have been conducted to evaluate mechanical properties of the alloys, by carrying out hardness, tensile and bending tests for welded and un-welded specimens.

Metal inert gas (MIG) has been carried out on sheet metal using ER- 4043(AlSi₅) as a filler metal and argon as shielded gas. The welded joints were tested by X-ray radiography and Faulty pieces were excluded.

Welding joints without defects are subjected to heat treatment including heating the joints in furnace to 170 °C for half an hour then air cooling to rel