Background: This study was conducted in pursuit of gaining an understand effects of the low level laser irradiation on whole blood is very essential way in revealing the mechanisms of the action of laser radiation  on biological tissues.
Objective: The purpose of this study is to investigate the in vitroeffect of laser radiation on some hematological parameters and erythrocyte sedimentation rate.
Subject and Method: Blood samples were obtained from 30 healthy volunteers, each sample was divided  into four new samples, one of them was considered as control while the other three were exposed to three  different laser doses. Thewavelength of532nm was used for irradiation with 4mm diameter beam spot on blood samples

The research is concerned about studying the absorption spectrum of the solution coumarin dye C47. The chloroform solvent was used with C47 dye in three different concentrations 10-4, 10-5 and 10-6 M. The laser dye solution was prepared by dissolving the required amount of dye in chloroform alcohol, while studying absorption spectrum before and after irradiation with gamma ray by cobalt-60 source 60Co at exposure time, which are 0, 4, 6 and 18 hours with different absorbed doses 0, 136, 204 and 612 Gy. The results show that red shift in the absorption spectrum was increased by increasing the concentration of laser dye solutions , while the increase of gamma dose led to increase the red shift after irradiation, as the exposure period and irr

Background: Decalcification of surface enamel adjacent to fixed orthodontic appliances, in the form of white spot lesions, is a wide spread and familiar well-known side effect of orthodontic treatment. The present study was carried out to evaluate the effect of enamel protective agent (Clinpro white varnish) on shear and tensile bond strength of Dentaurum orthodontic stainless steel brackets by using 3M Unitek and Ormco as orthodontic adhesive agents. Materials and methods: Sixty-four extracted human upper first premolar teeth were selected and randomly divided into two groups with 32 teeth each, representing the shear and tensile bond strength testing groups. Then according to the type of bonding adhesive and the addition of Clinpro before

In this work, the plasma parameters (electron temperature and
electron density) were determined by optical emission spectroscopy
(OES) produced by the RF magnetron Zn plasma produced by
oxygen and argon at different working pressure. The spectrum was
recorded by spectrometer supplied with CCD camera, computer and
NIST standard of neutral and ionic lines of Zn, argon and oxygen.
The effects of pressure on plasma parameters were studied and a
comparison between the two gasses was made.

The corrosion inhibition of low carbon steel in1N HCl solution in the presence of peach juice at temperature (30,40,50,and 60)°C at concentration ( 5, 10, 20, 30, 40and 50 cm3/L)were studied using weight loss and polarization techniques. Results show that the inhibition efficiency was increased with the increase of inhibitor concentration and increased with the increase of temperature up to 50ºC ,above 50ºC (i.e. at 60 ºC) the values of efficiency decreases. Activation parameters of the corrosion process such as activation energies, Ea, activation enthalpies, ΔH, and activation entropies, ΔS, were calculated. The adsorption of inhibitor follows Langmuir isotherm. Maximum inhibition efficiency obtained was a bout 91% at 50ºC in the

In this work we study the influence of the laser pulse energy and ablation time on the aluminum nanoparticles productivity during nanosecond laser ablation of bulk aluminum immersed in liquid.
Aluminum nanoparticles were synthesized by pulsed laser ablation of Al targets in ethanol for 3-8 minutes using the 1064 nm wavelength of a Nd:YAG laser with energies of 300-500 mJ per pulse.The laser energy was varied between 300 and 500 mJ/pulse, whereas the ablation time was set to 5 minutes. UV-Visible absorption spectra was used for the characterization and comparison of products.

Synthesis of a new ligand, namely [bis(2-(2-methyl-5-nitro-1H-imidazol-1-yl)ethyl) hydrogen borate] (BIB), utilizing the reaction of metronidazole with boric acid in a (2:1) mole ratio The metal complexes were synthesized utilizing the reaction of (NiCl₂.6H₂O and CuCl₂ .2H₂O) with (BIB) ligand in a 2:1 (L:M) mole ratio. All synthesized compounds were characterized utilizing spectroscopic techniques such as infrared (FTIR), nuclear magnetic resonance of protons(¹H NMR), ultra violet and visible radiation (UV-Vis), thermal analysis (TG), atomic absorption (A.A.S.), micro elemental analysis (C.H.N.S.), melting point (m.p.), magnetic susceptibility, molar conductivity, and chlor

Abstract

Black paint laser peening (bPLP) technique is currently applied for many engineering materials , especially for aluminum alloys due to high improvement in fatigue life and strength . Constant and variable   bending fatigue tests have been performed at RT and stress ratio R= -1 . The results of the present  work observed that the significance of the surface work hardening which generated high negative residual stresses in bPLP specimens .The fatigue life  improvement factor (FLIF)  for bPLP constant fatigue behavior was from 2.543 to 3.3 compared to untreated  fatigue and the increase in fatigue strength at 10⁷ cycle was 21% . The bPLP cumulative fatigue life behav

To add more details about the effect of the axial magnetic field on the plasma profile, the breakdown voltage of air was investigated at low pressure (9-15 Pa) in the presence of axial magnetic field (0.01-0.04T). The air was ignited by a DC voltage between two plain electrodes of aluminum separated by a distance (8.5cm). The measurements showed that the discharge voltage decreases to a minimum value, then returns to increase over the minimum with increasing the magnetic field strength, at all pressures in the range. It was also observed that a maximum decrease in the discharge voltage is obtained near the minimum of  Paschen curve from the right side. The decrease in the discharge voltage was caused mainly by the effect of magnetic